, Volume 10, Issue 6, pp 504–507 | Cite as

Failure Investigation of Direct Write Pen Tips

  • David A. Roberson
  • Eric MacDonald
  • Ken Church
  • Ryan B. Wicker
Technical Article---Peer-Reviewed
  • 102 Downloads

Abstract

Scanning electron microscopy of direct write pen tips provided fractographic evidence that pen tip failure was due to impact fracture. It is recommended that safeguards be implemented into the direct write system that will prevent impact between the pen tips and the print media.

Keywords

SEM Impact Ceramics Micro failure analysis Alumina Scanning electron microscope 

Notes

Acknowledgments

The research presented here was performed through the W.M. Keck Center for 3D Innovation at The University of Texas at El Paso (UTEP). This research was supported through the NSF under grant number HRD-0929727 and the Mr. and Mrs. MacIntosh Murchison Chair I in Engineering.

References

  1. 1.
    Powell, G.W.: ASM Handbook Volume 11: Failure Analysis and Prevention, pp. 745–757. ASM International, Ohio (1995)Google Scholar
  2. 2.
    Krell, A.: Fracture origin and strength in advanced pressureless-sintered alumina. J. Am. Ceram. Soc. 81(7), 1900–1906 (1998)CrossRefGoogle Scholar
  3. 3.
    Cottrel, B., Kamminga, J., Dickson, F.P.: The essential mechanics of conchoidal flaking. Int. J. Fract. 29, 205–221 (1985)CrossRefGoogle Scholar
  4. 4.
    Hull, D.: Fractography: Observing, Measuring, and Interpreting Fracture Surface Topography, pp. 38–40. Cambridge University Press, Cambridge (1999)Google Scholar
  5. 5.
    Kelly, R.J., Campbell, S.D., Bowen, K.H.: Fracture-surface analysis of dental ceramics. J. Prosthet. Dent. 62(5), 536–541 (1989)CrossRefPubMedGoogle Scholar

Copyright information

© ASM International 2010

Authors and Affiliations

  • David A. Roberson
    • 1
  • Eric MacDonald
    • 2
  • Ken Church
    • 2
  • Ryan B. Wicker
    • 3
  1. 1.Metallurgical and Materials EngineeringThe University of Texas at El PasoEl PasoUSA
  2. 2.Electrical and Computer EngineeringThe University of Texas at El PasoEl PasoUSA
  3. 3.Mechanical EngineeringThe University of Texas at El PasoEl PasoUSA

Personalised recommendations