Tuning oxygen vacancies in two-dimensional iron-cobalt oxide nanosheets through hydrogenation for enhanced oxygen evolution activity
- 515 Downloads
The oxygen evolution reaction (OER) represents the rate-determining step of electrocatalytic water splitting into hydrogen and oxygen. Creating oxygen vacancies and adjusting their density has proven to be an effective strategy to design high-performance OER catalysts. Herein, a hydrogenation method is applied to treat a two-dimensional (2D) iron-cobalt oxide (Fe1Co1Ox-origin), with the purpose of tuning its oxygen vacancy density. Notably, compared with Fe1Co1Ox-origin, the iron-cobalt oxide hydrogenated at 200 °C and 2.0 MPa optimized conditions exhibits a markedly improved OER activity in 1.0 M KOH (with an overpotential η of 225 mV at a current density of 10 mA·cm–2) and a rapid reaction kinetics (with a Tafel slope of 36.0 mV·dec–1). Moreover, the OER mass activity of the hydrogenated oxide is 1.9 times that of Fe1Co1Ox-origin at an overpotential of 350 mV. The experimental results, combined with density functional theory (DFT) calculations, reveal that the optimal control of oxygen vacancies in 2D Fe1Co1Ox via hydrogenation can improve the electronic conductivity and promote OH– adsorption onto nearby low-coordinated Co3+ sites, resulting in a significantly enhanced OER activity.
Keywordshydrogenation tuning oxygen vacancy oxygen evolution reaction
Unable to display preview. Download preview PDF.
The financial support from ARC is highly appreciated, through ARC Discovery Project (No. DP170103317), ARC Future Fellowship (No. FT120100720) and ARC Discovery Early Career Researcher Award (No. ARC DE180101030). L. Z. Z. acknowledges the support from International Postgraduate Research Scholarship (IPRS) and UQ Centennial Scholarship (UQCent). The authors acknowledge the scientific and technical assistance of the Australian Microscopy and Microanalysis Research Facility at the UQ Centre.
- Jia, X. D.; Zhao, Y. F.; Chen, G. B.; Shang, L.; Shi, R.; Kang, X. F.; Waterhouse, G. I. N.; Wu, L. Z.; Tung C.-H.; Zhang, T. R. Ni3FeN nanoparticles derived from ultrathin NiFe-layered double hydroxide nanosheets: An efficient overall water splitting electrocatalyst. Adv. Energy Mater. 2016, 6, 1502585.CrossRefGoogle Scholar
- Jia, Y. Zhang, L. Z.; Gao, G. P.; Chen, H.; Wang, B.; Zhou, J. Z.; Soo, M. T.; Hong, M.; Yan, X. C.; Qian, G. R. et al. A heterostructure coupling of exfoliated Ni-Fe hydroxide nanosheet and defective graphene as a bifunctional electrocatalyst for overall water splitting. Adv. Mater. 2017, 29, 1700017.CrossRefGoogle Scholar
- Li, Y. B.; Zhang, H. M.; Wang, Y.; Liu, P. R.; Yang, H. G.; Yao, X. D.; Wang, D.; Tang, Z. Y.; Zhao, H. J. A selfsponsored doping approach for controllable synthesis of S and N co-doped trimodal-porous structured graphitic carbon electrocatalysts. Energy Environ. Sci. 2014, 7, 3720–3726.CrossRefGoogle Scholar
- Li, H.; Tsai, C.; Koh, A. L.; Cai, L. L.; Contryman, A. W.; Fragapane, A. H.; Zhao, J. H.; Han, H. S.; Manoharan, H. C.; Abild-Pedersen, F. et al. Activating and optimizing MoS2 basal planes for hydrogen evolution through the formation of strained sulphur vacancies. Nat. Mater. 2016, 15, 48–53.CrossRefGoogle Scholar
- Hadt, R. G.; Hayes, D.; Brodsky, C. N.; Ullman, A. M.; Casa, D. M.; Upton, M. H.; Nocera, D. G.; Chen, L. X. X-ray spectroscopic characterization of Co(IV) and metal-metal interactions in Co4O4: Electronic structure contributions to the formation of high-valent states relevant to the oxygen evolution reaction. J. Am. Chem. Soc. 2016, 138, 11017–11030.CrossRefGoogle Scholar
- Chen, J. M.; Chin, Y. Y.; Valldor, M.; Hu, Z. W.; Lee, J. M.; Haw, S. C.; Hiraoka, N.; Ishii, H.; Pao, C. W.; Tsuei, K. D. et al. A complete high-to-low spin state transition of trivalent cobalt ion in octahedral symmetry in SrCo0.5Ru0.5O3–δ. J. Am. Chem. Soc. 2014, 136, 1514–1519.CrossRefGoogle Scholar