Evidence of Electrochemical Resistance on Ternary V-C-N Layers
- 2 Downloads
In this research, vanadium carbo-nitride (VCN) coatings were synthesized via physical vapor deposition with the aim to determinate the electrochemical behavior of the VCN layers on industrial steel substrates. The VCN coatings, deposited at various negative bias voltage were characterized by X-ray diffraction (XRD), exhibiting the crystallography orientations corresponding to a mix of VCN, VC and VN phases while the X-ray photoelectron spectroscopy (XPS) measurements were used to determinate the chemical composition of the metallic carbon-nitride materials. By using electrochemical impedance spectroscopy (EIS) and Tafel curves, it was possible to estimate the electrochemical behavior of the VCN coatings in a sodium chloride (NaCl) solution. Moreover, scanning electron microscopy (SEM) was performed to analyze morphological and chemical surfaces changes on the VCN layer due to the reaction in NaCl/VCN/steel surface interface. The electrochemical behavior of the VCN coatings in relation to the uncoated AISI 8620 steel showed a reduction of 98% in the corrosion rate, indicating that the applied VCN coatings may be a promising material for industrial applications.
KeywordsVCN coatings Corrosion resistance Industrial applications
Unable to display preview. Download preview PDF.
This research was supported by the Universidad Militar Nueva Granada, Colombia, contract number ING-1775-2015 and the Universidad del Quindío, Colombia.
- 8.Lewin E, Persson P, Lattemann M, Stuber M, Gorgoi M, Sandell A, Ziebert C, Schafers F, Braun W, Halbritter J, Ulrich S, Eberhardt W, Hultman L, Siegbahn H, Svensson S, Jansson U (2008) On the origin of a third spectral component of C1s XPS-spectra for nc-TiC/aC nanocomposite thin films. Surf Coat Technol 202:3563–3570CrossRefGoogle Scholar
- 9.Anthony MD, Lad RJ, Christensen TM (1996) Surface structure of crystalline ceramics. Surf Interface Anal 24:681Google Scholar
- 28.Moreno C, Hernández S, Santana JJ, González Guzmán J, Souto RM, González S (2012) Characterization of water uptake by organic coatings used for the corrosion protection of steel as determined from capacitance measurements. Int J Electrochem Sci 7:8444–8457Google Scholar