, Volume 16, Issue 3, pp 449–456 | Cite as

Finite Element Analysis of Hydrogen Transport in Steel Pressure Vessel at Room Temperature

  • T. C. Cui
  • P. F. Liu
  • J. Y. Zheng
  • C. H. Gu
Technical Article---Peer-Reviewed

Abstract

Hydrogen embrittlement is commonly considered as an important failure mechanism for steel pressure vessels and pipes made of such as Cr–Mo and 4130X steels under high-pressure hydrogen environments, which means hydrogen atom can easily penetrate and diffuse into the metal, leading to the distortion of microscopic lattice and the degradation of macroscopic strength and fracture toughness. Under the support of the National Key Fundamental Research and Development Project of China (2015.1-2019.12), we aim to launch a series of theoretical, experimental, and numerical research on the macroscopic damage evolution and microscopic fracture of steel structures under high-pressure hydrogen environment, which ultimately commits to gaining deep insight into the hydrogen embrittlement mechanisms. This work studies the hydrogen transport mechanisms in Cr–Mo steel pressure vessels under different hydrogen environments using finite element analysis (FEA), which is fundamental to subsequent research on the hydrogen-induced damage evolution and crack behaviors. The purpose of this paper is to explore the effects of the initial hydrogen concentrations and structural sizes on the hydrogen transport mechanisms in 2.25Cr-1Mo pressure vessels with a nozzle at room temperature. Numerical results by comparing different hydrogen concentration distributions show that structural discontinuities tend to accelerate the hydrogen embrittlement sensitivity.

Keywords

Hydrogen transport Cr–Mo steel pressure vessel Finite element analysis (FEA) 

Notes

Acknowledgments

All authors would sincerely appreciate the support of the National Program on Key Basic Research Project of China (973 Program, No. 2015CB057601) and Fundamental Research Funds for the Central Universities.

References

  1. 1.
    C.S. Oh, Y.J. Kim, K.B. Yoon, Coupled analysis of hydrogen transport using ABAQUS. J. Solid Mech. Mater. Eng. 4, 908–917 (2010)CrossRefGoogle Scholar
  2. 2.
    H. Kanayama, M. Ogino, R. Miresmaeili, T. Nakagawa, T. Toda, Hydrogen transport in a coupled elastoplastic-diffusion analysis near a blunting crack tip. J. Comput. Sci. Technol. 2, 499–510 (2008)CrossRefGoogle Scholar
  3. 3.
    K. Takayama, R. Matsumoto, S. Taketomi, N. Miyazaki, Hydrogen diffusion analyses of a cracked steel nozzle under internal pressure. Int. J. Hydrogen Energy 36, 1037–1045 (2011)CrossRefGoogle Scholar
  4. 4.
    A. Taha, P. Sofronis, A micromechanics approach to the study of hydrogen transport and embrittlement. Eng. Fract. Mech. 68, 803–837 (2001)CrossRefGoogle Scholar
  5. 5.
    J. Crank, The Mathematics of Diffusion (Clarendon Press, Oxford, 1956)Google Scholar
  6. 6.
    S.R. DeGroot, P. Mazur, Non Equilibrium Thermodynamics (North Holland Publishing Company, North Holland, 1962)Google Scholar
  7. 7.
    C. S. Oh, Y.J. Kim, K. B. Yoon, On coupled analysis of hydrogen transport using ABAQUS, Asian Pacific Conference for Materials and Mechanics (2009)Google Scholar
  8. 8.
    N. Yazdipour, A.J. Haq, K. Muzaka, E.V. Pereloma, 2D modelling of the effect of grain size on hydrogen diffusion in X70 steel. Comput. Mater. Sci. 56, 49–57 (2012)CrossRefGoogle Scholar
  9. 9.
    O. Vigdis, S. Afaf, L. Jemblie, R. Johnsen, FE simulation of hydrogen diffusion in duplex stainless steel. Int. J. Hydrog. Energy 39, 1156–1163 (2014)CrossRefGoogle Scholar
  10. 10.
    N.I. Dmitrii, S. Nicolas, J.M. Olive, A. Remill, I. Aubert, Simulation of hydrogen diffusion affected by stress-strain heterogeneity in polycrystalline stainless steel. Int. J. Hydrog. Energy 39, 2418–2422 (2014)CrossRefGoogle Scholar
  11. 11.
    T. Fujii, T. Nazama, H. Makajima, R. Horita, A safety analysis on overlay disbonding of pressure vessels for hydrogen service, J. Am. Soc. Met. 361–368 (1982)Google Scholar
  12. 12.
    S. Govindjee, J.C. Simo, Coupled stress diffusion: case: II. J. Mech. Phys. Solids 41, 863–887 (1993)CrossRefGoogle Scholar
  13. 13.
    D.C. Ahna, P. Sofronisa Jr, R.H. Dodds, On hydrogen-induced plastic flow localization during void growth and coalescence. Int. J. Hydrog. Energy 32, 3734–3742 (2007)CrossRefGoogle Scholar
  14. 14.
    L. Anand, A thermo-mechanically-coupled theory accounting for hydrogen diffusion and large elastic-viscoplastic deformations of metals. Int. J. Solids Struct. 48, 962–971 (2011)CrossRefGoogle Scholar
  15. 15.
    V.D.L. Claudio, L. Annad, Hydrogen in metals: a coupled theory for species diffusion and large elastic-plastic deformation. Int. J. Plast 43, 42–69 (2013)CrossRefGoogle Scholar
  16. 16.
    Abaqus Version 6.14 Documentation-Abaqus Theory GuideGoogle Scholar
  17. 17.
    A.H.M. Krom, R.W.J. Koers, A. Bakker, Hydrogen transport near a blunting crack tip. J. Mech. Phys. Solids 47, 971–992 (1999)CrossRefGoogle Scholar
  18. 18.
    P. Sofronis, R.M. McMeeking, Numerical analysis of hydrogen transport near a blunting crack tip. J. Mech. Phys. Solids 37, 317–350 (1989)CrossRefGoogle Scholar

Copyright information

© ASM International 2016

Authors and Affiliations

  1. 1.Institute of Chemical Machinery and Process EquipmentZhejiang UniversityHangzhouChina

Personalised recommendations