Abstract
A thermomechanical processing (TMP) method consisting of annealing, cold working, and partial remelting was employed to modify the microstructure and mechanical properties of Al 2024 alloy. The effects of the semi-solid temperature and holding time at the semi-solid temperature on the microstructure of the alloy were studied. The results showed that the optimum parameters were 610 °C and 7 min. Also, T6 heat treatment was applied to the thermomechanical processed alloy with the best combination of the parameters to examine its effect on the characteristics of the alloy. The results revealed that the amounts of yield strength and ultimate tensile strength increased, but T6 heat treatment did not have any remarkable effect on the tensile properties of the thermomechanical processed sample but improved the hardness of the alloy. In addition, the fracture mode in the thermomechanical processed sample was ductile while in the sample that underwent T6, brittle fracture was dominant.
Similar content being viewed by others
References
Güven E A, Trans Indian Inst Met 69 (2016) 935.
Li L, Zhou R F, Cen Q, Lu D, Jiang Y, and Zhou R, Trans Indian Inst Met 66 (2013) 163.
Hajizamani M, Alizadeh M, and Jenabali-Jahromi S A, Acta Metallurgica Sinica (English Lett) 29 (2016) 39.
Hajizamani M, and Alizadeh M, Int J Mater Res 108 (2017) 840.
Mohsen H, Mostafa A, Ali A, and Seyed Ahmad J-J, Mater Res Express 5 (2018) 026520.
Vaneetveld G, Rassili A, Pierret J C, and Lecomte-Beckers J, in Solid State Phenomena, Trans Tech Publ (2008), p 707.
Vaneetveld G, Rassili A, Pierret J-C, and Lecomte-Beckers J, Int J Mater Form 3 (2010) 783.
Karamouz M, Alizadeh M, and Ahmadi A, Int J Mater Res 108 (2017) 1073.
Prabhu T R, Arch Civ Mech Eng 16 (2016) 335.
Chen T-j, Ma Y, Wang R-q, Li Y-d, and Hao Y, Trans Nonferrous Met Soc China 20 (2010) 1615.
Lu Y, Li M, Niu Y, and Li X, J Mater Eng Perform 17 (2008) 25.
Lin Y C, Xia Y-C, Jiang Y-Q, and Li L-T, Mater Sci Eng A 556 (2012) 796.
Wang S C, and Starink M J, Acta Materialia 55 (2007) 933.
Azpilgain Z, Hurtado I, Basterrechea G, Gandarias E, Goni J, Eguieabal P, Lakehal M, Sarries I, Landa I, and Wielanek L, in 8th International Conference on Semi-Solid Processing of Alloys and Composites, Limassol, Cyprus (2004), p 23.
Tzimas E, and Zavaliangos A, Mater Sci Eng A 289 (2000) 228.
Queudet H, Lemonnier S, Barraud E, Guyon J, Ghanbaja J, Allain N, and Gaffet E, Mater Sci Eng A 685 (2017) 227.
Sathiyamoorthi P, Basu J, Kashyap S, Pradeep K, and Kottada R S, Mater Design 134 (2017) 426.
Salvo L, Suery M, Charentenay Y, and Loue W, in Proceedings of the Fourth International Conference on Semi-solid Processing of Alloys and Composites, Sheffield, UK (1996) p 10.
Voorhees P W, J Stat Phys 38 (1985) 231.
Dieter G E, and Bacon D, Mechanical Metallurgy, McGraw-Hill, New York (1986).
Zhou J, Xu S, Huang S, Meng X, Sheng J, Zhang H, Li J, Sun Y, and Boateng E A, Metals 6 (2016) 279.
Cheng S, Zhao Y, Zhu Y, and Ma E, Acta Materialia 55 (2007) 5822.
Ghandvar H, Farahany S, and Idris J, Mater Manuf Process 30 (2015) 1442.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Negini, H., Rezaei, A., Hajisafari, M. et al. Effects of semi-solid thermomechanical processing on microstructure and mechanical properties of Al 2024. Trans Indian Inst Met 72, 1201–1209 (2019). https://doi.org/10.1007/s12666-019-01608-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-019-01608-0