Construction of Phase Diagrams for AlxHfNbTaTiZr Refractory High Entropy Alloy

  • Sana Anilkumar
  • Regala Aneela
  • Vadali V. S. S. Srikanth
Technical paper
  • 92 Downloads

Abstract

This work involves construction of phase diagrams of AlxHfNbTaTiZr refractory high entropy alloy (RHEA) with an objective to understand the phase stability of the alloy at different concentrations of Al, which is expected to stabilize the body-centred cubic (BCC) structure. The constructed hexanal phase diagrams of AlxHfNbTaTiZr RHEA shows that continuous BCC solid solution forms up to 1.5 mol of initial concentration of Al and any further increase in the Al concentration results in the formation of intermetallic phases. Further, the phase stability of AlxHfNbTaTiZr RHEA as a function of Al concentration has been discussed in correlation with the concerned Valence Electron Concentration parameter.

Keywords

CALPHAD FactSage Hexanal isopleths High entropy alloy Refractory high entropy alloy 

Notes

Acknowledgements

The authors sincerely thank Dr. Koteswararao V Rajulapati (University of Hyderabad) for some inputs and useful scientific discussion.

References

  1. 1.
    Yeh J W, Chen S K, Lin S J, Gan J Y, Chin T S, Shun T T, Tsau C H, and Chang S Y, Adv Eng Mater 6 (2004) 299.CrossRefGoogle Scholar
  2. 2.
    Senkov O N, Senkova S V, Woodward C, and Miracle D B, Acta Mater 61 (2013) 1545.CrossRefGoogle Scholar
  3. 3.
    Senkov O N, Senkova S V, and Woodward C, Acta Mater 68 (2014) 214.CrossRefGoogle Scholar
  4. 4.
    Stepanov N D, Shaysultanov D G, Salishchev G A, and Tikhonovsky M A, Mater Lett 142 (2015) 153.CrossRefGoogle Scholar
  5. 5.
    Lin C M, Juan C C, Chang C H, Tsai C W, and Yeh W, J Alloys Compd 624 (2015) 100.CrossRefGoogle Scholar
  6. 6.
    Tazuddin, Gurao N P, and Krishanu B, J Alloys Compd 697 (2017) 434.CrossRefGoogle Scholar
  7. 7.
    Wu Y D, Cai Y H, Wang T, Si J J, Zhu J J, Wang Y D, and Hui X D, Mater Lett 130 (2014) 277.CrossRefGoogle Scholar
  8. 8.
    Yurchenko N Y, Stepanov N D, Shaysultanov D G, Tikhonovsky M A, and Salishchev G A, Mater Charact 9 (2016) 39.Google Scholar
  9. 9.
    Ma Y, Jiang B, Li C, Wang Q, Dong C, Liaw P K, Xu F, and Sun L, Metals 7 (2017) 57.CrossRefGoogle Scholar
  10. 10.
    Zhang F, Zhang C, Chen S L, Zhu J, Cao W S, and Kattner U R, Calphad 45 (2014) 1.CrossRefGoogle Scholar
  11. 11.
    Sheng G, and Liu C T, Prog Nat Sci Mater Int 21 (2011) 433.CrossRefGoogle Scholar
  12. 12.
    Mizutani U, Hume-Rothery Rules for Structurally Complex Alloy Phases, CRC Press, Boca Raton (2011).Google Scholar
  13. 13.
    Bale C W, Chartrand P, Degterov S A, Eriksson G, Hack K, Mahfoud R B, Melancon J, Petersen S, and Pelton A D, Calphad 26 (2002) 189.CrossRefGoogle Scholar

Copyright information

© The Indian Institute of Metals - IIM 2017

Authors and Affiliations

  1. 1.School of Engineering Sciences and TechnologyUniversity of HyderabadGachibowliIndia

Personalised recommendations