Investigation of Probable Cause of Premature Cracking of Downcomer Nozzle of Heat Recovery Steam Generator
The premature failure (cracked) of a downcomer nozzle attached with intermediate pressure drum of heat recovery steam generator was investigated. The conventional wet fluorescent magnetic particle and dye-penetrant testing along with macro analysis, sulfur print, and microstructural examination were used in the investigation. In addition, energy dispersive spectroscopy was also carried out to understand the reason of premature failure. Finally, it was concluded that presence of excessive multiphase inclusions containing manganese in localized areas caused formation of cracks at those locations during forging.
KeywordsDowncomer nozzle HRSG Failure EDX Inclusions
- 1.British Electricity International: Modern Power Station Practice, Vol. B: Boilers and Ancillary Plants, 3rd edn. Elsevier, Amsterdam (1991)Google Scholar
- 2.Viswanathan, R., Foulds, J.R.: Service experience, structural integrity, severe accidents and erosion in nuclear and fossil plants. In: ASME Pressure Vessels and Piping Conference, vol. 303, pp. 187–205 (1995)Google Scholar
- 4.Viswanathan, R.: Damage Mechanisms and Life Assessment of High Temperature Components. ASM International, Metals Park, OH (1989)Google Scholar
- 5.Ellis, F.B.: Remaining life assessment of boiler pressure parts. Final report RP 22353-1, vols. 1–5. EPRI, Paolo Alto, CA (1988) Google Scholar