YBCO Superconducting Film Coated on LaAlO3 Substrate by TFA-MOD Process

  • X. M. Cui
  • B. W. Tao
  • J. Xiong
  • X. Z. Liu
  • Y. R. Li
Article

Abstract

Epitaxial YBCO film was coated on (001) LaAlO3 single-crystal substrate by metalorganic deposition of metal trifluoroacetate precursors. From XRD and EDS analysis, it was observed that the film contains CuO or Cu2BaO2 segregation, but transport measurement found the segregation structure does not severely prevent the percolation of supercurrent-carrying material. The YBCO film’s performance is up to 2.4 MA/cm2 with Ic of 137 A/cm-width at 77 K and 0 T, and superconducting transition temperature Tc reaches around 91.3 K with sharp transition temperature ΔTc of 0.36 K.

Keywords

YBCO film TFA-MOD segregation analysis 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. W. Sun, H. S. Kim, B. K. Ji, H. W. Park, G. W. Hong, C. H. Jung, S. D. Park, B. H. Jim, and C. J. Kim, IEEE Trans. Appl. Supercond. 13, 2539 (2003).CrossRefGoogle Scholar
  2. 2.
    Y. Iijima, K. Kakimoto, and T. Saitoh, IEEE Trans. Appl. Supercond . 13, 2466 (2003).CrossRefGoogle Scholar
  3. 3.
    K. R. Marken, S. Hong, B. Czabai, A. C. King, S. S. Shoup, M. K. White, S. L. Krebs, D. M. Mattox, T. Policy, and N. Darnell, IEEE Trans. Appl. Supercond. 13, 2643 (2003).CrossRefGoogle Scholar
  4. 4.
    C. Liu, S. J. Du, and X. Wu, Rare Met. Mater. Eng. 31, 330 (2002).Google Scholar
  5. 5.
    J. Yang, D. Q. Shi, and X. H. Wang, Physica C 341–348, 2499 (2000).Google Scholar
  6. 6.
    M. W. Rupich, U. Schoop, D. T. Verebelyi, C. Thieme, W. Zhang, X. Li, T. Kodenkandath, N. Nquyen, E. Sieqal, D. Buczek, J. Lynch, M. Jowett, E. Thompson, J. S. Wang, J. Scudiere, A. P. Malozemoff, Q. Li, S. Annavarapu, S. Cui, L. Fritzemeier, B. Aldrich, C. Craven, F. Niu, R. Schwall, A. Goyal, and M. Paranthaman, IEEE Trans. Appl. Supercond. 13, 2458 (2003).CrossRefGoogle Scholar
  7. 7.
    J. A. Smith, M. J. Cima., and N. Sonnenberg, IEEE Trans. Appl. Supercond. 9, 1531 (1999).Google Scholar

Copyright information

© Springer Science + Business Media, Inc. 2005

Authors and Affiliations

  • X. M. Cui
    • 1
    • 2
  • B. W. Tao
    • 1
  • J. Xiong
    • 1
  • X. Z. Liu
    • 1
  • Y. R. Li
    • 1
  1. 1.Institute of Microelectronics and Solid State ElectronicsUniversity of Electronic Science and Technology of China (UESTC)ChengduPeople’s Republic of China
  2. 2.Department of Material Science and EngineeringPanzhihua UniversityPanzhihuaPeople’s Republic of China

Personalised recommendations