Silver Chloride Loaded Hollow Mesoporous Silica Particles and Their Application in the Antibacterial Coatings on Denture Base

Article

Abstract

Hollow mesoporous silica particles(HMSPs) were prepared by using polystyrene microspheres as a tem-plate and loaded with silver chloride(AgCl) to act as antibacterial agents. The HMSPs possess radially oriented pore channels and a high loading amount of AgCl. The AgCl loaded HMSPs were then dispersed in hybrid coatings with different mass ratios to fabricate antibacterial coatings. The antibacterial activities of the coatings were tested against Candida albicans(ATCC 10231) and Streptococcus mutants(ATCC 25175). The resulting antibacterial coatings exhi-bited high antibacterial activities, high hardness, and acceptable adhesion to the substrate.

Keywords

Hollow mesoporous silica Silver chloride Antibacterial Hybrid coating 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Hong G., Murata H., Li Y. A., Sadamori S., Hamada T., J. Prosthet. Dent., 2009, 101, 205CrossRefGoogle Scholar
  2. [2]
    Yildirim M. S., HasanreİSoǦLu U., Hasirci N., Sultan N., J. Oral Rehabil., 2005, 32, 518CrossRefGoogle Scholar
  3. [3]
    Batoni G., Pardini M., Giannotti A., Ota F., Rita Giuca M., Gabriele M., Eur. J. Oral Sci., 2001, 109, 388CrossRefGoogle Scholar
  4. [4]
    Cui W. W., Liu Y., Wang Z. L., Wang H., Cui L. G., Zhang P. B., Chem. J. Chinese Universities, 2013, 34(3), 679Google Scholar
  5. [5]
    Zhang Y. F., Li Y. L., Yao Y., Li W. Y., Hu Q. L., Chem. J. Chinese Universities, 2012, 33(8), 1860Google Scholar
  6. [6]
    Liu F., Wang X., Ye K. Q., Qiu L. Y., Shen J. C., Chem. J. Chinese Universities, 2011, 32(4), 990Google Scholar
  7. [7]
    Top A., Ulku S., Appl. Clay Sci., 2004, 27, 13CrossRefGoogle Scholar
  8. [8]
    Jia H., Hou W., Wei L., Xu B., Liu X., Dent. Mater., 2008, 24, 244CrossRefGoogle Scholar
  9. [9]
    Hrenovic J., Milenkovic J., Goic-Barisic I., Rajic N., Micropor. Me-sopor. Mater., 2013, 169, 148CrossRefGoogle Scholar
  10. [10]
    Yu B., Leung K. M., Guo Q., Lau W. M., Yang J., Nanotechnology, 2011, 22, 115603CrossRefGoogle Scholar
  11. [11]
    Duan S. E., Zhai Y. H., Qu Y. J., Ma M. Y., Chem. J. Chinese Univer-sities, 2012, 33(11), 2617Google Scholar
  12. [12]
    Chen H. J., Xu F. Q., Xue D., Yang Y. F., Zhang Q. F., Acta Chimica Sinica, 2012, 12, 1362CrossRefGoogle Scholar
  13. [13]
    Zhang Y., Qu Q., Cao X., Zhao Y., Chem. Comm., 2017, 53(88), 12032CrossRefGoogle Scholar
  14. [14]
    Li Y. H., Chen Y. Y., Pan W., Yu Z. Z., Yang L. M., Wang H. Y., Li N., Tang B., Nanoscale, 2017, 9(44), 17318CrossRefGoogle Scholar
  15. [15]
    Ciesla U., Schüth F., Micropor. Mesopor. Mater., 1999, 27, 131CrossRefGoogle Scholar
  16. [16]
    Wang C. W., Hong H., Lin Z. F., Yuan Y., Liu C. S., Ma X. Y., Cao X. Y., RSC Advances, 2015, 5(126), 104289CrossRefGoogle Scholar
  17. [17]
    Bois L., Chassagneux F., Desroches C. D., Battie Y., Destouches N., Gilon N., Parola S., Stephan O., Langmuir, 2010, 26, 8729CrossRefGoogle Scholar
  18. [18]
    Zhang X., Gu S. J., Zhou B. Y., Shi L. W., Yang F. J., Wang L. J., Jiang W. H., Luo W., Jiang W., J. Am. Ceram. Soc., 2016, 99(5), 1579CrossRefGoogle Scholar
  19. [19]
    Du X., He J., Nanoscale, 2012, 4, 852CrossRefGoogle Scholar
  20. [20]
    Lee K. S., El-Sayed M. A., J. Phys. Chem. B, 2006, 110, 19220CrossRefGoogle Scholar
  21. [21]
    Taylor P. L., Ussher A. L., Burrell R. E., Biomaterials, 2005, 26, 7221CrossRefGoogle Scholar
  22. [22]
    Kumar R., Münstedt H., Biomaterials, 2005, 26, 2081CrossRefGoogle Scholar
  23. [23]
    Marini M., de Niederhausern S., Iseppi R., Bondi M., Sabia C., To-selli M., Pilati F., Biomacromolecules, 2007, 8, 1246CrossRefGoogle Scholar
  24. [24]
    Li X. L., Zuo W. W., Luo M., Shi Z. S., Cui Z. C., Zhu S., Chem. Res. Chinese Universities, 2013, 29(6), 1214CrossRefGoogle Scholar
  25. [25]
    Qi G., Wang Y., Estevez L., Switzer A. K., Duan X., Yang X., Gian-nelis E. P., Chem. Mater., 2010, 22, 2693CrossRefGoogle Scholar
  26. [26]
    Guo L., Li J., Zhang L., Li J., Li Y., Yu C., J. Mater. Chem., 2008, 18, 2733CrossRefGoogle Scholar
  27. [27]
    Min S. H., Yang J. H., Kim J. Y., Kwon Y. U., Micropor. Mesopor. Mater., 2010, 128, 19CrossRefGoogle Scholar
  28. [28]
    Walcarius A., Delacôte C., Chem. Mater., 2003, 15, 4181CrossRefGoogle Scholar

Copyright information

© Jilin University, The Editorial Department of Chemical Research in Chinese Universities and Springer-Verlag GmbH Germany, part of Springer Nature 2018

Authors and Affiliations

  • Xianliang Li
    • 1
  • Zuosen Shi
    • 2
  • Zhanchen Cui
    • 2
  • Song Zhu
    • 3
  1. 1.College of Material Science and EngineeringShenyang University of Chemical TechnologyShenyangP. R. China
  2. 2.State Key Laboratory of Supramolecular Structure and Materials, College of ChemistryJilin UniversityChangchunP. R. China
  3. 3.Hospital of StomatologyJilin UniversityChangchunP. R. China

Personalised recommendations