A New Approach for Using Interlayer and Analysis of the Friction Welding of Titanium to Stainless Steel

Technical Paper

Abstract

Dissimilar material joining is often more difficult than joining the similar material or alloys with minor differences in physical properties and composition. The formation of deleterious intermediate phases consisting of intermetallic compounds during welding of titanium and stainless steel is a challenge to the welding processes, for decades. Friction welding has been used in an attempt to reduce formation of intermetallic compounds through inserting an interlayer material. In recent years, a number of approaches have been developed to insert interlayer between the substrates to avoid the metallurgical incompatibility. In this research, dissimilar joint of titanium and stainless steel were welded effectively using a new technique of electrodeposited nickel coating on one of the substrate (stainless steel) as interlayer. The bonding interface of the joints was characterized using optical microscopy, scanning electron microscopy and energy dispersive spectroscopy. Tensile strength of the nickel interlayer joints was higher than the direct joints. The microstructural characterization in the interface of titanium and stainless steel showed the absence of brittle Fe–Ti intermetallic compounds, which was a condition attributed to the use of interlayer technique. Whereas, the characterization of interface were identified as the presence of Ti–Ni phases which were more plastic than Fe–Ti intermetallic compounds.

Keywords

Friction welding Titanium Nickel interlayer Stainless steel Intermetallic compounds Fractography 

Notes

Acknowledgements

The authors would like to acknowledge the grants received from Directorate of Naval R&D, Naval Research Board, New Delhi (DNRD/05/4003/NRB/126, dated 20.11.2007) for this research work.

References

  1. 1.
    Çam G, and Koçak M, Inter Mater Rev 43 (1998) 1.CrossRefGoogle Scholar
  2. 2.
    Muralimohan C H, Haribabu S, Hariprasada Reddy Y, Muthupandi V, and Sivaprasad K, Adv Mech Eng Sci 1 (2015) 57.CrossRefGoogle Scholar
  3. 3.
    Deng Y Q, Sheng G M, Huang Z H, and Fan L Z, Sci Technol Weld Join 18 (2013) 143.CrossRefGoogle Scholar
  4. 4.
    Peng H, Jiuhai Z, Ronglin Z, and Xiaoqiang L, Mater Character 43 (1999) 287.CrossRefGoogle Scholar
  5. 5.
    Kundu S, and Chatterjee S, Mater Character 59 (2008) 631.CrossRefGoogle Scholar
  6. 6.
    Murali Mohan C, Muthupandi V, and Loganathan S, Mater Sci Forum 710 (2012) 620.CrossRefGoogle Scholar
  7. 7.
    Li J L, Huo L P, Zhang F S, Xiong J T, and Li W Y, Mater Sci Forum 620–622 (2009) 399.Google Scholar
  8. 8.
    Kahraman N, Gulence B, and Findik F, J Mater Process Technol 169 (2005) 127.CrossRefGoogle Scholar
  9. 9.
    Qin B, Sheng G M, Huang J W, Zhou B, Qiu S Y, and Li C, Mater Character 56 (2006) 32.CrossRefGoogle Scholar
  10. 10.
    Dey H C, Ashfaq M, Bhaduri A K, and Prasad Rao K, J Mater Proc Technol 209 (2009) 5862.CrossRefGoogle Scholar
  11. 11.
    Khalid Rafi H, Janaki Ram G D, Phanikumar G, and Prasad Rao K, Mater Des 31 (2010) 2375.CrossRefGoogle Scholar
  12. 12.
    Muralimohan C H, Haribabu S, Hariprasada Reddy Y, Muthupandi V, and Sivaprasad K, Procedia Mater Sci 5 (2014) 1107.CrossRefGoogle Scholar
  13. 13.
    Pokataev E P, and Trykov YP, Weld Inter 15 (2001) 827.CrossRefGoogle Scholar
  14. 14.
    Kundu S, Ghosh M, and Chatterjee S, ISIJ Int 44 (2004) 1882.CrossRefGoogle Scholar
  15. 15.
    Muralimohan C H, Muthupandi V, and Sivaprasad K, Procedia Mater Sci 5 (2014) 1120.CrossRefGoogle Scholar
  16. 16.
    Muralimohan C H, and Muthupandi V, Adv Mater Res 794 (2013) 351.CrossRefGoogle Scholar
  17. 17.
    He P, Zhang J, Zhou R, and Li X, Mater Character 43 (1999) 287.CrossRefGoogle Scholar
  18. 18.
    Muralimohan C H, Ashfaq M, Ashiri R, Muthupandi V, and Sivaprasad K, Metall Mater Trans A 47 (2016) 347.CrossRefGoogle Scholar
  19. 19.
    Torun O, Karabulut A, Baksan B, and Çelikyürek I, Mater Des 29 (2008) 2043.CrossRefGoogle Scholar
  20. 20.
    Muralimohan C H, Muthupandi V, and Sivaprasad K, Inter J Mater Res 105 (2014) 350.CrossRefGoogle Scholar
  21. 21.
    Ochi H, Ogawa K, Yamamoto Y, and Suga Y, Weld J 83 (2004) 36.Google Scholar
  22. 22.
    Lee W-B, Kim Y-J, and Jung S-B, Intermetallics 12 (2004) 671.CrossRefGoogle Scholar
  23. 23.
    Fuji A, North T H, Ameyama K, and Futamata M, Mater Sci Technol 8 (1992) 219.CrossRefGoogle Scholar
  24. 24.
    Ates H, and Kaya N, Arch Metall Mater 59 (2014) 841.CrossRefGoogle Scholar
  25. 25.
    Peng L, Jinglong L, Muhammad S, Li L, Jiangtao X, and Fusheng Z, Mater Des 56 (2014) 649.CrossRefGoogle Scholar
  26. 26.
    Özdemir N, Sarsılmaz F, and Hasçalık A, Mater Des 28 (2007) 301.CrossRefGoogle Scholar
  27. 27.
    Yılmaz M, Çöl M, and Acet M, Mater Character 49 (2002) 421.CrossRefGoogle Scholar
  28. 28.
    Massalski T B, Binary Alloy Phase Diagrams, Second ed, ASM International, Materials Park (1996).Google Scholar
  29. 29.
    Muralimohan C H, and Muthupandi V, International Symposium on Joining of Materials, India (2012) p 1.Google Scholar
  30. 30.
    Fuji A, Horiuchi Y, and Yamamoto K, Sci Technol Weld Join 10 (2005) 287.CrossRefGoogle Scholar
  31. 31.
    Sassani F, and Neelam J R, Weld Res Suppl 333 (1988) 264.Google Scholar

Copyright information

© The Indian Institute of Metals - IIM 2017

Authors and Affiliations

  1. 1.Department of Advanced Materials and Industrial Management EngineeringDong-Eui UniversityBusanRepublic of Korea
  2. 2.FARCAMT, Advanced Manufacturing InstituteKing Saud UniversityRiyadhSaudi Arabia
  3. 3.Department of Metallurgical and Materials EngineeringNational Institute of TechnologyTiruchirappalliIndia

Personalised recommendations