Failure Investigation of a Final Super Heater Tube in a 140 MW Thermal Power Plant

  • Atanu Saha
  • H. Roy
  • A. K. Shukla
Case History---Peer-Reviewed

Abstract

This article describes the findings of a detailed investigation into the failure of a final super heater tube in a 140 MW thermal power plant. Preliminary macroscopic examinations along with visual examination, dimensional measurement, chemical analysis, evaluation of mechanical properties, and oxide scale thickness measurement were carried out to deduce the probable cause of failure. In addition, optical microscopy was a necessary supplement to understand the cause of failure. It was concluded that the tube had failed due to stress rupture. The tube metal had been exposed to a temperature above the safe operating limit for a long duration. As a result the tube metal had lost its strength, suffered creep deformation and failed to support the working stress resulting in final rupture. The adherent scale, particularly on internal surface formed due to exposure at high temperature. It had acted as an insulating blanket in view of its much lower thermal conductivity than that of the tube metal. The progressive build-up of scale had greatly affected heat transfer and raised the tube metal temperature above A1 for a short duration before bursting of the tube. The overheating in this case may be due to poor circulation over the localized area.

Keywords

Super heater Stress rupture Deformation Failure 

References

  1. 1.
    W.T. Reid, External Corrosion and Deposits—Boilers and Gas Turbines (Elsvier, New York, 1971)Google Scholar
  2. 2.
    J. Stringer, High temperature problems in electric power industry and their solutions, in High Temperature Corrosion, ed. by R.A. Rapp (National Association of Corrosion Engineers, Houston, 1983), p. 389Google Scholar
  3. 3.
    D.N. French, Liquid ash corrosion problems in fossil fuel boilers. Proc. Electrochem. Soc. 83–85, 68 (1983)Google Scholar
  4. 4.
    B.C. Syratt, Corrosion in fossil fuel power plants, in Metal Handbook, vol. 13, ed. by B.C. Syratt (American Society for Metals, Metals Park, 1987), p. 985Google Scholar
  5. 5.
    R.D. Porta, H.M. Herro, The Nalco Guide to Boiler Failure Analysis (McGraw-Hill, New York, 1991)Google Scholar
  6. 6.
    R.B. Dooley, Boiler tube failures—a perspective and vision, in Proceedings International Conference on Boiler Tube Failures in Fossil Plants (EPRI, Palo Alto, 1992)Google Scholar
  7. 7.
    J. Calannino, Prevent boiler tube failure Part I: Fire-side mechanisms, Chem. Eng. Prog., 33 (1993)Google Scholar
  8. 8.
    J. Calannino, Prevent boiler tube failure Part II: Waterside mechanisms, Chem. Eng. Prog., 73 (1993) Google Scholar
  9. 9.
    G.A. Lamping, R.M. Arrowwood Jr., Manual for Investigation and Correction of Boiler Tube Failures. Report CS-3945 (Electric Power Research Institute, Palo Alto, 1985)Google Scholar
  10. 10.
    F. Garofalo, Fundamentals of Creep and Creep Rupture in Metals (Macmillan, New York, 1965)Google Scholar
  11. 11.
    J. Bressers (ed.), Creep and Fatigue in High Temperature Alloys (Applied Science Publishers, London, 1981)Google Scholar
  12. 12.
    G. Bernasconi, G. Piatti (eds.), Creep of Engineering Materials and Structures (Applied Science Publishers, London, 1979)Google Scholar
  13. 13.
    R. Viswanathan, J.R. Foulds, D.I. Roberts, in Proceedings on Boiler Tube Failures in Fossil Power Plants, vol. 10 (EPRI, Palo Alto, 1987), pp. 3.35–3.53Google Scholar
  14. 14.
    R. Viswanathan, J.R. Foulds, Service experience, structural integrity, severe accidents and erosion in nuclear and fossil plants, in ASME Pressure Vessels and Piping Conference, vol. 303, pp. 187–205, 1995Google Scholar
  15. 15.
    R. Viswanathan, Damage Mechanisms and Life Assessment of High Temperature Components (ASM International, Metals Park, 1989)Google Scholar
  16. 16.
    M.C. Coleman, J.D. Parker, D.T. Welters, Behaviour of ferritic weldments in thick section Cr–Mo–V pipe at elevated temperatures. Int. J. Press. Vessel. Pip. 18, 277–310 (1985)CrossRefGoogle Scholar
  17. 17.
    F.R. Larson, J. Miller, A time-temperature relationship for rupture and creep stresses. Trans. ASME 74, 765–775 (1952)Google Scholar

Copyright information

© ASM International 2015

Authors and Affiliations

  1. 1.NDT and Metallurgy GroupCSIR - Central Mechanical Engineering Research InstituteDurgapurIndia

Personalised recommendations