Abstract
The grease-lubricated roller bearing of an electric motor that drove a supply blower suddenly failed during operation. In order to identify the causes of the failure, a variety of characterizations were carried out. The failed surfaces of the bearing were observed visually and microscopically, and the characteristics of the lubricating grease were also investigated. Results showed that the surface of the inner ring of the bearing contained contact fatigue damage, and was covered with a multitude of debris and contact fatigue pits. What’s more, the lubricating grease was subjected to severe thermally induced degradation due to high service temperature, which consequently resulted in the decrease of the lubricating capacity of the grease. Thus, the lubricant film in the roller/raceway contacts was not formed effectively and the lubrication of the roller bearing was poor. As a result, serious local wear as well as contact fatigue damage were brought about on the roller and raceway and the wear finally led to the failure of the bearing.
Similar content being viewed by others
References
Zhou, Z.X.: 滚动轴承常见失效形式分析与正确维护 (Common failure type analysis of rolling bearing and its correct maintenance). Constr. Mach. 9, 67–71 (2003) (in Chinese)
Li, Y.J., Tao, C.H., Zhang, W.F., et al.: Fracture analysis on cage rivets of a cylindrical roller bearing. Eng. Fail. Anal. 15(6), 796–801 (2008) (in English)
Fernandes, P.J.L.: Contact fatigue in rolling-element bearings. Eng. Fail. Anal. (4), 155–160 (1997) (in English)
Yang, W.Q., Chen, Y.Z.: 减少电动机滚动轴承故障的途径 (Methods for reducing the faults in rolling contact bearing of motor). Explos. Proof Electr. Mach. 40(2), 28–30 (2005) (in Chinese)
Carré, D.J., Bauer, R., Fleischauer, P.D.: Chemical analysis of hydrocarbon grease from spin-bearing tests. ASLE Trans. 26, 475–480 (1983) (in English)
Tomaru, M., Suzuki, T., Ito, H., Suzuki, T.: Grease-life estimation and grease deterioration in sealed ball bearings. In: Proc. JSLE Int. Trib. Conf., 1985, pp. 1039–1044 (in English)
Hosoya, S., Hayano, M.: Deterioration of lithium soap greases and functional life in ball bearings. NLGI Spokesm. 53, 246–251 (1989) (in English)
Cann, P.M., Doner, J.P., Webster, M.N., Wickstrom, V.: Grease degradation in rolling element bearings. STLE Trans. 44, 399–404 (2001) (in English)
Cann, P.M.: Grease degradation in a bearing simulation device. Trib. Int. 39, 1698–1706 (2006) (in English)
Komatsuzaki, S., Uematsu, T., Kobayashi, Y.: Change of grease characteristics to the end of lubricating life. NLGI Spokesm. 63, 22–27 (2000) (in English)
Fernandes, P.J.L., Mcduling, C.: Surface contact fatigue failures in gears. Eng. Fail. Anal. 4(2), 99–107 (1997) (in English)
ASM Metals Handbook, Failure of Rolling-Element Bearings, Vol. 11, Failure Analysis and Prevention, 9th edn. American Society for Metals, Metals Park, OH, pp. 490–513 (1986) (in English)
Xie, F., Yu, Y.P., Yao, J.B.: 脂的氧化与抑制 (Oxidation of grease and its inhibition). Synth. Lubr. 30(3), 49–52 (2003) (in Chinese)
Xue, J., Zhang, J.Y., Wang, C.T.: 红外波谱技术在轴承润滑脂分析上的应用 (Application of infrared spectrum technique in bearing grease analysis). Bearing 7, 25–29 (2003) (in Chinese)
Eichler, J.W., Matthews, A., Leyland, A., et al.: The influence of coatings on the oil-out performance of rolling bearings. Surf. Coat. Technol. 202, 1073–1077 (2007) (in English)
Berthier, Y., Vincent, L., Godet, M.: Fretting fatigue and fretting wear. Trib. Int. 22, 235–242 (1989) (in English)
Acknowledgments
This investigation was supported by Shanghai Leading Academic Discipline Project, Project Number B113. The support is gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yu, ZQ., Yang, ZG. Fatigue Failure Analysis of a Grease-Lubricated Roller Bearing from an Electric Motor. J Fail. Anal. and Preven. 11, 158–166 (2011). https://doi.org/10.1007/s11668-010-9422-z
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11668-010-9422-z