Abstract
Aluminium alloy AA7075 matrix composites reinforced with varying vol% (5, 10 and 15 vol%) of niobium carbide (NbC) were fabricated by friction stir processing. Micrographs revealed that a homogeneous dispersion of NbC in the AA7075 matrix had no interfacial reaction. Significant degree of grain refinement was observed in the composites due to dynamic recrystallization and pinning effect of NbC particles. Hardness and tensile strength of AA7075 matrix were found to be enhanced by the addition of NbC particles. The fracture surface of the tensile-tested samples revealed deep dimples indicating a good ductility.
Similar content being viewed by others
References
Johannes L B, and Mishra R S, Mater Sci Eng A 464 (2007) 255.
Satish Kumar T, Shalini S, and Krishna Kumar K, Arch Metall Mater 63 (2018) 689.
Dieguez T, Burgueñob A, and Svoboda H, Procedia Mater Sci 1 (2012) 110.
Hozief W, Toschi S, Ahmed M M Z, Morri A L, Mahdy A A, El-Sayed Seleman M M, El-Mahallawi I, Ceschini L, and Atlam A, Mater Des 106 (2016) 273.
Liu Q, Ke L, Liu F, Huang C, and Xing L, Mater Des 45 (2013) 343.
Sathiskumar R, Murugan N, Dinaharan I, and Vijay S J, Mater Charact 84 (2013)16.
Bauri R, Yadav D, Shyam Kumar C N, and Balaji B, Mater Sci Eng A 620 (2015) 67.
Ma Z Y, Metall Mater Trans A 39 (2008) 642.
Akramifard H R, Shamanian M, Sabbaghian M, and Esmailzadeh M, Mater Des 54(2014) 838.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Satish Kumar, T., Suganya Priyadharshini, G., Shalini, S. et al. Characterization of NbC-Reinforced AA7075 Alloy Composites Produced Using Friction Stir Processing. Trans Indian Inst Met 72, 1593–1596 (2019). https://doi.org/10.1007/s12666-019-01566-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-019-01566-7