Failure and Fracture Analysis of a Zn-Alloy Casting

  • George A. Pantazopoulos
Case History---Peer-Reviewed

Abstract

A Zn-alloy casting failed during use, displaying a macroscopically brittle fracture. Failure analysis investigation determined the origin of fracture, located on the top corner of the component, while an extensive amount of gas porosity was identified. The subsurface porosity seems that triggered the crack initiation and the internal porosity reduced severely the fracture toughness, leading to fast and unstable crack propagation. Careful review and revision of the component casting conditions are recommended in order to prevent gas evolution and entrapment and to increase the component lifetime.

Keywords

Fractography Zn-alloy casting Gas porosity 

Notes

Acknowledgments

The author wishes to thank Dr. Ioannis Pantazopoulos for the provision of the fractured component and the colleagues Dr. Athanasios Vazdirvanidis and Mr. Andreas Rikos for their helpful assistance and continuous support.

References

  1. 1.
    D. Hull, Fractography Observing: Measuring and Interpreting Fracture Surface Topography (Cambridge University Press, Cambridge, 1999)Google Scholar
  2. 2.
    G. Pantazopoulos, Damage assessment using fractography as failure evaluation: applications in industrial metalworking machinery. J. Fail. Anal. Prev. 11(6), 588–594 (2011)CrossRefGoogle Scholar
  3. 3.
    R.A. Higgins, Engineering Metallurgy—Part I: Applied Physical Metallurgy (Arnold, London, 1993)Google Scholar
  4. 4.
  5. 5.
    J.E. Shigley, C.R. Mischke, Mechanical Engineering Design (McGraw Hill, New York, 1988)Google Scholar
  6. 6.
    G. Pantazopoulos, A. Vazdirvanidis, A. Rikos, A. Toulfatzis, Analysis of abnormal fatigue failure of forklift forks. Case Stud. Eng. Fail. Anal. 2(1), 9–14 (2014)CrossRefGoogle Scholar
  7. 7.
    A. Venugopal Reddy, Investigation of aeronautical and engineering component failures (CRC Press, Boca Raton, 2004)CrossRefGoogle Scholar
  8. 8.
    J. Cambell, Castings (Butterworth-Heinemann, Oxford, 1998)Google Scholar
  9. 9.
    L. Darken, R. Gurry, Physical Chemistry of Metals (McGraw Hill, New York, 1953)Google Scholar
  10. 10.
    F.D. Richardson, J.H.E. Jeffes, The thermodynamics of substances of interest in iron and steel making from 0 to 2400 °C. J. Iron Steel Inst. 160, 261–270 (1948)Google Scholar
  11. 11.
    G. Pantazopoulos, A. Vazdirvanidis, D.C. Papamantellos, Metallurgical Investigation on Low Ductility Failures of Cu-ETP Components, Materials Science Forum, vol. 638–642 (2010), pp. 3901–3906. (Invited paper at THERMEC 2009, International Conference on Processing and Manufacturing of Advanced Materials, August 25–29, 2009, Berlin Germany)Google Scholar

Copyright information

© ASM International 2017

Authors and Affiliations

  1. 1.ELKEME Hellenic Research Centre for Metals S.A.Oinofyta, ViotiasGreece

Personalised recommendations