Synthesis and Comparison of Two cBN Composites with Starting Ternary Carbide Binders
- 71 Downloads
Ti3SiC2 and Ti3AlC2 are two promising binders for the ultrahard composite polycrystalline cubic boron nitride (PcBN). In this study, the cBN composites with Ti3SiC2 and Ti3AlC2 binders with different binder contents were synthesized under the same high pressure (~5.5 GPa) and high temperature (1350 °C) conditions. Their mechanical properties were measured separately, including Vickers hardness, bending hardening, and compression hardening. Together with XRD results, the phase compounds were also investigated. The decomposition and reaction processes were affected by binder content. Some new compounds formed during sintering, these compounds were TiC, TiSi2, SiC, TiB2, SiB4, TiB2, and TiC0.7N0.3 in Ti3SiC2-cBN composites, as well as TiC0.7N0.3, TiB2, and AlN in Ti3AlC2-cBN composites. The microstructure of the cracks surface was obtained after the bending tests, and was used to further investigate and compare their crack mode by SEM. The crack surface profile and elementary analysis on the oxidative surface were also discussed.
Keywordscubic boron nitride mechanical property microstructure Ti3AlC2 Ti3SiC2
This paper is supported by the Natural Science Foundation of Shandong Province (No.ZR2014EMM011).
- 9.E. Piskorska, K. Lawniczak-Jablonska, R. Minikayev, A. Wolska, W. Paszkowicz, P. Klimczyk, and E. Benko, Quantitative Phase Analysis of Cubic Boron Nitride Based Composites by x-ray Absorption Near edge Structure, Spectrochim. Acta Part B Atomic Spectrosc., 2007, 62(5), p 461–469CrossRefGoogle Scholar
- 16.T. Prikhna, A. Starostina, D. Lizkendorf, I. Petrusha, S. Ivakhnenko, A. Borimskii, Y.D. Filatov, M. Loshak, M. Serga, and V. Tkach, Studies of the Oxidation Stability, Mechanical Characteristics of Materials Based on Max Phases of the Ti-Al-(C, N) Systems, and of the Possibility of Their Use as Tool Bonds and Materials for Polishing, J. Superhard Mater., 2014, 36(1), p 9–17CrossRefGoogle Scholar