Abstract
Sericite sample having potash (K2O) content ~ 9% was evaluated as a source of potash. The mineralogical studies revealed the fine grain structure of sericite containing muscovite, orthoclase, and phlogopite as the major potash bearing phases. The feed sample directly leached in different lixiviants yielded low potash dissolution values. Planetary ball milling was carried out to liberate the potash values from silicate matrix. It was observed that the K-bearing phases were quite stable, with milling action of about 8 h yielded ~ 30% values. The heat treatment of sericite with NaOH resulted in ~ 90% K-dissolution at optimum conditions (60% flux, 600 °C, 30 min) with the formation of sodium silicate and kalsilite. Mechanical activation had a positive effect on heat treatment kinetics as temperature decreased from 600 to 250 °C with ~ 100% potash recovery. CaCl2 and Na2CO3 were also evaluated as flux and based on a comparison of process variables and yield, NaOH was found to be the best flux.
Similar content being viewed by others
References
Amundson R, Berhe A A, Hopmans J W, Olson C, Sztein A E, and Sparks D L, Soil Sci 348 (2015) 647.
Ciceri D, Manning D A C, and Allanore A, Sci Total Environ 502 (2015) 590.
IBM, Indian Minerals Yearbook 2017 (Part- III: Mineral Reviews), 56th edn, Potash.
Jena S K, Dhawan N, Rao D S, Mishra B K, and Das B, Int J Miner Process 133 (2014) 13.
Santos W O, Mattiello E M, Marciano da Costa L, Abrahao W A P, Ferreira de Novais R, and Cantarutti R B, Int J Miner Process 140 (2015) 72.
Manning D A C, Nat Resour Res 27 (2017) 217.
Mazumder A K, Sharma T, and Rao T C, Int J Miner Process 38 (1993) 111.
Varadachari C, Ind Eng Chem Res, 36 (1997) 4768.
Jena S K, Dhawan N, Rao D S, and Das B, Sep Sci Technol 51 (2015) 269.
Ciceri D, Oliveira M D, and Allanore A, Green Chem, 19 (2017) 5187.
Shekhar S, Mishra D, Agarwal A, and Sahu K K, J Clean Prod 147 (2017) 681.
Rudmina M, Banerjee S, Mazurov A, Makarov B, and Martemyanovd D, Appl Clay Sci 150 (2017) 225.
Rudmina M, Oskinaa Y, Banerjee S, Mazurova A, Soktoeva B, and Shaldybina M, Appl Clay Sci 162 (2018) 121.
Shekhar S, Mishra D, Agarwal A, and Sahu K K, App Clay Sci 143 (2017) 50.
Eberl D D, Srodon J, Lee M, Nadeau P H, and Northrop H R, Am Miner 72 (1987) 914.
Shih Y J, and Shen Y H, Appl Clay Sci 43 (2009) 282.
Silvester E J, Heyes G W, Bruckard W J, and Woodcock J T, Miner Process Extr Metall 120 (2013) 10.
Wang H, Feng Q, Tang X, Zuo K, and Liu K, Minerals 7 (2017) 1.
Sreenivas B, Roy A B, Srinivasan R, Proc Indian Acad Sci (Earth Planet Sci), 110 (2001) 39.
IBM, Indian Minerals Yearbook 2016 (Part- I: General Reviews), 55th edn, State Reviews Madhya Pradesh.
Prasad C S, Mukhopadhyay T K, and Maiti K M, Trans Ceram Soc 48 (1989) 96.
Balaz P, Mechanochemistry in Nanoscience and Minerals Engineering, Springer, Berlin (2008), ISBN 3-540-74854-0.
Kleiv R A, and Thornhill M, Miner Eng 20 (2007) 334.
Williams, P J, and Cloete, T E, S Afr J Sci 106 (2010) 1.
Acknowledgements
The authors would like to acknowledge the funding received from Ministry of Mines (Grant No. MOM-1004-MMED) and Science Engineering Research Board (Grant No. SER-1052-MMED) to carry out the research work.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kumar, G., Tanvar, H., Pratap, Y. et al. Thermal and Mechanical Activation of Sericite for Recovery of Potash Values. Trans Indian Inst Met 72, 17–25 (2019). https://doi.org/10.1007/s12666-018-1452-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-018-1452-3