Synthesis and enhanced microwave absorption properties of BaM-P/BaM-T/PVB ternary composite with ordered inter-filled structure

  • Published:
Journal of Materials Science: Materials in Electronics Aims and scope Submit manuscript

Abstract

The granular ferrite fillers like BaFe12O19 (BaM-P) usually work as an auxiliary material in the EMA composite, but shows weak electromagnetic wave absorbing (EMA) capability (RL > − 10 dB) when single used. In this work, an orderly filled ferrite/polymer composite has been made by a versatile tape casting method. The micron BaFe12O19 template particles (BaM-T) were obtained by a two-step molten salt method and were oriented and uniformly inserted into the BaM-P/polyvinyl butyral (PVB) composite to form a BaM-T/BaM-P/PVB ternary composite with laminated micro-structure. The composite shows greatly enhanced EMA properties with broadening effective EMA bandwidth. The optimal sample displayed a minimum reflection loss of − 45.8 dB at 6.6 GHz and effective EMA bandwidth (RL < − 10 dB) of 3–18 GHz with 2–5 mm thick. The maximum effective EMA bandwidth of 4.16 GHz was obtained at the thickness of 1.8 mm. Finite element simulation verified that, the strong barrier interfaces attributed by the oriented BaM-T flakes can effectively improve absorptive intensity and decrease sample thickness via a particular multiple reflection mechanism. Additionally, the large range of filler particle size from nano to micro can make the effective bandwidth to be broadened. This work demonstrates the great potential of the ferrite materials for EMA application.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9

Similar content being viewed by others

References

  1. Y. Lin, J. Dai, H. Yang, L. Wang, F. Wang, Chem. Eng. J. 334, 1740–1748 (2018)

    Article  CAS  Google Scholar 

  2. T. Chen, J. Qiu, K. Zhu, Y. Che, Y. Zhang, J. Zhang, H. Li, F. Wang, Z. Wang, J. Mater. Sci.-Mater. Electron. 25, 3664–3673 (2014)

    Article  CAS  Google Scholar 

  3. Y. Wang, X. Wu, W. Zhang, C. Luo, J. Li, Y. Wang, Mater. Res. Bull. 98, 59–63 (2018)

    Article  CAS  Google Scholar 

  4. K. Chen, C. Xiang, L. Li, H. Qian, Q. Xiao, F. Xu, J. Mater. Chem. 22, 6449–6455 (2012)

    Article  CAS  Google Scholar 

  5. B. Quan, X. Liang, G. Ji, Y. Cheng, W. Liu, J. Ma, Y. Zhang, D. Li, G. Xu, J. Alloy. Compd. 728, 1065–1075 (2017)

    Article  CAS  Google Scholar 

  6. M.H. Flaifel, S.H. Ahmad, M.H. Abdullah, R. Rasid, A.H. Shaari, A.A. El-Saleh, S. Appadu, Compos. Sci. Technol. 96, 103–108 (2014)

    Article  CAS  Google Scholar 

  7. M. Oyharcabal, T. Olinga, M.P. Foulc, S. Lacomme, E. Gontier, V. Vigneras, Compos. Sci. Technol. 74, 107–112 (2013)

    Article  CAS  Google Scholar 

  8. Y.J. Chen, M.S. Cao, T.H. Wang, Q. Wan, Appl. Phys. Lett. 84, 3367–3369 (2004)

    Article  CAS  Google Scholar 

  9. H.M. Mesfin, A.C. Baudouin, S. Hermans, A. Delcorte, I. Huynen, C. Bailly, Appl. Phys. Lett. 105, (2014)

  10. Y.C. Du, W.W. Liu, R. Qiang, Y. Wang, X.J. Han, J. Ma, P. Xu, ACS Appl. Mater. Inter. 6, 12997–13006 (2014)

    Article  CAS  Google Scholar 

  11. A. Shah, Y.H. Wang, H. Huang, L. Zhang, D.X. Wang, L. Zhou, Y.P. Duan, X.L. Dong, Z.D. Zhang, Compos. Struct. 131, 1132–1141 (2015)

    Article  Google Scholar 

  12. V.G. Harris, IEEE Trans. Magn. 48, 1075–1104 (2012)

    Article  CAS  Google Scholar 

  13. H.B. Yang, T. Ye, Y. Lin, M. Liu, Appl. Surf. Sci. 357, 1289–1293 (2015)

    Article  CAS  Google Scholar 

  14. V. Sunny, P. Kurian, P. Mohanan, P.A. Joy, M.R. Anantharaman, J. Alloy. Compd. 489, 297–303 (2010)

    Article  CAS  Google Scholar 

  15. T.H. Ting, R.P. Yu, Y.N. Jau, Mater. Chem. Phys. 126, 364–368 (2011)

    Article  CAS  Google Scholar 

  16. W. Hu, L. Wang, Q. Wu, H. Wu, J. Mater. Sci.-Mater. Electron. 25, 5302–5308 (2014)

    Article  CAS  Google Scholar 

  17. K.L. Kelly, E. Coronado, L.L. Zhao, G.C. Schatz, J. Phys. Chem. B 107, 668–677 (2003)

    Article  CAS  Google Scholar 

  18. J. Ryu, J. Choi, D.H. Lim, H.L. Seo, S.Y. Lee, Y. Sohn, J.H. Park, J.H. Jang, H.J. Kim, S.A. Hong, P. Kim, S.J. Yoo, Appl. Catal. B-Environ. 174, 526–532 (2015)

    Article  Google Scholar 

  19. Y.Y. Sun, W.H. Zhang, H.L. Yu, C.L. Hou, D.S. Li, Y.H. Zhang, Y.Q. Liu, J. Alloy. Compd. 638, 182–187 (2015)

    Article  CAS  Google Scholar 

  20. T.T. Chen, F. Deng, J. Zhu, C.F. Chen, G.B. Sun, S.L. Ma, X.J. Yangm, J. Mater. Chem. 22, 15190–15197 (2012)

    Article  CAS  Google Scholar 

  21. Y.F. Tang, Y.Y. Liu, S.X. Yu, S.C. Mu, S.H. Xiao, Y.F. Zhao, F.M. Gao, J. Power Sources 256, 160–169 (2014)

    Article  CAS  Google Scholar 

  22. R.M. Walser, W. Win, P.M. Valanju, IEEE Trans. Magn. 34, 1390–1392 (1998)

    Article  Google Scholar 

  23. L.J. Deng, P.H. Zhou, J.L. Xie, L. Zhang, J. Appl. Phys. 101, 103916 (2007)

    Article  Google Scholar 

  24. G.Z. Xie, X.L. Song, B.S. Zhang, D.M. Tang, Q. Bian, H.X. Lu, Powder Technol. 210, 220–224 (2011)

    Article  CAS  Google Scholar 

  25. M. Han, X. Yin, X. Li, B. Anasori, L. Zhang, L. Cheng, Y. Gogotsi, ACS Appl. Mater. Inter. 9, 20038–20045 (2017)

    Article  CAS  Google Scholar 

  26. D. Micheli, A. Vricella, R. Pastore, M. Marchetti, Carbon 77, 756–774 (2014)

    Article  CAS  Google Scholar 

  27. Q.F. Li, S.Q. Yan, X. Wang, Z.K. Feng, Y.J. Chen, V.G. Harris, IEEE Trans. Magn. 51, 2802404 (2015)

    Google Scholar 

  28. L. He, H.B. Yang, D. Zhou, Y.J. Niu, F. Xiang, H. Wang, J. Phys. D Appl. Phys. 46, 125003 (2013)

    Article  Google Scholar 

  29. P.P. Chang, L. He, D.D. Wei, H. Wang, J. Eur. Ceram. Soc. 36, 2519–2524 (2016)

    Article  CAS  Google Scholar 

  30. D.B. Hovis, K.T. Faber, Scr. Mater. 44, 2525–2529 (2001)

    Article  CAS  Google Scholar 

  31. Y.Y. Ren, L. Yang, L.D. Wang, T.T. Xu, G.L. Wu, H.J. Wu, Powder Technol. 281, 20–27 (2015)

    Article  CAS  Google Scholar 

  32. L.B. Kong, Z.W. Li, L. Liu, R. Huang, M. Abshinova, Z.H. Yang, C.B. Tang, P.K. Tan, C.R. Deng, S. Matitsine, Int. Mater. Rev. 58, 203–259 (2013)

    Article  CAS  Google Scholar 

  33. B.J.P. Adohi, V. Laur, B. Haidar, C. Brosseau, Appl. Phys. Lett. 104, 082902 (2014)

  34. M.Z. Wu, Y.D. Zhang, S. Hui, T.D. Xiao, S.H. Ge, W.A. Hines, J.I. Budnick, G.W. Taylor, Appl. Phys. Lett. 80, 4404–4406 (2002)

    Article  CAS  Google Scholar 

  35. P.B. Liu, Y. Huang, X. Zhang, Compos. Sci. Technol. 107, 54–60 (2015)

    Article  CAS  Google Scholar 

  36. J.P. Calame, J. Appl. Phys. 99, 084101 (2006)

    Article  Google Scholar 

  37. Y. Zhang, Y. Huang, T. Zhang, H. Chang, P. Xiao, H. Chen, Z. Huang, Y. Chen, Adv. Mater. 27, 2049–2053 (2015)

    Article  CAS  Google Scholar 

  38. W. She, H. Bi, Z. Wen, Q. Liu, X. Zhao, J. Zhang, R. Che, ACS Appl. Mater. Int. 8, 9782–9789 (2016)

    Article  CAS  Google Scholar 

  39. L.S. Fu, J.T. Jiang, C.Y. Xu, L. Zhen, Crystengcomm. 14, 6827–6832 (2012)

    Article  CAS  Google Scholar 

  40. X. Wang, R. Gong, H. Luo, Z. Feng, J. Alloy. Compd. 480, 761–764 (2009)

    Article  CAS  Google Scholar 

  41. J. Huang, Y. Qin, J. Li, X. Jiang, F. Ma, J. Nanosci. Nanotechnol. 8, 3967–3972 (2008)

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work is supported by National Natural Science Foundation of China (Grant No. 51602256), Natural Science Foundation of Shaanxi Province of China (Grant No. 2017JQ5024), Young Talent fund of University Association for Science and Technology in Shaanxi, China (Grant No. 20170514).

Author information

Authors and Affiliations

  1. School of Automation and Information Engineering, Xi’an University of Technology, Xi’an, 710048, China

    Li He, Yuchen Zhao, Jianhong Wang, Pengyu Wang, Hongwei Xie & Chao Zhang

Authors
  1. Li He
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Yuchen Zhao
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Jianhong Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Pengyu Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Hongwei Xie
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Chao Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Li He.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

He, L., Zhao, Y., Wang, J. et al. Synthesis and enhanced microwave absorption properties of BaM-P/BaM-T/PVB ternary composite with ordered inter-filled structure. J Mater Sci: Mater Electron 29, 7730–7738 (2018). https://doi.org/10.1007/s10854-018-8769-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10854-018-8769-x

Search

Navigation