An effective method is proposed for processing production waste after firing glass ceramic providing introduction into main production of about one third of original raw material with a marked increase in milling equipment productivity.
Similar content being viewed by others
References
E. I. Suzdal’tsev, M. Yu. Rusin, D. V. Kharitonov, T. V. Zaichuk, and N. I. Ipatova, RF Patent 2366637 MPK C04B 35/19, C04B 33/28. Method for preparing high-density aqueous slips based on lithium aluminium silicate glass, No. 2008102891/03, Claim 01.25.08, Publ. 09.10.09, Byul. No. 25.
E. I. Suzdal’tsev, D. V. Kharitonov, M. M. Tsvetkova, P. M. Savchenko, and M. Yu. Rusin, RF Patent 2513072, MPK C04B 35/14. Method for preparing high-density aqueous slip based on quartz glass, No 2012154132/03, Claim 12.13.12, Publ. 04.20.2014, Byul. No. 11.
Author information
Authors and Affiliations
Corresponding author
Additional information
Part 1 of the article published in Novye Ogneupory No. 12 (2014), Part 2 in No. 2 (2015).
Translated from Novye Ogneupory, No. 4, pp. 34 – 37, April 2015.
Rights and permissions
About this article
Cite this article
Suzdal’tsev, E.I. Production Features of β-Spodumene Composition Glass Ceramic Synthesis. Part 3. Study of the Possibility of Processing Fired β-Spodumene Composition Material1 . Refract Ind Ceram 56, 184–187 (2015). https://doi.org/10.1007/s11148-015-9809-1
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11148-015-9809-1