Abstract
Complete circumferential (360°) tearing has been observed at the bottom of body walls in a number of three-piece, steel, cylindrical aerosol containers. This type of failure has not been well documented and analyzed in previous aerosol can failure analysis literature. In one instance, a worker accidentally dropped an aerosol spray paint can, and it instantly burst via catastrophic 360° circumferential failure near the bottom of the body wall. This was a relatively low-pressure, low-temperature, nearly instantaneous fracture. The burst aerosol became a high-velocity rocket and impacted the worker in the face and caused the loss of one eye. Other similar incidents involving this same failure mechanism have occurred with varying degrees of injury. The objective of this study was to determine why the aerosols catastrophically burst in the 360° circumferential manner and, more importantly, to find a remedy and prevent future failures. Test methods were developed to quantitatively control the force and angle of impact that might result from the tapping, hitting, or accidental dropping of an aerosol container. More common failure analysis methods were also used, such as metallography, scanning electron microscopy, energy dispersive spectroscopy, simple bending tests to simulate low-cycle fatigue, and a method to measure internal aerosol pressure as a function of temperature. The most likely root cause for the 360° burst failures was determined to be a combination of pre-existing circumferential flaw or flaws, the anisotropic microstructure of the aerosol body steel and above yield stress that is facilitated by the geometry of the body-to-bottom design when the aerosol is tapped, hit, or accidentally dropped. Experiments show that changing microstructure and/or design significantly reduce the likelihood of this failure mechanism and offer simple, cost-effective remedies.
Similar content being viewed by others
References
Fox, M., Hastings, R.: Pressurized 3-piece steel container explosions and failure mechanisms. Pract. Fail. Anal. 3(3), 78–82 (2003)
Daehn, R.C., Blum, J.J.: Failure analysis of three-piece steel aerosol cans. J. Fail. Anal. Prevent. 4(4), 58–67 (2004)
Fox, M.: Failure analysis of aerosol containers. J. Fail. Anal. Prevent. 5(3), 57–65 (2005)
Fox, M., Hastings, R.: The interaction of test methods and failure criteria. J. Fail. Anal. Prevent. 6(2), 50–56 (2006)
Fox, M., Hastings, R., Lovald, S., Heinrich, J.: Case study of an aerosol explosion and a method to determine explosion temperature. J. Fail. Anal. Prevent. 7(3), 165–174 (2007)
Fox, M.: Measuring and improving the puncture resistance of self-pressurized containers. J. Fail. Anal. Prevent. 8(4), 353–361 (2008)
Kuhn, H.A.: Failure of an Aerosol Can, Materials Science and Technology 2009, Pittsburgh, PA (2009)
Code of Federal Regulations 49CFR173.306 and 49CFR178.33
Johnsen, M.A.: The Aerosol Handbook, p. 49. Wayne Dorland Company, Mendham, NJ (1982)
Higdon, A., Ohlsen, E., Stiles, W.: Mechanics, pp. 77–80. John Wiley & Sons, New York, NY (1960)
Ryder, D.A., Davies, T.J., Brough, I.: General practice in failure analysis. In: ASM Handbook of Failure Analysis and Prevention, vol. 11, pp. 15, 31 (1986)
Fox, M.: Environment related pipe cracking remedies. Mater. Perform. 22(2), 17–21 (1983)
Fox, M.: A Review of Boiling Water Reactor Water Chemistry. Special report prepared for the U.S. Nuclear Regulatory Commission, NUREG/CR-5115, ANL-88-42, February 1989
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Fox, M. Circumferential Catastrophic Burst Failures of Pressurized Cylinders. J Fail. Anal. and Preven. 11, 320–331 (2011). https://doi.org/10.1007/s11668-011-9431-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11668-011-9431-6