Abstract
Recent research and a simulation of heat transfer and solidification during acoustically generated convection showed that the location of the coolest liquid, and thus the place where the first grains are expected to form, is under the sonotrode. Further, the generated vigorous convection produces a very flat temperature gradient in the bulk of the melt facilitating the formation of a refined equiaxed structure throughout the casting. This study validates these findings through a series of experiments on an Al-2 wt pct Cu alloy, which evaluate grain formation under the sonotrode over time and relate this to the formation of the macrostructure of a cast ingot. Analysis of the results confirms the predictions of the simulation and shows that, for the conditions applied, most grains nucleated in the cavitation zone are swept into the melt by acoustically generated convection and, over a period of 70 seconds, the number of grains increase and they grow with spherical and globular morphology gradually filling the casting with refined equiaxed grains. It was found that the macrostructure of each casting is made up of three microstructural zones. A fine grained equiaxed zone forms from the bottom of the casting due to settling of grains during and after termination of ultrasonic treatment (UST), which increases in size with the increasing duration of UST. Above this zone, a coarse-grained structure is formed due to depletion of UST-generated grains on termination of UST. At the top of the casting, a zone of columnar grains growing from the top surface of the melt is formed. The latter two zones decrease in size with the increasing UST duration until 80 seconds, when the macrostructure consists entirely of the equiaxed zone.
Similar content being viewed by others
References
G.I. Eskin: Ultrasonic Treatment of Light Alloy Melts, Gordon and Breach Science Publishers, Amsterdam, 1998.
O.V. Abramov: Ultrasound in Liquid and Solid Metals, CRC press, Boca Raton, FL, 1994.
Eskin GI, Eskin DG (2014) Ultrasonic Treatment of Light Alloy Melts, 2nd edn. CRC Press, Boca Raton, FL, pp. 129-170
Y. Ozawa, X. Liu, S. Takamori, H. Somekawa, and T. Mukai: Materials Transactions, 2008, vol. 49, pp. 972–975.
T.V. Atamanenko, D.G. Eskin, L. Zhang, and L. Katgerman: Metallugical and Materials Transactions A, 2010, vol. 41, pp. 2056–2066.
N. Srivastava, G.P. Chaudhari, M.Qian: Journal of Materials Processing Technology, 2017, vol. 249, pp. 367-378.
H.R. Kotadia, M. Qian, D.G. Eskin, A. Das: Materials & Design, 2017, vol. 132, pp. 266-274.
Q. Liu, Q. Zhai, F. Qi, and Y. Zha: Materials Letters, 2017, vol. 61, pp. 2422–2425.
J. Kang, X. Zhang,Y. Hu, J. Ma, Y. Hu and T. Huang: ISIJ International, 2014, vol. 54, pp. 281–287.
B. Nagasivamuni, G. Wang, D.H. StJohn, M.S. Dargusch: Journal of Crystal Growth, 2018, vol. 495, pp. 20-28.
R. Chen, D. Zheng, T. Ma, H. Ding, Y. Su, J. Guo, H. Fu: Scientific Reports, 2017, vol. 7, 41463.
D. Ensminger and L.J. Bond: Ultrasonics: Fundamentals, Technologies, and Applications, 3rd ed., CRC Press, Boca Raton, FL, 2012.
Juan A. Gallego-Juárez and Karl F. Graff, Power ultrasonics : applications of high-intensity ultrasound, Woodhead Publishing Ltd, Waltham, Massachusetts, 2015.
Y. Ishiwata, S. Komarov, and Y. Takeda: Proc. 13th Int. Conf. Alum. Alloys (ICAA13), H. Weiland, A.D. Rollett, and W.A. Cassada, eds., TMS (The Minerals, Metals & Materials Society), Warrendale, 2012, pp. 183–88.
G. Wang, P. Croaker, M. Dargusch, D. McGuckin and D. StJohn: Computational Materials Science, 2017, vol. 134, pp. 116-125.
M.C. Schenker, MJBM Pourquie, D.G. Eskin, B.J. Boersma: Ultrasonics Sonochemistry, 2013, vol. 20, pp. 502–509.
G.S.B. Lebon, G. Salloum-Abou-Jaoude, D. Eskin, I. Tzanakis, K. Pericleous, P. Jarry: Ultrasonics Sonochemistry, 2019, vol. 54, pp. 171–182.
G.S.B. Lebon, I. Tzanakis, K. Pericleous, D. Eskin, P.S. Grant: Ultrasonics Sonochemistry, 2019, vol. 55, pp.243-255.
T. Yamamoto and S. Komarov: Light Metals, 2019, pp. 1527–31. https://doi.org/10.1007/978-3-030-05864-7_192.
G. Wang, M.S. Dargusch, M. Qian, D.G. Eskin, and D.H. StJohn: Journal of Crystals Growth, 2014, vol. 408, pp. 119–124.
G. Wang, M.S. Dargusch, M. Qian, D.G. Eskin, and D.H. StJohn: Advanced Engineering Materials, 2018, 1800521, pp. 1–12.
J. Lighthill: Journal of Sound Vibration, 1978, vol. 61, pp. 391–418.
D.H. StJohn, A. Prasad, M.A. Easton, M. Qian: Metallurical and Materials Transactions A, 2015, vol. 46, pp. 4868–4885.
G. Chai, L. Backerud, T. Rolland, L. Arnberg: Metallurical and Materials Transactions A, 1995, vol. 26, pp. 965- 976.
T. Sumitomo, D.H. StJohn, T. Steinberg: Materials Science and Engineering A, 2000, vol. 289, pp. 18-19.
B. Nagasivamuni, G. Wang, D.H. StJohn, and M.S. Dargusch: in Light Met. 2019, Light Met. Symp., TMS Annu. Meet. Exhib., C. Chesonis, ed., San Antonio, TX, 10–14 March 2019, pp. 1579–86.
J. Hutt & D. StJohn: International Journal of Cast Metals Research, 1998, vol. 11, pp. 13-22.
A. Ohno: The Solidification of Metals, Chijin Shokan Co., Tokyo, 1976.
A.Ohno: Solidification - The Separation Theory and its Practical Applications, Springer-Verlag, Berlin Heidelberg New York London Paris Tokyo, 1987
Z. Yin, D. Liang, Y. Chen, Y. Cheng, Q. Zhai: Trans. Nonferrous Metals Soc. China, 2013, vol. 23, pp. 92–97.
Y.J. Li, W.Z. Tao, Y.S. Yang: J. Mater. Process. Technol., 2012, vol. 212, pp. 903–909.
I. Tzanakis, G.S.B Lebon, D. Eskin, K. Pericleous: Ultrasonics Sonochemistry, 2017, vol. 34, pp. 651–662.
S.D. McDonald, K. Nogita, A.K. Dahle: Acta Materitalia, 2004, vol. 52, pp. 4273-4280.
J. Hirsch, B. Skrotzki, G. Gottstein: Aluminium Alloys: Their Physical and Mechanical Properties (ICAA11), Wiley-VCH, Weinheim, 2008, pp. 316–320.
A. Prasad, E. Liotti, S.D. McDonald, K. Nogita, H. Yasuda, P.S. Grant and D.H. StJohn: IOP Conference Series: Materials Science And Engineering, 2015, vol. 84, 012014, pp. 1-9.
Acknowledgments
The authors gratefully acknowledge the financial support from the Defence Materials Technology Center (DMTC) which was established, and supported by the Australian Government’s Defence Future Capability Technology Centres Programme, the Australian Research Council Grant DP140100702, and the ExoMet Project co-funded by the European Commission’s 7th Framework Programme (Contract FP7-NMP3-LA-2012-280421), by the European Space Agency and by the individual partner organizations.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Manuscript submitted May 31, 2019.
Rights and permissions
About this article
Cite this article
Wang, G., Wang, Q., Balasubramani, N. et al. The Role of Ultrasonically Induced Acoustic Streaming in Developing Fine Equiaxed Grains During the Solidification of an Al-2 Pct Cu Alloy. Metall Mater Trans A 50, 5253–5263 (2019). https://doi.org/10.1007/s11661-019-05448-x
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-019-05448-x