Abstract
Zinc-air battery is one of the most promising next-generation energy conversion and storage systems. Green and low-cost catalysts with high oxygen reduction reaction (ORR) catalytic activity are desired to meet the requirements of Zinc-air batteries. Herein, poly-active centric Co3O4-CeO2/Co-N-C (ketjenblack carbon) catalysts were prepared by a facile method. The Co3O4 and CeO2 nanoparticles are uniformly anchored on the surface of Co and N doped carbon support. The half-wave potential of Co3O4-CeO2/Co-N-C in the rotating disk electrode testing is close to that of Pt/C. The Zn-air battery using Co3O4-CeO2/Co-N-C as the cathode catalyst can provide a high specific capacity of 728 mA h g−1 at 20 mA cm−2 and maintain a stable discharge voltage. The remarkable catalytic performance is mainly attributed to the synergistic effect among Co3O4, CeO2 and Co-N-C, the outstanding electrical conductivity and the large surface area. Benefitting from the high catalytic activity, environmental friendliness and the facile synthesis process, Co3O4-CeO2/Co-N-C catalyst lends itself well to a great prospect in the application of metal-air batteries.
摘要
为了满足新一代金属空气电池对绿色、 低成本且具有高氧还原催化活性催化剂的迫切需求, 本文通过简便方法制备了具有 多活性中心的Co3O4-CeO2/Co-N-C(科琴黑)氧还原催化剂. 其中, Co3O4和CeO2纳米颗粒均匀地固定在Co、 N共掺杂的碳载体表面. Co3O4-CeO2/Co-N-C在旋转圆盘电极测试中的半波电位与Pt/C接近. 以Co3O4-CeO2/Co-N-C作为阴极催化剂的锌空气电池可以在 20 mA cm−2下提供728 mA h g−1的高比容量并能够维持稳定的放电电压. 其优异的催化性能主要归功于Co3O4、 CeO2和Co-N-C之间的协同作用、高导电性和大比表面积. Co3O4-CeO2/Co-N-C催化剂具有催化活性高、 环境友好、 合成工艺简单等优点, 在金属空气电池中具有广阔的应用前景.
Article PDF
Similar content being viewed by others
References
Shen M, Gao K, Xiang F, et al. Nanocellulose-assisted synthesis of ultrafine Co nanoparticles-loaded bimodal micro-mesoporous N-rich carbon as bifunctional oxygen electrode for Zn-air batteries. J Power Sources, 2020, 450: 227640–227649
Qin L, Lv W, Wei W, et al. Oxygen-enriched carbon nanotubes as a bifunctional catalyst promote the oxygen reduction/evolution reactions in Li-O2 batteries. Carbon, 2019, 141: 561–567
Zhao CX, Li BQ, Liu JN, et al. Transition metal coordinated framework porphyrin for electrocatalytic oxygen reduction. Chin Chem Lett, 2019, 30: 911–914
Wang Z, Liao X, Lin Z, et al. 3D nitrogen-doped graphene encapsulated metallic nickel-iron alloy nanoparticles for efficient bifunctional oxygen electrocatalysis. Chem Eur J, 2020, 26
Suen NT, Hung SF, Quan Q, et al. Electrocatalysis for the oxygen evolution reaction: recent development and future perspectives. Chem Soc Rev, 2017, 46: 337–365
Lu XF, Xia BY, Zang S-, et al. Metal-organic frameworks based electrocatalysts for the oxygen reduction reaction. Angew Chem, 2020, 132: 4662–4678
Lee DU, Xu P, Cano ZP, et al. Recent progress and perspectives on bi-functional oxygen electrocatalysts for advanced rechargeable metal-air batteries. J Mater Chem A, 2016, 4: 7107–7134
Huang X, Shen T, Zhang T, et al. Efficient oxygen reduction catalysts of porous carbon nanostructures decorated with transition metal species. Adv Energy Mater, 2019, 10: 1900375–1900396
Liu J, Ma Q, Huang Z, et al. Recent progress in graphene-based noble-metal nanocomposites for electrocatalytic applications. Adv Mater, 2019, 31: 1800696–1800716
Liu L, Zhang J, Ma W, et al. Co/N co-doped graphene-like nanocarbon for highly efficient oxygen reduction electrocatalyst. Sci China Mater, 2019, 62: 359–367
Lei H, Wang Z, Yang F, et al. NiFe nanoparticles embedded N-doped carbon nanotubes as high-efficient electrocatalysts for wearable solid-state Zn-air batteries. Nano Energy, 2020, 68: 104293–104322
Luo M, Qin Y, Li M, et al. Interface modulation of twinned PtFe nanoplates branched 3D architecture for oxygen reduction catalysis. Sci Bull, 2020, 65: 97–104
Liu J, Jiao M, Mei B, et al. Carbon-supported divacancy-anchored platinum single-atom electrocatalysts with superhigh Pt utilization for the oxygen reduction reaction. Angew Chem, 2019, 131: 1175–1179
Tian X, Zhao X, Su YQ, et al. Engineering bunched Pt-Ni alloy nanocages for efficient oxygen reduction in practical fuel cells. Science, 2019, 366: 850–856
Xiong Y, Ma Y, Zou L, et al. N-doping induced tensile-strained Pt nanoparticles ensuring an excellent durability of the oxygen reduction reaction. J Catal, 2020, 382: 247–255
Cheng Y, Zhao X, Yu Y, et al. Indium oxide supported Pt-In alloy nanocluster catalysts with enhanced catalytic performance toward oxygen reduction reaction. J Power Sources, 2020, 446: 227332–227338
Patil B, Satilmis B, Uyar T. Metal-free N-doped ultrafine carbon fibers from electrospun polymers of intrinsic microporosity (PIM-1) based fibers for oxygen reduction reaction. J Power Sources, 2020, 451: 227799–227809
Zhu P, Gao J, Chen X, et al. An efficient metal-free bifunctional oxygen electrocatalyst of carbon co-doped with fluorine and nitrogen atoms for rechargeable Zn-air battery. Int J Hydrogen Energy, 2020, 45: 9512–9521
Wütscher A, Eckhard T, Hiltrop D, et al. Nitrogen-doped metal-free carbon materials derived from cellulose as electrocatalysts for the oxygen reduction reaction. ChemElectroChem, 2019, 6: 514–521
Huang Z, Li G, Huang Y, et al. Facile one-pot synthesis of low cost MnO2 nanosheet/super P Li composites with high oxygen reduction reaction activity for Zn-air batteries. J Power Sources, 2020, 448: 227385–227393
Xiong C, Yang Q, Dang W, et al. Fabrication of eco-friendly carbon microtubes @ nitrogen-doped reduced graphene oxide hybrid as an excellent carbonaceous scaffold to load MnO2 nanowall (PANI nanorod) as bifunctional material for high-performance supercapacitor and oxygen reduction reaction catalyst. J Power Sources, 2020, 447: 227387–227396
Chen LN, Yu WS, Wang T, et al. Fluorescence detection of hydroxyl radical generated from oxygen reduction on Fe/N/C catalyst. Sci China Chem, 2020, 63: 198–202
Li M, Luo F, Zhang Q, et al. Atomic layer Co3O4−x nanosheets as efficient and stable electrocatalyst for rechargeable zinc-air batteries. J Catal, 2020, 381: 395–401
Reza Ugalde A, Kesler O, Naguib HE. Highly stable bifunctional catalyst for Zn-air batteries: The effect of a nitrated carbon support on Co3O4 activity. J Power Sources, 2020, 453: 227834–227846
Cui C, Du G, Zhang K, et al. Co3O4 nanoparticles anchored in MnO2 nanorods as efficient oxygen reduction reaction catalyst for metal-air batteries. J Alloys Compd, 2020, 814: 152239–152246
Liu K, Zhou Z, Wang H, et al. N-doped carbon supported Co3O4 nanoparticles as an advanced electrocatalyst for the oxygen reduction reaction in Al-air batteries. RSC Adv, 2016, 6: 55552–55559
Huang Z, Qin X, Li G, et al. Co3O4 nanoparticles anchored on nitrogen-doped partially exfoliated multiwall carbon nanotubes as an enhanced oxygen electrocatalyst for the rechargeable and flexible solid-state Zn-air battery. ACS Appl Energy Mater, 2019, 2: 4428–4438
Zhang J, Wang T, Xue D, et al. Energy-level engineered hollow N-doped NiS1.03 for Zn-air batteries. Energy Storage Mater, 2020, 25: 202–209
Li J, Zhou Z, Liu K, et al. Co3O4/Co-N-C modified ketjenblack carbon as an advanced electrocatalyst for Al-air batteries. J Power Sources, 2017, 343: 30–38
Huang Z, Qin X, Gu X, et al. Mn3O4 quantum dots supported on nitrogen-doped partially exfoliated multiwall carbon nanotubes as oxygen reduction electrocatalysts for high-performance Zn-air batteries. ACS Appl Mater Interfaces, 2018, 10: 23900–23909
Hessien MM, El-Bagoury N, Mahmoud MHH, et al. Implementation of La3+ ion substituted M-type strontium hexaferrite powders for enhancement of magnetic properties. J Magn Magn Mater, 2020, 498: 166187–166219
Sing KSW. Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity. Pure Appl Chem, 1985, 57: 603–619
Chen J, Yuan X, Lyu F, et al. Integrating MXene nanosheets with cobalt-tipped carbon nanotubes for an efficient oxygen reduction reaction. J Mater Chem A, 2019, 7: 1281–1286
Raj K A, Panda MR, Dutta DP, et al. Bio-derived mesoporous disordered carbon: An excellent anode in sodium-ion battery and full-cell lab prototype. Carbon, 2019, 143: 402–412
Etesami M, Oroujzadeh M, Mehdipour-Ataei S. 3D nitrogen-doped carbon supported non-precious metals electrocatalyst for oxygen reduction reaction. Mol Catal, 2020, 485: 110834–110841
Lv Q, Wang N, Si W, et al. Pyridinic nitrogen exclusively doped carbon materials as efficient oxygen reduction electrocatalysts for Zn-air batteries. Appl Catal B-Environ, 2020, 261: 118234
Rashad M, Rüsing M, Berth G, et al. CuO and Co3O4 nanoparticles: Synthesis, characterizations, and Raman spectroscopy. J Nanomaterials, 2013, 2013: 1–6
Jiang L, Yao M, Liu B, et al. Controlled synthesis of CeO2/graphene nanocomposites with highly enhanced optical and catalytic properties. J Phys Chem C, 2012, 116: 11741–11745
Qu D, Zheng M, Zhang L, et al. Formation mechanism and optimization of highly luminescent N-doped graphene quantum dots. Sci Rep, 2015, 4: 5294
Zhu L, Wang C, Qiu Y. Influence of the amount of absorbed moisture in nylon fibers on atmospheric pressure plasma processing. Surf Coatings Tech, 2007, 201: 7453–7461
Dubois JE, Lacaze PC, Pham MC. Obtaining thin films of “reactive polymers” on metal surfaces by electrochemical polymerization. J Electroanal Chem Interfacial Electrochem, 1981, 117: 233–241
Zhang H, Kuila T, Kim NH, et al. Simultaneous reduction, exfoliation, and nitrogen doping of graphene oxide via a hydrothermal reaction for energy storage electrode materials. Carbon, 2014, 69: 66–78
Wei L, Li W, Zhao T, et al. Cobalt nanoparticles shielded in N-doped carbon nanotubes for high areal capacity Li-S batteries. Chem Commun, 2020, 56: 3007–3010
Ou B, Wang J, Wu Y, et al. Efficient removal of Cr (VI) by magnetic and recyclable calcined CoFe-LDH/g-C3N4via the synergy of adsorption and photocatalysis under visible light. Chem Eng J, 2020, 380: 122600–122612
Chen W, Ge L, Ding L, et al. Modification of pyridinic N and O-rich defects in a bifunctional electrocatalyst with enhanced electrocatalytic performance. J Alloys Compd, 2019, 789: 874–880
Li HH, Zhou L, Zhang LL, et al. Co3O4 nanospheres embedded in a nitrogen-doped carbon framework: An electrode with fast surface-controlled redox kinetics for lithium storage. ACS Energy Lett, 2017, 2: 52–59
Gao Z, Liu X, Chang J, et al. Graphene incorporated, N doped activated carbon as catalytic electrode in redox active electrolyte mediated supercapacitor. J Power Sources, 2017, 337: 25–35
Xi J, Xia Y, Xu Y, et al. (Fe,Co)@nitrogen-doped graphitic carbon nanocubes derived from polydopamine-encapsulated metal-organic frameworks as a highly stable and selective non-precious oxygen reduction electrocatalyst. Chem Commun, 2015, 51: 10479–10482
Zhu J, Li H, Zhong L, et al. Perovskite oxides: preparation, characterizations, and applications in heterogeneous catalysis. ACS Catal, 2014, 4: 2917–2940
Jiang G, Jiang N, Zheng N, et al. MOF-derived porous Co3O4-NC nanoflake arrays on carbon fiber cloth as stable hosts for dendrite-free Li metal anodes. Energy Storage Mater, 2019, 23: 181–189
Xu J, Zhang W, Chen Y, et al. MOF-derived porous N-Co3O4@N-C nanododecahedra wrapped with reduced graphene oxide as a high capacity cathode for lithium-sulfur batteries. J Mater Chem A, 2018, 6: 2797–2807
Kim SM, Jo YG, Lee MH, et al. The plasma-assisted formation of Ag@Co3O4 core-shell hybrid nanocrystals for oxygen reduction reaction. Electrochim Acta, 2017, 233: 123–133
Assumpção MHMT, Moraes A, De Souza RFB, et al. Influence of the preparation method and the support on H2O2 electrogeneration using cerium oxide nanoparticles. Electrochim Acta, 2013, 111: 339–343
Wu M, Hu X, Li C, et al. Encapsulation of metal precursor within ZIFs for bimetallic N-doped carbon electrocatalyst with enhanced oxygen reduction. Int J Hydrogen Energy, 2018, 43: 14701–14709
Acknowledgements
We gratefully acknowledge the financial support from the Department of Science and Technology of Guangdong Province, China (2019A050510043) and Shenzhen Science and Technology Innovation Commission (JCYJ20180507183818040).
Author information
Authors and Affiliations
Contributions
Author contributions Li G and Mu Y synthesized the material, did the SEM test, collected the electrochemical data and wrote the manuscript. Chen Y and Liu G did the XRD and XPS tests. Huang Z and Wang N analyzed the experimental data. Liu J conducted the TGA and electrochemical tests. Li OL and Shao M analyzed the experimental data and modified the manuscript. Shi Z conceived and supervised the experiments, and modified the manuscript. All authors contributed to the general discussion.
Corresponding authors
Ethics declarations
Conflict of interest The authors declare no conflict of interest.
Additional information
Guanzhou Li is currently a master candidate at Guangdong University of Technology. He received his BSc degree (majored in metallic materials engineering) from the same university in 2018. His MSc research focuses on oxygen reduction catalysts and zinc-ion batteries.
Yangchang Mu obtained his master degree in materials science and engineering from Guangdong University of Technology in 2019. His main interests focus on multifunctional electrocatalyst nanomaterials and devices and in particular on the fields of non-noble metal electrocatalyst materials for metal-air batteries and fuel cells.
Oi Lun (Helena) Li completed her PhD in 2010 at McMaster University, concentrating on plasma chemistry and process. She has focused on the syntheses and modification of carbon nanomaterials and applied carbon catalysts for renewable energy conversion system. Her major research interests include metal/heteroatom-doped carbon catalysts for metal-air batteries and fuel cells, as well as functional carbon nanomaterials for biomass conversion.
Minhua Shao earned his PhD degree in materials science and engineering from the State University of New York at Stony Brook (2006). He is now a professor in the Department of Chemical and Biological Engineering and Associate Director of Energy Institute of the Hong Kong University of Science and Technology. His research mainly focuses on electrocatalysis, fuel cells, and advanced batteries.
Zhicong Shi earned his PhD degree in physical chemistry from Xiamen University, China (2005). He is now a professor in the Department of New Energy Materials and Devices, Guangdong University of Technology, and Director of Guangdong Provincial Engineering Technology Centre on New Energy Materials and Devices. His research mainly focuses on new electrode materials, electrocatalysts and solid electrolytes for advanced batteries.
Rights and permissions
About this article
Cite this article
Li, G., Mu, Y., Huang, Z. et al. Poly-active centric Co3O4-CeO2/Co-N-C composites as superior oxygen reduction catalysts for Zn-air batteries. Sci. China Mater. 64, 73–84 (2021). https://doi.org/10.1007/s40843-020-1378-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40843-020-1378-y