Performance of the MCM-41-NH2 Functionalized Mesoporous Material Synthetized from the Rice Husk Ash on the Removal of the Polycyclic Aromatic Hydrocarbons

Abstract

In this work, the authors propose of the synthesis of a new adsorbent functionalized mesoporous material (MCM-41-NH2 (RHA)) from the Brazilian rice husk for the removal of the polycyclic aromatic hydrocarbons (PAHs). The new MCM-41-NH2 (RHA) was characterized using FTIR, TGA, SAXS, and N2 adsorption-desorption analyses, on the other hand, the removal experiments were performed to determine the adsorption parameters, such as the initial concentration, MCM-41-NH2 (RHA) amount, pH, time, and temperature. The hydrothermal/post-grafting methods were sustainable for the synthesis of the MCM-41-NH2 (RHA) functionalized mesoporous material, the same presented the main characteristic absorption bands of the mesoporous arrays, hexagonal mesostructure, type IV isotherms with H1 hysteresis, high surface area, and good thermal stability. Assessment of the adsorption of the MCM-41-NH2 (RHA) showed that the amount of the PAHs mixture adsorbed increased with the increase of the initial concentration, MCM-41-NH2 (RHA) amount, and contact time, as well as, the pH = 5.6 was the best for the removal of the PAHs mixture. However, the temperature variation did not significantly alter the efficiency of the MCM-41-NH2 (RHA). The removal percentage of the PAHs were 81.20, 94.25, 94.87, and 98.14% for the naphthalene (Nap), benzo[a]pyrene (B[a]P), benzo[k]fluoranthene (B[k]F), and benzo[b]fluoranthene (B[b]F), respectively, with the equilibrium time of approximately 200 min for the all PAHs. In addition, the adsorption equilibrium followed the nonlinear pseudo-second-order and the Langmuir models, which describe satisfactory adsorption of the PAHs mixture on the MCM-41-NH2 (RHA) functionalized mesoporous material.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    Busso IT, Tames F, Silva JA et al (2018) Biomonitoring levels and trends of PAHs and synthetic musks associated with land use in urban environments. Sci Total Environ 618:93–100. https://doi.org/10.1016/j.scitotenv.2017.10.295

    CAS  Article  Google Scholar 

  2. 2.

    Hindersmann B, Achten C (2018) Urban soils impacted by tailings from coal mining: PAH source identification by 59 PAHs, BPCA and alkylated PAHs. Environ Pollut 242:1217–1225. https://doi.org/10.1016/j.envpol.2018.08.014

    CAS  Article  PubMed  Google Scholar 

  3. 3.

    Costa JAS, Garcia ACFS, Santos DO et al (2014) A new functionalized MCM-41 mesoporous material for use in environmental applications. J Braz Chem Soc 25:197–207. https://doi.org/10.5935/0103-5053.20130284

    CAS  Article  Google Scholar 

  4. 4.

    Costa JAS, Garcia ACFS, Santos DO, Sarmento VHV, Mesquita ME, Romão LPC (2015) Applications of inorganic-organic mesoporous materials constructed by self-assembly processes for removal of benzo[k]fluoranthene and benzo[b]fluoranthene. J Sol-Gel Sci Technol 75:495–507. https://doi.org/10.1007/s10971-015-3720-6

    CAS  Article  Google Scholar 

  5. 5.

    da Costa CG, Pinho NC, Alves Silva IA et al (2019) Removal of heavy crude oil from water surfaces using a magnetic inorganic-organic hybrid powder and membrane system. J Environ Manag 247:9–18. https://doi.org/10.1016/j.jenvman.2019.06.050

    CAS  Article  Google Scholar 

  6. 6.

    Brasil (2011) Ministério da Saúde. Portaria MS No 2914 12 Dezembro 2011 2011:32

  7. 7.

    U.S. EPA (1993) Provisional Guidance forQuantitative Risk Assessment of Polycyclic Aromatic Hydrocarbons. EPA/600/R-:1–28

  8. 8.

    Conama (2005) Resolução n 357, 18 de março de 2005. Diário Of 58–63

  9. 9.

    IARC (2010) IARC monographs on the evaluation of carcinogenic risks to humans: some non-heterocyclic polycyclic aromatic hydrocarbons and some related exposures. IARC Monogr Eval Carcinog Risks Hum 92:1–868

    Google Scholar 

  10. 10.

    Meng Y, Lu S, Zhou J et al (2019) A review on occurrence and risk of polycyclic aromatic hydrocarbons (PAHs) in lakes of China. Sci Total Environ 651:2497–2506. https://doi.org/10.1016/j.scitotenv.2018.10.162

    CAS  Article  PubMed  Google Scholar 

  11. 11.

    Kang Y, Xie H, Li B et al (2018) Performance of constructed wetlands and associated mechanisms of PAHs removal with mussels. Chem Eng J 357:280–287. https://doi.org/10.1016/j.cej.2018.09.152

    CAS  Article  Google Scholar 

  12. 12.

    Santos LFS, de Jesus RA, Costa JAS et al (2019) Evaluation of MCM-41 and MCM-48 mesoporous materials as sorbents in matrix solid phase dispersion method for the determination of pesticides in soursop fruit (Annona muricata). Inorg Chem Commun 101:45–51. https://doi.org/10.1016/j.inoche.2019.01.013

    CAS  Article  Google Scholar 

  13. 13.

    Costa JAS, de Jesus RA, da Silva CMP, Romão LPC (2017) Efficient adsorption of a mixture of polycyclic aromatic hydrocarbons (PAHs) by Si–MCM–41 mesoporous molecular sieve. Powder Technol 308:434–441. https://doi.org/10.1016/j.powtec.2016.12.035

    CAS  Article  Google Scholar 

  14. 14.

    Costa JAS, de Jesus RA, Dorst DD et al (2017) Photoluminescent properties of the europium and terbium complexes covalently bonded to functionalized mesoporous material PABA-MCM-41. J Lumin 192:1149–1156. https://doi.org/10.1016/j.jlumin.2017.08.046

    CAS  Article  Google Scholar 

  15. 15.

    Santos DO, Santos MLN, Costa JAS et al (2013) Investigating the potential of functionalized MCM-41 on adsorption of Remazol Red dye. Environ Sci Pollut Res 20:5028–5035. https://doi.org/10.1007/s11356-012-1346-6

    CAS  Article  Google Scholar 

  16. 16.

    Costa JAS, Vedovello P, Paranhos CM (2019) Use of ionic liquid as template for hydrothermal synthesis of the MCM-41 mesoporous material. Silicon. https://doi.org/10.1007/s12633-019-00121-9

  17. 17.

    FAO (2018) Production international trade domestic prices. Rice Mark Monit XXI:1–35

  18. 18.

    Costa JAS, Paranhos CM (2018) Systematic evaluation of amorphous silica production from rice husk ashes. J Clean Prod 192:688–697. https://doi.org/10.1016/j.jclepro.2018.05.028

    CAS  Article  Google Scholar 

  19. 19.

    Costa JAS, Paranhos CM (2019) Evaluation of rice husk ash in adsorption of Remazol Red dye from aqueous media. SN Appl Sci 1:1–8. https://doi.org/10.1007/s42452-019-0436-1

    CAS  Article  Google Scholar 

  20. 20.

    Shylesh S, Singh A (2004) Synthesis, characterization, and catalytic activity of vanadium-incorporated, -grafted, and -immobilized mesoporous MCM-41 in the oxidation of aromatics. J Catal 228:333–346. https://doi.org/10.1016/j.jcat.2004.08.037

    CAS  Article  Google Scholar 

  21. 21.

    Dai X, Qiu F, Zhou X et al (2014) Amino-functionalized MCM-41 for the simultaneous electrochemical determination of trace lead and cadmium. Electrochim Acta 144:161–167. https://doi.org/10.1016/j.electacta.2014.08.093

    CAS  Article  Google Scholar 

  22. 22.

    Costa JAS, Sarmento VHV, Romão LPC, da Silva CMP (2019) Adsorption of organic compounds on mesoporous material from rice husk ash (RHA). Biomass Convers Biorefinery

  23. 23.

    Costa JAS, Sarmento VHV, Romão LPC, Paranhos CM (2019) Synthesis of functionalized mesoporous material from rice husk ash and its application in the removal of the polycyclic aromatic hydrocarbons. Environ Sci Pollut Res. https://doi.org/10.1007/s11356-019-05852-1

  24. 24.

    Luo G, Kang L, Zhu M, Dai B (2014) Highly active phosphotungstic acid immobilized on amino functionalized MCM-41 for the oxidesulfurization of dibenzothiophene. Fuel Process Technol 118:20–27. https://doi.org/10.1016/j.fuproc.2013.08.001

    CAS  Article  Google Scholar 

  25. 25.

    Balati A, Shahbazi A, Amini MM, Hashemi SH (2015) Adsorption of polycyclic aromatic hydrocarbons from wastewater by using silica-based organic–inorganic nanohybrid material. J Water Reuse Desalin 5:50. https://doi.org/10.2166/wrd.2014.013

    CAS  Article  Google Scholar 

  26. 26.

    Costa AA, Wilson WB, Wang H et al (2012) Comparison of BEA, USY and ZSM-5 for the quantitative extraction of polycyclic aromatic hydrocarbons from water samples. Microporous Mesoporous Mater 149:186–192. https://doi.org/10.1016/j.micromeso.2011.06.016

    CAS  Article  Google Scholar 

  27. 27.

    Liu JJ, Wang XC, Fan B (2011) Characteristics of PAHs adsorption on inorganic particles and activated sludge in domestic wastewater treatment. Bioresour Technol 102:5305–5311. https://doi.org/10.1016/j.biortech.2010.12.063

    CAS  Article  PubMed  Google Scholar 

  28. 28.

    Almeida CAP, Debacher NA, Downs AJ, Cottet L, Mello CA (2009) Removal of methylene blue from colored effluents by adsorption on montmorillonite clay. J Colloid Interface Sci 332:46–53. https://doi.org/10.1016/j.jcis.2008.12.012

    CAS  Article  PubMed  Google Scholar 

  29. 29.

    Cottet L, Almeida CAP, Naidek N et al (2014) Adsorption characteristics of montmorillonite clay modified with iron oxide with respect to methylene blue in aqueous media. Appl Clay Sci 95:25–31. https://doi.org/10.1016/j.clay.2014.03.023

    CAS  Article  Google Scholar 

  30. 30.

    Özcan AS, Özcan A (2004) Adsorption of acid dyes from aqueous solutions onto acid-activated bentonite. J Colloid Interface Sci 276:39–46. https://doi.org/10.1016/j.jcis.2004.03.043

    CAS  Article  PubMed  Google Scholar 

  31. 31.

    Wang N, Jin RN, Omer AM, Ouyang XK (2017) Adsorption of Pb(II) from fish sauce using carboxylated cellulose nanocrystal: isotherm, kinetics, and thermodynamic studies. Int J Biol Macromol 102:232–240. https://doi.org/10.1016/j.ijbiomac.2017.03.150

    CAS  Article  PubMed  Google Scholar 

Download references

Acknowledgments

The authors thank FAPESP (Research Support Foundation of the State of São Paulo) (Grants 2014/05679-4, 2017/06775-5, and 2018/18894-1), CAPES (Coordination for the Improvement of Higher Education Personnel) (Grant 309342/2010-4), and CDMF (Center for the Development of Functional Materials) (Grant 2013/07296-2) for the financial support and LNLS for the SAXS measurements (Project SAXS1 12642).

Author information

Affiliations

Authors

Corresponding author

Correspondence to José A. S. Costa.

Ethics declarations

Conflict of Interest

The authors declare that they have no conflict of interest.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Costa, J.A.S., Sarmento, V.H.V., Romão, L.P.C. et al. Performance of the MCM-41-NH2 Functionalized Mesoporous Material Synthetized from the Rice Husk Ash on the Removal of the Polycyclic Aromatic Hydrocarbons. Silicon 12, 1913–1923 (2020). https://doi.org/10.1007/s12633-019-00289-0

Download citation

Keywords

  • Rice husk ash
  • Functionalized mesoporous material
  • MCM-41-NH2 (RHA)
  • Adsorption
  • PAHs mixture