Corrosion Fatigue Failure Analysis of a Supporting Pipe Weld in Deaerization Plant

  • Qiaoling Chu
  • Min Zhang
Technical Article---Peer-Reviewed
  • 177 Downloads

Abstract

The aim of this work is to reveal the failure mechanism of a supporting pipe weld after 20 years of service in a deaerization plant. The characterization methods included inductively coupled plasma, optical microscopy, scanning electron microscope, X-ray energy dispersive spectrometer, mechanical tests, and finite element analysis (FEA). The results showed that the supporting pipe weld failed by corrosion fatigue cracking. Cracks initiated from the surface pits which were due to corrosion. FEA analysis revealed that stress concentration occurred in the failed weld. This paper brings out the details of the investigation and suggests remedial measures to improve performance of such pipe welds in deaerization plants.

Keywords

Corrosion fatigue Failure analysis Weld 

Notes

Acknowledgments

The authors gratefully acknowledge the financial support from the National High Technology Research and Development Program of China (Grant No. 2013AA031303), the Chinese National Engineering Research Center for Petroleum, and Natural Gas Tubular Goods and the Doctoral Innovation Fund of Xi’an University of Technology (Grant No. 207-002j1405).

References

  1. 1.
    J.H. Bulloch, Deaerator feedwater vessel weld cracking monitored over a service time of around 80000 hours. Int. J. Press. Vessels Pip. 80, 607–615 (2003)CrossRefGoogle Scholar
  2. 2.
    R. Ebara, Corrosion fatigue phenomena learned from failure analysis. Eng. Fail. Anal. 13, 516–525 (2006)CrossRefGoogle Scholar
  3. 3.
    C.R. Gagg, Failure of components and products by ‘engineered-in’ defects: case studies. Eng. Fail. Anal. 12, 1000–1026 (2005)CrossRefGoogle Scholar
  4. 4.
    H. Kazempour-Liacy, M. Mehdizadeh, M. Akbari-Garakani, S. Abouali, Corrosion and fatigue failure analysis of a forced draft fan blade. Eng. Fail. Anal. 18, 1193–1202 (2011)CrossRefGoogle Scholar
  5. 5.
    W. Lv, C. Pan, W. Su, Z. Wang, S. Liu, C. Wang, A study on atmospheric corrosion of 304 stainless steel in a simulated marine atmosphere. J. Mater. Eng. Perform. 24, 2597–2604 (2015)CrossRefGoogle Scholar
  6. 6.
    Li Shuxin, R. Akid, Corrosion fatigue life prediction of a steel shaft material in seawater. Eng. Fail. Anal. 34, 324–334 (2013)CrossRefGoogle Scholar
  7. 7.
    S. Kaewkumsai, W. Khonraeng, A. Chainpairote, Corrosion fatigue cracking of AISI 316L stainless steel screen mesh. Eng. Fail. Anal. 17, 857–863 (2010)CrossRefGoogle Scholar
  8. 8.
    R. Rivera, A. Chiminelli, C. Gomez, J.L. Nunez, Fatigue failure analysis of a spring for elevator doors. Eng. Fail. Anal. 17, 731–738 (2010)CrossRefGoogle Scholar
  9. 9.
    M. Reihanian, K. Sherafatnia, M. Sajjadnejad, Fatigue failure analysis of holding U-bolts of a cooling fan blade. Eng. Fail. Anal. 18, 2019–2027 (2011)CrossRefGoogle Scholar

Copyright information

© ASM International 2015

Authors and Affiliations

  1. 1.College of Materials Science and EngineeringXi’an University of TechnologyXi’anChina

Personalised recommendations