Abstract
Li4Mn5O12 nanorods were successfully prepared by using β-MnO2 nanorod precursors as self-templates. The obtained Li4Mn5O12 nanorods were approximately 0.8–1.5 μm in length and 0.15 μm in width, and were employed as electrode materials and applied in supercapacitors. The results show that Li4Mn5O12 nanorods can deliver 211 F g−1 within the potential range of 0–1.4 V at a scan rate of 5 mV s−1 in 1 mol L−1 Li2SO4 solution, which presents a good electrochemical performance.
References
M. Cheng, K.J. Zhu, L. Yang, L. Zhu, Y. Li, and W.P. Tang, J. Alloys Compd. 686, 496 (2016).
Y.G. Li, B. Tan, and Y.Y. Wu, Nano Lett. 8, 265 (2008).
J.F. Tan and X.T. Huang, Sens. Actuators B 237, 159 (2016).
Y. Zhang, R.Y. Li, X.R. Zhou, M. Cai, and X.L. Sun, J. Phys. Chem. C 112, 10038 (2008).
W.S. Gao, C.S. Wu, M. Cao, J. Huang, L.J. Wang, and Y. Shen, J. Alloys Compd. 688, 668 (2016).
K. Thorkelsson, P. Bai, and T. Xu, Nano Today 10, 48 (2015).
X.Y. Zhou, G.H. Chen, J.J. Tang, Y.P. Ren, and J. Yang, J. Power Sources 299, 97 (2015).
G.X. Wang, X.P. Shen, and J. Yao, J. Power Sources 189, 543 (2009).
T. Takada, E. Akiba, F. Izumi, and B.C. Chakoumakos, J. Solid State Chem. 130, 74 (1997).
C.M. Julien and K. Zaghib, Electrochim. Acta 50, 411 (2004).
X. Wang and Y.D. Li, J. Am. Chem. Soc. 124, 2880 (2002).
T. Takada, H. Hayakawa, E. Akiba, F. Izumi, and B.C. Chakoumakos, J. Power Sources 68, 613 (1997).
X.Y. Wang, X.Y. Wang, W.G. Huang, P.J. Sebastian, and S. Gamboa, J. Power Sources 140, 211 (2005).
S.B. Yoon, E.H. Yoon, and K.B. Kim, J. Power Sources 196, 10791 (2011).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Zhao, Y., Wang, L., Mu, Y. et al. Preparation and Electrochemical Performance of Li4Mn5O12 Nanorods using β-MnO2 Nanorods as Precursor. J. Electron. Mater. 47, 3387–3391 (2018). https://doi.org/10.1007/s11664-018-6157-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-018-6157-1