Investigating the Effects of Locks on the Fracture Force and Stress Intensity Using Experimental Photoelasticity

  • A. Kamali
  • M. Rezaeizadeh
  • E. Jomehzadeh
Technical Article---Peer-Reviewed

Abstract

Most of the engineering materials are faced with fracture phenomenon that needs to be controlled. There are several methods for controlling crack growth such as hole technique, using locks etc. In order to predict crack growth, stress intensity factor can be conducted as a useful tool. In this paper, the photoelasticity method is conducted as an experimental stress analysis tool in order to calculate the stress intensity factor (SIF). The investigations were conducted to find the effects of holes and locks on the fracture resistance and the SIF. This research is specially focused on the crack stitch as a unique technique to control crack propagation. In this technique, holes of locks are drilled close to each other in rows perpendicular to the crack then keys are inserted into the holes. Three batches including six different edge crack samples of polymethyl methacrylate rectangular plates were used for fracture tests. In the present study, the effects of locks in various geometries were investigated on the SIF. The results were obtained using a polariscope and the tensile load was applied to the specimens on the mode fracture (I) strength; then, the fracture forces were measured. The results showed that the samples with lock and hole have more fracture strength and thus their SIF decreases in comparison with the lock-less or hole-less samples.

Keywords

Fracture mechanics Photoelasticity Stress intensity factor Metalock Metal stitching 

References

  1. 1.
    F.J. Gómez, M. Elices, F. Berto, P. Lazzarin, Fracture of V-notched specimens under mixed mode (I + II) loading in brittle materials. Int. J. Fract. 159, 121–135 (2009)CrossRefGoogle Scholar
  2. 2.
    T.N. Chakherlou, H.N. Maleki, A.B. Aghdam, B. Abazadeh, Effect of bolt clamping force on the fracture strength of mixed mode fracture in an edge crack with different sizes experimental and numerical investigations. Mater. Des. 45, 430–439 (2013)CrossRefGoogle Scholar
  3. 3.
    H.N. Atahan, M.A. Tasdemir, C. Tasdemir, N. Ozyurt, S. Akyuz, Mode I and mixed mode fracture studies in brittle materials using the Brazilian disc specimen. Mater. Struct. 38, 305–312 (2005)CrossRefGoogle Scholar
  4. 4.
    N. Irani, J.J.C. Remmers, V.S. Deshpande, A discrete dislocation analysis of hydrogen-assisted mode-i fracture. Mech. Mater. 105, 67–79 (2017)CrossRefGoogle Scholar
  5. 5.
    A. Carpinteri, Stress-singularity and generalized fracture toughness at the vertex of re-entrant corners. Eng. Fract. Mech. 26, 143–155 (1987)CrossRefGoogle Scholar
  6. 6.
    P. Lazzarin, R. Zambardi, P. Livieri, A J-integral-based approach to predict the fatigue strength ofcomponents weakened by sharp V-shaped notches. Int. J. Comput. Appl. Technol. 15(4–5), 202–210 (2002)CrossRefGoogle Scholar
  7. 7.
    Z. Domazet, comparison of fatigue crack retardation methods. Eng. Fail. Anal. 3(2), 137–147 (1996)CrossRefGoogle Scholar
  8. 8.
    Xing-Quan Zhang, Xin Zhang, Long Li, Shi-Wei Duan, Sheng-Zhi Li, Zhi-Lai Huang, Yi-Wei Zhang, Jian-You Feng, Investigation of the influence of small hole on the fatigue crack growth path. J Fail. Anal. And Preven. 16, 391–399 (2016)CrossRefGoogle Scholar
  9. 9.
    W. Elber, Fatigue crack closure under cyclic tension. Eng. Fract. Mech. 2, 37–45 (1970)CrossRefGoogle Scholar
  10. 10.
    M.R. Ayatollahi, S.M.J. Razavi, M.Y. Yahya, Mixed mode fatigue crack initiation and growth in a CT specimen repaired by stop hole technique. Eng. Fract. Mech. 145, 115–127 (2015)CrossRefGoogle Scholar
  11. 11.
    P.K. Sharp, J.Q. Clayton, G. Clar, Retardation and repair of fatigue cracks by adhesive infiltration. Fatigue Fract. Eng. Mater. Struct. 20(4), 605–614 (1997)CrossRefGoogle Scholar
  12. 12.
    C.S. Shin, C.Q. Cai, A model for evaluating the effect of fatigue crack repair by the infiltration method. Fatigue Fract. Eng. Mater. Struct. 23(10), 835–845 (2000)CrossRefGoogle Scholar
  13. 13.
    C. Liu, D.O. Northwood, S.D. Bhole, Tensile fracture behavior in co2 laser beam welds of 7075-t6 aluminum alloy. Mater. Des. 25, 573–577 (2004)CrossRefGoogle Scholar
  14. 14.
    T.W. Eagar, P.F. Mendez, Penetration and defect formation in high current arc welding. Final ReportGoogle Scholar
  15. 15.
    M.R.M. Aliha, M.R. Ayatollahi, Geometry effects on fracture behavior of polymethyl methacrylate. Mater. Sci. Eng. A 527, 526–530 (2010)CrossRefGoogle Scholar
  16. 16.
    Metalock-Engineering, Metal stitching. Metalock Engineering UK [Online]. Available: https://www.metalock.co.uk/typical-on-site-repairs/metal-stitching.aspx. Accessed 11 Apr 2016
  17. 17.
    Z. Line, Y. Haruvy, N. Lao, M. Ryeom, E.P. Muelljzr, Radiation induced sterilization of polymeric materials for medical implants. I. radiation-induced damage in irradiated polymethylmethacrylate. R&at. Phys. Chem. 38(6), 565–572 (1991)Google Scholar
  18. 18.
    L.S. Kahan, Medical devices; reclassification of polymethylmethacrylate (pmma) bone cement. Final rule. Fed. Regist. 67(137), 46852 (2002)Google Scholar
  19. 19.
    L.I.U. Bao-jun, L.I. De-jun, Han-qing. f + ion implantation for enhancing surface hydrophobicity of medical polymethylmethacrylate. Chin. Phys. Lett. 15(9), 662 (1998)CrossRefGoogle Scholar
  20. 20.
    M.R. Ayatollahi, S.M.J. Razavi, H.R. Chamani, Fatigue life extension by crack repair using stop-hole technique under pure mode-I and pure mode-II loading conditions. Proc. Eng. 74, 18–21 (2014)CrossRefGoogle Scholar
  21. 21.
    W. Hao, J. Zhu, Q. Zhu, Y. Yuan, Study of matrix crack-tilted fiber bundle interaction using caustics and finite element method. Rev. Sci. Instrum. 87(2), 023109 (2016)CrossRefGoogle Scholar
  22. 22.
    W. Hao, C. Tang, Y. Yuan, Y. Ma, Photoelastic investigation of interaction between matrix crack and different shapes of inclusions. J. Test. Eval. 44(6), 2352–2360 (2015)Google Scholar
  23. 23.
    H. Tada, P.C. Paris, G.R. Irwin, The Stress Analysis of Cracks Handbook (Del Research Corporation, 1973)Google Scholar
  24. 24.
    W. Hao, J. Zhu, Q. Zhu, Y. Yuan, Photoelastic analysis of matrix crack-tilted fiber bundle interaction. Polym. Test. 51, 101–108 (2016)CrossRefGoogle Scholar
  25. 25.
    T.N. Chakherlou, H.N. Maleki, A.B. Aghdam, B. Abazadeh, Effect of bolt clamping force on the fracture strength of mixed mode fracture in an edge crack with different sizes: experimental and numerical investigations. Mater. Des. 45, 430–439 (2013)CrossRefGoogle Scholar

Copyright information

© ASM International 2018

Authors and Affiliations

  1. 1.Department of Mechanical EngineeringGraduate University of Advanced TechnologyKermanIran

Personalised recommendations