Friction Stir Welding of EH46 Steel Grade at Dwell Stage: Microstructure Evolution

Technical Article
  • 184 Downloads

Abstract

This work aims to understand the effect of changes in friction stir welding (FSW) process parameters on the resulting microstructure specifically the effect of the plunge depth and tool rotational speed, during the “dwell” period on the resulting microstructure. A series of (FSW) of 14.8-mm-thick EH46 steel plate using a hybrid polycrystalline boron nitride FSW tool with spindle speeds of 120 and 200 revolutions per minute have been produced with increasing plunge depths from 0.1 to 0.7 mm. Thermocouples embedded around the top surface of each plunge case were used to measure the peak temperature during the process. The plunge depths were measured using the infinite focus microscopy, and the microstructure of all the heat affected regions was investigated extensively by scanning electron microscopy. It was found that phase transformation is sensitive to the variation on plunge depth. Small increase in plunge depth caused a significant change in the microstructure. Increasing tool rotational speed was also found to cause a significant difference in the microstructure.

Keywords

EH46 steel Friction stir welding Plunge depth Microstructure 

Notes

Acknowledgments

The authors would like to thank the Ministry of higher education Iraq for funding this project, thanks for TWI/Yorkshire Company for providing samples, data and advice.

References

  1. 1.
    A. Toumpis, A. Gallawi, S. Cater, L. Molter, A techno-economic evolution of friction stir welding of DH36 steel, in 10th Friction Stir Welding Symposium, 10th FSWS, 20–22/05/2014 (Beijing, 2014), pp. 1–11Google Scholar
  2. 2.
    Z. Feng, M.L. Santella, S.A. David, R.J. Steel, S. M. Packer, T. Pan, M. Kuo, R.S. Bhatnagar, Friction stir spot welding of advanced high-strength steels: a feasibility study, SAE Technical Paper, vol. 2005-01, p. 1248 (2005)Google Scholar
  3. 3.
    T.C. Lomholt, K. Pantleon, M.A.J. Somers, Y. Adachi, J. Peterson, R. Steel, Microstructure characterization of friction stir spot welded TRIP steel. Adv. Mater. Res. 409, 275–280 (2012)CrossRefGoogle Scholar
  4. 4.
    C.C.P. Mazzaferro, T.S. Rosendo, M.A.D. Tier, J.A.E. Mazzaferro, J.F. Dos Santos, T.R. Strohaecker, Microstructural and mechanical observations of galvanized trip steel after friction stir spot welding. Mater. Manuf. Process 30, 1090–1103 (2015)CrossRefGoogle Scholar
  5. 5.
    Y. Hovanski, M.L. Santella, G.J. Grant, FSSW in hot-stamped boron steel. Scr. Mater. 57, 873–876 (2007)CrossRefGoogle Scholar
  6. 6.
    M. Miles, T. Hartman, C. Cunningham, N. Saunders, Y. Hovanski, in High Speed Friction Stir Spot Welding of Advanced High Strength Steel, Material Science and Technology Conference and Exhibition, 7–11 October Pennsylvania, USA, vol. 1–2 (2012)Google Scholar
  7. 7.
    T. Nishihara, Y. Nagasaka, Measurement of tool temperature during friction stir welding, in Symposium on Friction stir welding (Park city, Utah, 2003)Google Scholar
  8. 8.
    A. Fehrenbacher, J.R. Schmale, M.R. Zinn, F.E. Pfefferkorn, Measurement of tool-workpiece interface temperature distribution in friction stir welding. J. Manuf. Sci. Eng. 136(2), 21009 (2014)CrossRefGoogle Scholar
  9. 9.
    H. Schmidt, J. Hattel, Modelling heat flow around tool probe in friction stir welding. Sci. Technol. Weld. Join. 10(2), 176–186 (2005)CrossRefGoogle Scholar
  10. 10.
    Di Martino, S.F. Thewlis, Transformation characteristics of ferrite/carbide aggregate in continuously cooled, low carbon–manganese steels. Metall. Mater. Trans. A 45(2), 579–594 (2013)CrossRefGoogle Scholar
  11. 11.
    S.R. Mishra, W.M. Mahoney, Friction Stir Welding and Processing (ASM International, Materials Park, 2007), pp. 163–167Google Scholar
  12. 12.
    M. Al-moussawi, A. Smith, A. Young, S. Cater, M. Faraji, An advanced numerical model of friction stir welding of DH36 steel, in 11th International Symposium FSW (TWI Granta Park Cambridge, Cambridge, 2016)Google Scholar

Copyright information

© Springer Science+Business Media, LLC and ASM International 2017

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Authors and Affiliations

  1. 1.Al-Furat Al-Awsat Technical UniversityKufaIraq
  2. 2.MERISheffield Hallam UniversitySheffieldUK
  3. 3.Coventry UniversityCoventryUK

Personalised recommendations