Journal of Failure Analysis and Prevention

, Volume 7, Issue 1, pp 12–17 | Cite as

Failure Analysis of a Vehicle Engine Crankshaft

  • M. A. Alfares
  • A. H. Falah
  • A. H. Elkholy
Case History


An investigation of a damaged crankshaft from a horizontal, six-cylinder, in-line diesel engine of a public bus was conducted after several failure cases were reported by the bus company. All crankshafts were made from forged and nitrided steel. Each crankshaft was sent for grinding, after a life of approximately 300,000 km of service, as requested by the engine manufacturer. After grinding and assembling in the engine, some crankshafts lasted barely 15,000 km before serious fractures took place. Few other crankshafts demonstrated higher lives. Several vital components were damaged as a result of crankshaft failures. It was then decided to send the crankshafts for laboratory investigation to determine the cause of failure. The depth of the nitrided layer near fracture locations in the crankshaft, particularly at the fillet region where cracks were initiated, was determined by scanning electron microscope (SEM) equipped with electron-dispersive X-ray analysis (EDAX). Microhardness gradient through the nitrided layer close to fracture, surface hardness, and macrohardness at the journals were all measured. Fractographic analysis indicated that fatigue was the dominant mechanism of failure of the crankshaft. The partial absence of the nitrided layer in the fillet region, due to over-grinding, caused a decrease in the fatigue strength which, in turn, led to crack initiation and propagation, and eventually premature fracture. Signs of crankshaft misalignment during installation were also suspected as a possible cause of failure. In order to prevent fillet fatigue failure, final grinding should be done carefully and the grinding amount must be controlled to avoid substantial removal of the nitrided layer. Crankshaft alignment during assembly and proper bearing selection should be done carefully.


Engine crankshaft Nitriding Failure analysis Grinding Misalignment Hardness Microstructure 



This study was supported by Kuwait University under grant no. EM 04/06. The authors would like to thank the Faculty of Science for providing their facilities to carry out this study. The authors are also grateful to Mr M. Rafiq, Mr S. Iqbal, Ms M. Dashty and Ms M. Otaiby for their assistance during all phases of study and data compilation.


  1. 1.
    Campbell, A.J.: Optical alignment of reciprocating compressors. In: 12th Annual Fall Technical Conference of the ASME Internal Combustion Engine Division, New Technology in Large Bore Engines American Society of Mechanical Engineers, Internal Combustion Engine Division (Publication) ICE, vol. 13, pp. 139–142 (1990).Google Scholar
  2. 2.
    McNabb, J., Wilde, L.: Determining accurate crankshaft deviation. Diesel Gas Turbine Worldwide 19(3), 30–32 (1987).Google Scholar
  3. 3.
    Haddara, M.R., Younis, M.A.: Effect of connecting rod obliquity on the torsional vibration of marine diesel engines with variable inertia. Trans. Canadian Soc. Mech. Eng. 10(4), 201–211 (1986).Google Scholar
  4. 4.
    Pasricha, M.S., Carnegie, W.D.: Application of the WKBJ approximation processes for the analysis of the torsional vibrations of diesel engine systems. Inst. of Phys, Stress Anal Group, Annu Conf Stress, Vib and Noise Anal in Veh, pp. 439–449 (1975).Google Scholar
  5. 5.
    Taylor, D., Zhou, W., Ciepalowicz, A.J., Devlukia, J.: Mixed-mode fatigue from stress concentrations: an approach based on equivalent stress intensity. Int. J. Fatig. 21(2), 173–178 (1999).CrossRefGoogle Scholar
  6. 6.
    Silva, F.S.: Analysis of a vehicle crankshaft failure. Eng. Failure Anal. 10(5), 605–616 (2003).CrossRefGoogle Scholar
  7. 7.
    Silva, F.S.: An investigation into the mechanism of a crankshaft failure. Key Eng. Mater. 245–346, 351–358, 2003.CrossRefGoogle Scholar
  8. 8.
    Balasiu, D.: Premature failure of crankshaft shell bearings. Prakt. Metallogr. 28(6), 314–316 (1991).Google Scholar
  9. 9.
    Motohiro, T., Katsuji, Y.: Influence on failure of high-speed diesel engines by operational condition: report of survey on failures of main engines of high-speed ferries. J. Jpn. Inst. Mar. Eng. 40(2), 235–241 (2005).Google Scholar
  10. 10.
    Pasricha M.S.: Effect of gas forces on parametrically excited torsional vibrations of reciprocating engines. J. Ship Res. 45(4), 262–268 (2001).Google Scholar
  11. 11.
    Sofronas, T.: Analyzing a crankshaft failure. Hydrocarbon Proc. 82(4), 89 (2003).Google Scholar
  12. 12.
    Kauffmann W.M.: Prevent engine – crankshaft failures. Power 124(9), 101–103 (1980).Google Scholar

Copyright information

© ASM International 2007

Authors and Affiliations

  1. 1.Mechanical Engineering DepartmentKuwait UniversitySafatKuwait

Personalised recommendations