Hydrothermal conversion of ETS-10 to TS-1



Titanium silicalite-1 (TS-1) was hydrothermally using ETS-10 as a dual source of silicon and titanium after acid and calcination treatment. The conversion process was monitored by XRD, SEM, UV–Vis and FT-IR spectra. Catalytic performance of the prepared TS-1 catalyst was tested by 1-hexene epoxidation using H2O2 as oxidant, which established that the TS-1 converted from ETS-10 has essentially identical physicochemical properties to those of conventional TS-1 prepared using pure alkoxide precursors.


TS-1 ETS-10 Hydrothermal synthesis 1-Hexene epoxidation 



This work was supported by Inha University, and we would like to thank Prof. W.J. Kim of Konkuk University in Korea for help in ETS-10 preparation.


  1. 1.
    C.S. Cundy, P.A. Cox, Microporous Mesoporous Mater. 82, 1 (2005)CrossRefGoogle Scholar
  2. 2.
    Y. Kubota, H. Maekawa, S. Miyata, T. Tatsumi, Y. Sugi, Microporous Mesoporous Mater. 101, 115 (2007)CrossRefGoogle Scholar
  3. 3.
    F.G. Dwyer, P. Chu, J. Catal. 59, 263 (1979)CrossRefGoogle Scholar
  4. 4.
    H. Jon, K. Nakahata, B. Lu, Y. Oumi, T. Sano, Microporous Mesoporous Mater. 96, 72 (2006)CrossRefGoogle Scholar
  5. 5.
    H. Jon, S. Takahashi, H. Sasaki, Y. Oumi, T. Sano, Microporous Mesoporous Mater. 113, 56 (2008)CrossRefGoogle Scholar
  6. 6.
    Y. Kubota, S. Tawada, K. Nakagawa, C. Naitoh, N. Sugimoto, Y. Fukushima, T. Hanaoka, Y. Imada, Y. Sugi, Microporous Mesoporous Mater. 37, 291 (2000)CrossRefGoogle Scholar
  7. 7.
    S.I. Zones, R.A. Van Nordstrand, Zeolites 8, 409 (1988)CrossRefGoogle Scholar
  8. 8.
    S.I. Zones, J.Chem. Soc. Faraday Trans. 86, 3467 (1990)CrossRefGoogle Scholar
  9. 9.
    S.I. Zones, Y. Nakagawa, Microporous Mater. 2, 543 (1994)CrossRefGoogle Scholar
  10. 10.
    R.K. Ahedi, Y. Kubota, Y. Sugi, J. Mater. Chem. 11, 2922 (2001)CrossRefGoogle Scholar
  11. 11.
    M. Matsukata, M. Ogura, T. Osaki, P.R. Hari Prasad Rao, M. Nomura, E. Kikuchi, Top. Catal. 9, 77 (1999)CrossRefGoogle Scholar
  12. 12.
    P.R. Hari Prasad Rao, K. Ueyama, E. Kikuchi, M. Matsukata, Chem. Lett. 27, 311 (1998)Google Scholar
  13. 13.
    S. Inagaki, M. Ogura, T. Inami, Y. Sasaki, E. Kikuchi, M. Matsukata, Microporous Mesoporous Mater. 74, 163 (2004)CrossRefGoogle Scholar
  14. 14.
    S. Tanaka, H. Okada, N. Nakatani, T. Maruo, N. Nishiyama, Y. Miyake, J. Colloid Interface Sci. 333, 491 (2009)CrossRefGoogle Scholar
  15. 15.
    S.M. Kuznicki, U.S. Patent No. 4,853,202 (1989)Google Scholar
  16. 16.
    Z. Lin, J. Rocha, A. Navajas, C. Tellez, J. Coronas, J. Santamaria, Microporous Mesoporous Mater. 67, 79 (2004)CrossRefGoogle Scholar
  17. 17.
    B. Akata, B. Yilmaz, A. Sacco Jr., J. Porous. Mater. 15, 351 (2008)CrossRefGoogle Scholar
  18. 18.
    B.J. Shen, H.F. Li, W.C. Zhang, Y. Zhao, Z.H. Zhang, X.H. Wong, S.K. Shen, Catal. Today 106, 206 (2005)CrossRefGoogle Scholar
  19. 19.
    A. Philippou, M.W. Anderson, J. Catal. 189, 395 (2000)CrossRefGoogle Scholar
  20. 20.
    H.F. Li, B.J. Shen, W.C. Zhang, Y. Zhao, X.H. Wong, Z.H. Zhang, S.K. Shen, Fuel 85, 2445 (2006)CrossRefGoogle Scholar
  21. 21.
    J.M. Marchetti, V.U. Miguel, A.F. Errazu, Renew. Sust. Energ. Rev. 11, 1300 (2007)CrossRefGoogle Scholar
  22. 22.
    J.H. Choi, S.D. Kim, Y.J. Kwon, W.J. Kim, Microporous Mesoporous Mater. 96, 157 (2006)CrossRefGoogle Scholar
  23. 23.
    S. Uma, S. Rodrigues, I.N. Martyanov, K.J. Klabunde, Microporous Mesoporous Mater. 67, 181 (2004)CrossRefGoogle Scholar
  24. 24.
    Y. Goa, H. Yoshitake, P. Wu, T. Tatsumi, Microporous Mesoporous Mater. 70, 93 (2004)CrossRefGoogle Scholar
  25. 25.
    C.C. Pavel, S.-H. Park, A. Dreier, B. Tesche, W. Schmidt, Chem. Mater. 18, 3813 (2006)CrossRefGoogle Scholar
  26. 26.
    W. Fan, R.G. Duan, T. Yokoi, P. Wu, Y. Kubota, T. Tatsumi, J. Am. Chem. Soc. 130, 10150 (2008)CrossRefGoogle Scholar
  27. 27.
    X. Ke, L. Xu, C. Zeng, L. Zhang, N. Xu, Microporous Mesoporous Mater. 106, 68 (2007)CrossRefGoogle Scholar
  28. 28.
    G. Yang, X. Lan, J. Zhuang, D. Ma, L. Zhou, X. Liu, X. Han, X. Bao, Appl. Catal. A 337, 58 (2008)CrossRefGoogle Scholar
  29. 29.
    J. Jarupatrakorn, T.D. Tilley, J. Am. Chem. Soc. 124, 8380 (2002)CrossRefGoogle Scholar
  30. 30.
    S.H. Noh, S.D. Kim, Y.J. Chung, J.W. Park, D.K. Moon, D.T. Hayhurst, W.J. Kim, Microporous Mesoporous Mater. 88, 197 (2006)CrossRefGoogle Scholar
  31. 31.
    D.P. Serrano, M.A. Uguina, G. Ovejero, R. Van Grieken, M. Camacho, Appl. Catal. A 124, 391 (1995)CrossRefGoogle Scholar
  32. 32.
    M. Taramasso, G. Perego, B. Notari, U.S. Patent No. 4,410,501 (1983)Google Scholar
  33. 33.
    X. Yang, J.L. Paillaud, H.F.W.J. van Breukelen, H. Kessler, E. Duprey, Microporous Mesoporous Mater. 46, 1 (2001)CrossRefGoogle Scholar
  34. 34.
    T.K. Das, A.J. Chandwadkar, S. Sivasanker, J. Mol. Catal. A Chem. 107, 199 (1996)CrossRefGoogle Scholar
  35. 35.
    M.A. Camblor, A. Corma, J. Perez-Pariente, Chem. Commun. (1993) 557Google Scholar
  36. 36.
    B. Mihailova, V. Valtchev, S. Mintova, L. Konstantinov, Zeolites 16, 22 (1996)CrossRefGoogle Scholar
  37. 37.
    C. Lamberti, Microporous Mesoporous Mater. 30, 155 (1999)CrossRefGoogle Scholar
  38. 38.
    C.E. Ramachandran, H. Du, Y.J. Kim, M.C. Kung, R.O. Snurr, L.J. Broadbelt, J. Catal. 253, 148 (2008)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2010

Authors and Affiliations

  1. 1.Department of Chemical EngineeringInha UniversityIncheonKorea

Personalised recommendations