Impact of Reversed Austenite on the Impact Toughness of the High-Strength Steel of Low Carbon Medium Manganese
- 262 Downloads
We elucidate the relationship between the volume fraction of austenite and the Charpy impact toughness in a medium-Mn steel in terms of microstructural evolution with impact temperature. Different from retained austenite in the matrix after direct quenching, sub-micron lath-shaped morphology-reversed austenite in medium-Mn steel was produced by intercritical annealing. We found that reversed austenite steadily affected the fracture mode; only ductile fractures and dimples decreased with decreasing impact temperature. After the impact fracture test, the content of reversed austenite in the matrix increased slightly with a decreasing impact temperature due to the stability of the austenite grains caused by recrystallization of α′ martensite. Reversed austenite slightly decreased during the impact process with a decreasing impact temperature.
The authors gratefully appreciate the financial support by the National High-tech R&D Program (863 Program) No. 2015AA03A501.
This study was funded by the National High-tech R&D Program (863 Program) (No. 2015AA03A501).
Conflict of interest
The authors declare that they have no conflict of interest.
- 18.C.M. Enloe, J.P. Singh and J.J. Coryell, in Proceedings of the International Symposium on New Developments in Advanced High-Strength Sheet Steels (Keystone, CO, USA: Association for Iron & Steel Technology, Warrendale, PA, 2017), pp. 1–10Google Scholar
- 19.G.Q. Su, X.H. Gao, L.X. Du, D.Z. Zhang, J. Hu, and Z.G. Liu, Int. J. Electrochem. Sci. 11, 9447 (2017).Google Scholar
- 21.ISO 6892-1, Metallic Materials-tensile Testing-Part 1: Method of Test at Room Temperature (2009)Google Scholar