Failure Analysis of Spline Shaft in Beco Lathe
- 320 Downloads
The failure of Heavy Duty Facing Lathe has been systematically investigated using fractographic, metallographic, and analytical stress analysis methods. Failure occurred during machining of a large flange, the tool post had a collision with jaw of the rotating chuck and the spline shaft inside headstock was broken into two pieces. A detailed analysis of the fracture surfaces revealed partial damage of the surfaces due to their rubbing in operation and cleavage fracture in the remaining part of the surfaces. The stress analysis indicates that sudden reversing of the spindle had resulted in the stresses exceeding the fatigue limit of the shaft material. These stresses led to the formation of microcracks at the circlip groove. The collision accelerated the sudden failure of shaft. This failure analysis has led to identification of root cause and its elimination with corrective measures undertaken.
KeywordsMicrocrack Microhardness Effective torque Fatigue Micrograph Angular deceleration
I am immensely thankful to Director, IGCAR and Director, ESG for their guidance and support. I also thank the members of CWD, MJS, QAD, CG of IGCAR for the technical support in conducting the failure analysis.
- 1.BECO Lathe Machine Manual (1991)Google Scholar
- 2.Failure Analysis and Prevention, vol 11. ASM Metals Handbook, 10th edn. (ASM International, Materials Park, 1993)Google Scholar
- 3.R.L. Brockenbrough, F.S. Meritt, Structural Steel Designer’s Hand Book, 4th edn. (McGraw Hill, New York, 2005)Google Scholar
- 4.Fatigue and Fracture, vol 19. ASM Metals Handbook, 10th edn. (ASM International, Materials Park, 1993)Google Scholar
- 9.J. Carvill, Mechanical Engineers Data Book (Butterworth-Heinemann, Boston, 2001)Google Scholar