Fatigue Properties and Morphology of Fatigue Fracture of Bulk Metallic Glass
- 48 Downloads
Changes in the amorphous structure and fatigue resistance of Zr57.5Cu27.3Al8.5Ni6.7 bulk metallic glass are studied. A copper-rich phase produced by cyclic stresses is discovered. This phase observed on the fracture surface may hinder crack propagation. The specimens after fatigue failure have a V shape (do not break into two completely) due to the high density of shear bands and multiple branching of the shear bands in the strained region.