Advanced Mechanical Properties of a Powder Metallurgy Ti-Al-N Alloy Doped with Ultrahigh Nitrogen Concentration
- 219 Downloads
Titanium and its alloys are recognized for their attractive properties. However, high-performance Ti alloys are often alloyed with rare or noble-metal elements. In the present study, Ti alloys doped with only ubiquitous elements were produced via powder metallurgy. The experimental results showed that pure Ti with 1.5 wt.% AlN incorporated exhibited excellent tensile properties, superior to similarly extruded Ti-6Al-4V. Further analysis revealed that its remarkably advanced strength could primarily be attributed to nitrogen solid-solution strengthening, accounting for nearly 80% of the strength increase of the material. In addition, despite the ultrahigh nitrogen concentration up to 0.809 wt.%, the Ti-1.5AlN sample showed elongation to failure of ~ 10%. This result exceeds the well-known limitation for nitrogen (over 0.45 wt.%) that causes embrittlement of Ti alloys.
This work was partially supported by the Japan Science and Technology Agency (JST) under Industry–Academia Collaborative R&D Program “Heterogeneous Structure Control: Towards Innovative Development of Metallic Structural Materials.”
- 5.G. Lütjering and J.C. Williams, Titanium, 2nd ed. (Berlin: Springer, 2007).Google Scholar
- 9.K. Kondoh, B. Sun, S. Li, H. Imai, and J. Umeda, Int. J. Powder Metall. 50, 35 (2014).Google Scholar
- 26.R.I. Jaffee, H.R. Ogden, and D.J. Maykuth, Trans. AIME 188, 1261 (1950).Google Scholar