, Volume 10, Issue 4, pp 428–431 | Cite as

Microstructure and inclusion of Ti–6Al–4V fabricated by selective laser melting

  • Qianli Huang
  • Ningmin Hu
  • Xing Yang
  • Ranran Zhang
  • Qingling Feng
Communication

Abstract

Selective laser melting (SLM) was used in fabricating the dense part from pre-alloyed Ti-6Al-4V powder. The microstructural evolution and inclusion formation of as-fabricated part were characterized in depth. The microstructure was characterized by features of columnar prior β grains and acicular martensite α'. High density defects such as dislocations and twins can be produced in SLM process. Investigations on the inclusions find out that hard alpha inclusion, amorphous CaO and microcrystalline Al2O3 are three main inclusions formed in SLM. The inclusions formed at some specific sites on melt pool surface. The microstructural evolution and inclusion formation of as-fabricated material are closely related to the SLM process.

Keywords

metals and alloys laser processing microstructure inclusion 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Xin X, Xiang N, Chen J, et al. In vitro biocompatibility of Co–Cr alloy fabricated by selective laser melting or traditional casting techniques. Materials Letters, 2012, 88: 101–103CrossRefGoogle Scholar
  2. [2]
    Thijs L, Verhaeghe F, Craeghs T, et al. A study of the microstructural evolution during selective laser melting of Ti–6Al–4V. Acta Materialia, 2010, 58(9): 3303–3312CrossRefGoogle Scholar
  3. [3]
    Simonelli M, Tse Y Y, Tuck C. On the texture formation of selective laser melted Ti–6Al–4V. Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 2014, 45(6): 2863–2872CrossRefGoogle Scholar
  4. [4]
    Murr L E, Quinones S A, Gaytan S M, et al. Microstructure and mechanical behavior of Ti–6Al–4V produced by rapid-layer manufacturing, for biomedical applications. Journal of the Mechanical Behavior of Biomedical Materials, 2009, 2(1): 20–32CrossRefGoogle Scholar
  5. [5]
    Manero J M, Gil F J, Planell J A. Deformation mechanisms of Ti–6Al–4V alloy with a martensitic microstructure subjected to oligocyclic fatigue. Acta Materialia, 2000, 48(13): 3353–3359CrossRefGoogle Scholar
  6. [6]
    Vandenbroucke B, Kruth J P. Selective laser melting of biocompatible metals for rapid manufacturing of medical parts. Rapid Prototyping Journal, 2007, 13(4): 196–203CrossRefGoogle Scholar
  7. [7]
    Sears JW. Current processes for the cold-wall melting of titanium. JOM, 1990, 42(3): 17–21CrossRefGoogle Scholar
  8. [8]
    Cotton J, Clark L, Phelps H. Titanium investiment casting defects: A metallographic overview. JOM, 2006, 58(6): 13–16CrossRefGoogle Scholar
  9. [9]
    Zhang Y, Cao X, Wanjara P, et al. Oxide films in laser additive manufactured Inconel 718. Acta Materialia, 2013, 61(17): 6562–6576CrossRefGoogle Scholar
  10. [10]
    Hartman M, Pata J, Coughlin R W. Influence of porosity of calcium carbonates on their reactivity with sulfur dioxide. Industrial & Engineering Chemistry Process Design and Development, 1978, 17(4): 411–419CrossRefGoogle Scholar
  11. [11]
    Sofie S W, Dogan F. Freeze casting of aqueous alumina slurries with glycerol. Journal of the American Ceramic Society, 2001, 84 (7): 1459–1464CrossRefGoogle Scholar

Copyright information

© Higher Education Press and Springer-Verlag Berlin Heidelberg 2016

Authors and Affiliations

  1. 1.Department of Orthopedic Trauma, Affiliated General HospitalNingxia Medical UniversityYinchuanChina
  2. 2.State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and EngineeringTsinghua UniversityBeijingChina

Personalised recommendations