Sunlight-enhanced catalytic degradation over Ag–CuO nanoparticles thin films prepared by DC/RF sputtering technique

  • Waleed M A El Rouby
  • Attieh A Al-Ghamdi
  • M Sh Abdel-wahab
  • Asim Jilani
Article

Abstract

Herein, we report sunlight-activated photo-catalysis response of direct current radio frequency (DC/RF)-sputtered Ag–CuO nanoparticles thin films. We have adopted this approach for facile removal and easy recovery of thin films after use. Ag was incorporated at 2.5 and 5.4 wt% with reference to pure CuO. Structural analysis through X-ray diffraction showed successful incorporation of Ag into the CuO lattice. Surface morphological observation was carried out using a field emission scanning electron microscope, which showed a uniform deposition of the subjected thin films. The surface composition and change in the chemical state of pure and incorporated thin films were studied by X-ray photoelectron spectroscopy. In addition to structural and surface analysis, optical band gap evolution was also studied through UV–visible spectroscopy. The obtained results reflected that optical band gap decreased from 1.84 to 1.77 and 1.61 eV for 0, 2.5 and 5.4 wt% Ag, respectively. Methylene blue dye was used to investigate the photo-catalytic degradation response of deposited thin films in sunlight. Furthermore, the effect of pH and dye concentration was also taken into account. The degradation results indicate the acceleration of degradation process with the Ag incorporation into CuO lattice. Moreover, the pH also contributes positively to the degradation progression. This research study could provide a platform to understand and develop metal oxide thin films with an efficient photo-catalytic response in sunlight.

Keywords

CuO silver nanoparticles photo-catalysis thin films Methylene blue 

Notes

Acknowledgements

We acknowledge financial support from the Science and Technology Development Fund, Egypt (4435, 14790). We are also grateful to Faculty of Postgraduate Studies For Advanced Science, Egypt, and Center of Nanotechnology, King Abdulaziz University, Saudi Arabia, for providing all facilities for this work.

References

  1. 1.
    Konstantinou I K and Albanis T A 2004 Appl. Catal. B 49 1CrossRefGoogle Scholar
  2. 2.
    Tang W Z and An H 1995 Chemosphere 31 4157CrossRefGoogle Scholar
  3. 3.
    Farghali A, Bahgat M, El Rouby W and Khedr M 2012 J. Solution Chem. 41 2209CrossRefGoogle Scholar
  4. 4.
    Unterlass M M 2016 Eur. J. Inorg. Chem. 2016 1135CrossRefGoogle Scholar
  5. 5.
    El Rouby W, Farghali A and Hamdedein A 2016 Water Sci. Technol. 74 2325CrossRefGoogle Scholar
  6. 6.
    Aslam M, Ismail I M, Almeelbi T, Salah N, Chandrasekaran S and Hameed A 2014 Chemosphere 117 115CrossRefGoogle Scholar
  7. 7.
    Carp O, Huisman C L and Reller A 2004 Prog. Solid State Chem. 32 33CrossRefGoogle Scholar
  8. 8.
    Akpan U and Hameed B 2009 J. Hazard Mater. 170 520CrossRefGoogle Scholar
  9. 9.
    Umadevi M and Christy A J 2013 Spectrochim. Acta Part A 109 133CrossRefGoogle Scholar
  10. 10.
    Tamuly C, Hazarika M, Das J, Bordoloi M, Borah D J and Das M R 2014 Mater. Lett. 123 202CrossRefGoogle Scholar
  11. 11.
    Tadjarodi A, Akhavan O and Bijanzad K 2015 Trans. Nonferrous Met. Soc. China 25 3634CrossRefGoogle Scholar
  12. 12.
    Ahumada-Lazo R, Torres-Martínez L, Ruíz-Gómez M, Vega-Becerra O and Figueroa-Torres M 2014 Appl. Surf. Sci. 322 35CrossRefGoogle Scholar
  13. 13.
    Vaiano V, Sacco O, Sannino D and Ciambelli P 2015 Appl. Catal. B 170 153CrossRefGoogle Scholar
  14. 14.
    Bensouici F, Souier T, Dakhel A, Iratni A, Tala-Ighil R and Bououdina M 2015 Superlattices Microstruct. 85 255CrossRefGoogle Scholar
  15. 15.
    Kumar R, Rashid J and Barakat M 2015 Colloids Interface Sci. Commun. 5 1Google Scholar
  16. 16.
    Al-Ghamdi A A, Khedr M, Ansari MS, Hasan P, Abdel-Wahab M S and Farghali A 2016 Physica E 81 83CrossRefGoogle Scholar
  17. 17.
    Das S and Alford T 2013 J. Appl. Phys. 113 244905CrossRefGoogle Scholar
  18. 18.
    Jilani A, Abdel-Wahab M S, Al-Ghamdi A A, Sadik Dahlan A and Yahia I 2016 Physica B 481 97CrossRefGoogle Scholar
  19. 19.
    Al-Ghamdi A A, Alhumminay H, Abdel-Wahab M S and Yahia I S 2016 Optik 127 4324CrossRefGoogle Scholar
  20. 20.
    Mogal S I, Gandhi V G, Mishra M, Tripathi S, Shripathi T, Joshi P A et al 2014 Ind. Eng. Chem. Res. 53 5749CrossRefGoogle Scholar
  21. 21.
    Chervinskii S, Matikainen A, Dergachev A, Lipovskii A A and Honkanen S 2014 Nanoscale Res. Lett. 9 398CrossRefGoogle Scholar
  22. 22.
    Son M S, Im J E, Wang K K, Oh S L, Kim Y R and Yoo K H 2010 Appl. Phys. Lett. 96 023115CrossRefGoogle Scholar
  23. 23.
    Kim D K and Park C B 2014 J. Mater. Sci. Mater. Electron. 25 1589CrossRefGoogle Scholar
  24. 24.
    Abdel-Wahab M S, Jilani A, Yahia I S and Al-Ghamdi A A 2016 Superlattices Microstruct. 94 108CrossRefGoogle Scholar
  25. 25.
    Ehrenreich H and Spaepen F 2001 Solid State Physics, vol 56 (Amsterdam, Netherlands: Elsevier Publisher)Google Scholar
  26. 26.
    Shinde S L and Nanda K K 2012 RSC Adv. 2 3647CrossRefGoogle Scholar
  27. 27.
    Zhang X, Qin J, Xue Y, Yu P, Zhang B, Wang L et al 2014 Sci. Rep. 4 4596Google Scholar
  28. 28.
    Zhao Z, Zhang X, Zhang G, Liu Z, Qu D, Miao X et al 2015 Nano Res. 8 4061CrossRefGoogle Scholar
  29. 29.
    Kong H and Jang J 2008 Biomacromolecules 9 2677CrossRefGoogle Scholar
  30. 30.
    Yang H, Lan Y, Zhu W, Li W, Xu D, Cui J et al 2012 J. Mater. Chem. 22 16994CrossRefGoogle Scholar
  31. 31.
    Tang J, Zou Z and Ye J 2005 Res. Chem. Intermed. 31 513CrossRefGoogle Scholar
  32. 32.
    Bubacz K, Choina J, Dolat D and Morawski A W 2010 Polish J. Environ. 19 685Google Scholar
  33. 33.
    Al-Ghamdi A A, Abdel-Wahab M S, Farghali A and Hasan P 2016 Mater. Res. Bull. 75 71CrossRefGoogle Scholar

Copyright information

© Indian Academy of Sciences 2018

Authors and Affiliations

  • Waleed M A El Rouby
    • 1
  • Attieh A Al-Ghamdi
    • 2
    • 3
  • M Sh Abdel-wahab
    • 1
    • 2
  • Asim Jilani
    • 2
  1. 1.Materials Science and Nanotechnology Department, Faculty of Postgraduate Studies for Advanced SciencesBeni-Suef UniversityBeni-SuefEgypt
  2. 2.Center of NanotechnologyKing Abdulaziz UniversityJeddahSaudi Arabia
  3. 3.Department of Physics, Faculty of ScienceUniversity of JeddahJeddahSaudi Arabia

Personalised recommendations