Interfacial reaction issues for lead-free electronic solders

  • Published:
Journal of Materials Science: Materials in Electronics Aims and scope Submit manuscript

Abstract

The interfacial reactions between Sn-based solders and two common substrate materials, Cu and Ni, are the focuses of this paper. The reactions between Sn-based solders and Cu have been studied for several decades, and currently there are still many un-resolved issues. The reactions between Sn-based solders and Ni are equally challenging. Recent studies further pointed out that Cu and Ni interacted strongly when they were both present in the same solder joint. While this cross-interaction introduces complications, it offers opportunities for designing better solder joints. In this study, the Ni effect on the reactions between solders and Cu is discussed first. The presence of Ni can in fact reduce the growth rate of Cu3Sn. Excessive Cu3Sn growth can lead to the formation of Kirkendall voids, which is a leading factor responsible for poor drop test performance. The Cu effect on the reactions between solders and Ni is then covered in detail. The knowledge gained from the Cu and Ni effects is applied to explain the recently discovered intermetallic massive spalling, a process that can severely weaken a solder joint. It is pointed out that the massive spalling was caused by the shifting of the equilibrium phase as more and more Cu was extracted out of the solder by the growing intermetallic. Lastly, the problems and opportunities brought on by the cross-interaction of Cu and Ni across a solder joint is presented.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16
Fig. 17
Fig. 18
Fig. 19
Fig. 20
Fig. 21
Fig. 22
Fig. 23
Fig. 24
Fig. 25
Fig. 26

Similar content being viewed by others

References

  1. A. Rahn (ed.), in The Basics of Soldering (John Wiely & Sons, New York, 1993)

  2. J.H. Lau (ed.), in Flip Chip Technology (McGraw Hill, New York, 1996)

  3. K.N. Tu, K. Zeng, Mater. Sci. Eng. R34, 1 (2001)

    CAS  Google Scholar 

  4. W.G. Bader, Weld. J. Res. Suppl. 28, 551s (1969)

    Google Scholar 

  5. C.J. Thwaites, Electroplat. Met. Finish. 26, 10 (1973)

    CAS  Google Scholar 

  6. W.A. Mulholland, D.L. Willyard, Weld. J. Res. Suppl. 54, 466s (1974)

    Google Scholar 

  7. R. Duckett, M.L. Ackroyd, Electroplat. Met. Finish. 29, 13 (1976)

    CAS  Google Scholar 

  8. H. Heinzel, K.E. Saeger, Gold Bull. 9, 7 (1976)

    CAS  Google Scholar 

  9. D.M. Jacobson, G. Jumpston, Gold Bull. 22, 9 (1989)

    CAS  Google Scholar 

  10. P.A. Kramer, J. Glazer, J.W. Morris, Jr., Metall. Mater. Trans. 25A, 1249 (1994)

    CAS  Google Scholar 

  11. J. Glazer, Inter. Mater. Rev. 40, 65 (1995)

    CAS  Google Scholar 

  12. F.G. Yost, Gold Bull. 10, 94 (1977)

    CAS  Google Scholar 

  13. C.E. Ho, Y.M. Chen, C.R. Kao, J. Electron. Mater. 28, 1231 (1999)

    CAS  Google Scholar 

  14. C.E. Ho, S.Y. Tsai, C.R. Kao, IEEE Trans. Adv. Packag. 24, 493 (2001)

    Article  CAS  Google Scholar 

  15. Z. Huang, P.P. Conway, C. Liu, R.C. Thomson, J. Electron. Mater. 33, 1227 (2004)

    CAS  Google Scholar 

  16. J.W. Jang, P.G. Kim, K.N. Tu, D.R. Frear, P. Thomson, J. Appl. Phys. 85, 8456 (1999)

    Article  CAS  Google Scholar 

  17. P. Liu, Z. Xu, J.K. Shang, Metall. Mater. Trans. 31A, 2857 (2000)

    CAS  Google Scholar 

  18. H. Matsuki, H. Ibuka, H. Saka, Sci. Technol. Adv. Mater. 3, 261 (2002)

    Article  CAS  Google Scholar 

  19. K. Zeng, V. Vuorinen, J.K. Kivilahti, IEEE Trans. Electron. Packag. Manufact. 25, 162 (2002)

    Article  CAS  Google Scholar 

  20. S.K. Kang, D.Y. Shih, K. Fogel, P. Lauro, M.J. Yim, G.G. Advocate, Jr., M. Griffin, C. Goldsmith, D.W. Henderson, T.A. Gosselin, D.E. King, J.J. Konrad, A. Sarkhel, K.J. Puttlitz, IEEE Trans. Electron. Packag. Manufact. 25, 155 (2002)

    Article  CAS  Google Scholar 

  21. Y.D. Jeon, S. Nieland, A. Ostmann, H. Reichl, K.W. Paik, J. Electron. Mater. 32, 548 (2003)

    CAS  Google Scholar 

  22. N. Torazawa, S. Arai, Y. Takase, K. Sasaki, H. Saka, Mater. Trans. 44, 1438 (2003)

    Article  CAS  Google Scholar 

  23. T. Hiramori, M. Ito, M. Yoshikawa, A. Hirose, K.F. Kobayashi, Mater. Trans. 44, 2375 (2003)

    Article  CAS  Google Scholar 

  24. C.W. Hwang, K. Suganuma, M. Kiso, S. Hashimoto, J. Mater. Res. 18, 2540 (2003)

    CAS  Google Scholar 

  25. C.W. Hwang, K. Suganuma, M. Kiso, S. Hashimoto, J. Electron. Mater. 33, 1200 (2004)

    CAS  Google Scholar 

  26. M. He, Z. Chen, G. Qi, Acta Mater. 52, 2047 (2004)

    Article  CAS  Google Scholar 

  27. J.W. Yoon, S.W. Kim, S.B. Jung, J. Alloys Compd. 385, 192 (2004)

    Article  CAS  Google Scholar 

  28. Y.D. Jeon, K.W. Paik, A. Ostmann, H. Reichl, J. Electron. Mater. 34, 80 (2005)

    CAS  Google Scholar 

  29. T. Laurila, V. Vuorinen, J.K. Kivilahti, Mater. Sci. Eng. R49, 1 (2005)

    CAS  Google Scholar 

  30. T.T. Mattila, J.K. Kivilahti, J. Electron. Mater. 34, 969 (2005)

    CAS  Google Scholar 

  31. A. Kumar, M. He, Z. Chen, Surf. Coat. Tech. 198, 283 (2005)

    Article  CAS  Google Scholar 

  32. S.T. Kao, J.G. Duh, J. Electron. Mater. 34, 1129 (2005)

    CAS  Google Scholar 

  33. J.W. Yoon, S.B. Jung, J. Alloys Compd. 396, 122 (2005)

    Article  CAS  Google Scholar 

  34. D.G. Kim, J.W. Kim, S.B. Jung, Mater. Sci. Eng. B 121, 204 (2005)

    Article  CAS  Google Scholar 

  35. C.Y. Liu, K.N. Tu, T.T. Sheng, C.H. Tung, D.R. Frear, P. Elenius, J. Appl. Phys. 87, 750 (2000)

    Article  CAS  Google Scholar 

  36. P.S. Teo, Y.W. Huang, C.H. Tung, M.R. Marks, T.B. Lim, in Proc. of 2000 IEEE Electron. Comp. Tech. Conf. (ECTC), p. 33

  37. F. Zhang, M. Li, C.C. Chum, K.N. Tu, J. Mater. Res. 17, 2757 (2002)

    CAS  Google Scholar 

  38. F. Zhang, M. Li, C.C. Chum, Z.C. Shao, J. Electron. Mater. 32, 123 (2003)

    CAS  Google Scholar 

  39. M. Abtew, G. Selvaduray, Mater. Sci. Eng. R27, 95 (2000)

    CAS  Google Scholar 

  40. K. Suganuma, Curr. Opin. Solid State Mater. Sci. 5, 55 (2001)

    Article  CAS  Google Scholar 

  41. K. Zeng, K.N. Tu, Mater. Sci. Eng. R38, 55 (2002)

    CAS  Google Scholar 

  42. K.N. Tu, A.M. Gusak, M. Li, J. Appl. Phys. 93, 1335 (2003)

    Article  CAS  Google Scholar 

  43. C.M.L. Wu, D.Q. Yu, C.M.T. Law, L. Wang, Mater. Sci. Eng. R44, 1 (2004)

    CAS  Google Scholar 

  44. S.K. Kang, P.A. Lauro, D.-Y. Shih, D.W. Henderson, K.J. Puttlitz, IBM J. Res. & Dev. 49, 607 (2005)

    Article  CAS  Google Scholar 

  45. S. Ahat, M. Sheng, L. Luo, J. Electron. Mater. 30, 1317 (2001)

    CAS  Google Scholar 

  46. T.-C. Chiu, K. Zeng, R. Stierman, D. Edwards, K. Ano, in Proceedings of 2004 IEEE Electron. Comp. Tech. Conf. (ECTC), p. 1256

  47. M. Date, T. Shoji, M. Fujiyoshi, K. Sato, K. N. Tu, Proceedings of 2004 IEEE Electron. Comp. Tech. Conf. (ECTC), p. 668

  48. P.T. Vianco, J.A. Rejent, P.F. Hlava, J. Electron. Mater. 33, 991 (2004)

    CAS  Google Scholar 

  49. P. Borgesen, D. W. Henderson, Report of Universal Instruments (http://www.uci.com), (2004)

  50. K. Zeng, R. Stierman, T.-C. Chiu, D. Edwards, K. Ano, K.N. Tu, J. Appl. Phys. 97, 024508 (2005)

    Google Scholar 

  51. Z. Mei, M. Ahmad, M. Hu, G. Ramakrishna, in Proceedings of 2005 IEEE Electron. Comp. Tech. Conf. (ECTC), p. 415

  52. M. Oh, Doctor Dissertation, Lehigh University, (1994)

  53. S.W. Chen, S.H. Wu, S.W. Lee, J. Electron. Mater. 32, 1188 (2003)

    Google Scholar 

  54. J.Y. Tsai, Y.C. Hu, C.M. Tsai, C.R. Kao, J. Electron. Mater. 32, 1203 (2003)

    CAS  Google Scholar 

  55. C.M. Chung, P.C. Shih, K.L. Lin, J. Electron. Mater. 33, 1 (2004)

    Google Scholar 

  56. L. Garner, S. Sane, D. Suh, T. Byrne, A. Dani, T. Martin, M. Mello, M. Patel, R. Williams, Intel Technol. J. 9, 297 (2005)

    Google Scholar 

  57. I.E. Anderson, J.L. Harringa, J. Electron. Mater. 35, 94 (2006)

    CAS  Google Scholar 

  58. T.B. Massalski (ed.), in Binary Alloy Phase Diagrams (ASM International, Metal Park, OH, 1990) p. 1481

  59. P. Nash, A. Nash, Bull. Alloy Phase Diag. 6, 350 (1985)

    CAS  Google Scholar 

  60. E.K. Ohriner, Weld. J. Res. Suppl. 7, 191 (1987)

    Google Scholar 

  61. S. Bader, W. Gust, H. Hieber, Acta. Metall. Mater. 43, 329 (1995)

    CAS  Google Scholar 

  62. D. Gur, M. Bamberger, Acta Mater. 46, 4917 (1998)

    Article  CAS  Google Scholar 

  63. J.A. van Beek, S.A. Stolk, F.J. J. van Loo, Z. Metallkde 73, 441 (1982)

    Google Scholar 

  64. C.M. Liu, M.S. Thesis, National Central University, Taiwan (2000)

  65. K.-W. Moon, W.J. Boettinger, U.R. Kattner, F.S. Biancaniello, C.A. Handwerker, J. Electron. Mater. 29, 1122 (2000)

    CAS  Google Scholar 

  66. NEMI (National Electronics Manufacturing Initiative)-Workshop on Modeling and Data Needs for Lead-Free solders, (New Orleans, LA, February 15th 2001)

  67. Soldertec-ITRI, Lead-free alloys-the way forward, October 1999 (http://www.lead-free.org)

  68. IDEALS (International Dental Ethics and Law Society), Improved design life and environmentally aware manufacturing of electronics assemblies by lead-free soldering, Brite-Euram contract BRPR-CT96-0140, project number BE95-1994 (1994–1998)

  69. JEITA (Japan Electronics and Information Technology Industries Association), Lead-Free Roadmap 2002, v 2.1, (2002)

  70. K.F. Seeling, D.G. Lockard, United States Patent, Patent No. 5352407, (Oct 1994)

  71. IPC Roadmap, Assembly of Lead-Free Electronics, 4th draft, IPC, (Northbrook, IL, June 2000)

  72. L.S. Bai, Taiwan Printed Circuit Association (TPCA) Magazine 31, 21 (2006)

    Google Scholar 

  73. C.E. Ho, Y.L. Lin, C.R. Kao, Chem. Mater. 14, 949 (2002)

    Article  CAS  Google Scholar 

  74. J.W. Jang, D.R. Frear, T.Y. Lee, K.N. Tu, J. Appl. Phys. 88, 6359 (2000)

    Article  CAS  Google Scholar 

  75. C.E. Ho, R.Y. Tsai, Y.L. Lin, C.R. Kao, J. Electron. Mater. 31, 584 (2002)

    CAS  Google Scholar 

  76. S.M. Hong, C.S. Kang, J.P. Jung, IEEE Trans. Adv. Packag. 27, 90 (2004)

    Article  CAS  Google Scholar 

  77. G.Y. Jang, J.G. Duh, J. Electron. Mater. 34, 68 (2005)

    CAS  Google Scholar 

  78. C.M. Liu, C.E. Ho, W.T. Chen, C.R. Kao, J. Electron. Mater. 30, 1152 (2001)

    CAS  Google Scholar 

  79. M. Li, K.Y. Lee, D.R. Olsen, W.T. Chen, B.T. C. Tan, S. Mhaisalkar, IEEE Trans. Electron. Packag. 25, 185 (2002)

    Article  CAS  Google Scholar 

  80. S.K. Kang, W.K. Choi, M.J. Yim, D.Y. Shih, J. Electron. Mater. 31, 1292 (2002)

    CAS  Google Scholar 

  81. L.C. Shiau, C.E. Ho, C.R. Kao, Solder. Surf. Mount Tech. 14/3, 25 (2002)

    Google Scholar 

  82. M.O. Alam, Y.C. Chan, K.N. Tu, Chem. Master. 15, 4340 (2003)

    Article  CAS  Google Scholar 

  83. K.Y. Lee, M. Li, J. Electron. Mater. 32, 906 (2003)

    CAS  Google Scholar 

  84. C.B. Lee, J.W. Yoon, S.J. Suh, S.B. Jung, C.W. Yang, C.C. Shur, Y.E. Shin, J. Mater. Sci.: Mater. Electron. 14, 487 (2003)

    Article  CAS  Google Scholar 

  85. A. Sharif, M.N. Islam, Y.C. Chan, Mater. Sci. Eng. B 113, 184 (2004)

    Article  CAS  Google Scholar 

  86. D.Q. Yu, C.M. L. Wu, D.P. He, N. Zhao, L. Wang, J.K.L. Lai, J. Mater. Res. 20, 2205 (2005)

    Article  CAS  Google Scholar 

  87. W.T. Chen, C.E. Ho, C.R. Kao, J. Mater. Res. 17, 263 (2002)

    CAS  Google Scholar 

  88. W.C. Luo, C.E. Ho, J.Y. Tsai, Y.L. Lin, C.R. Kao, Mater. Sci. Eng. A 396, 385 (2005)

    Article  CAS  Google Scholar 

  89. C.E. Ho, W.C. Luo, S.C. Yang, C.R. Kao, in Proceedings of IMAPS Taiwan 2005 International Technical Symposium (Taipei, June 2005), p. 98

  90. C.E. Ho, Y.W. Lin, S.C. Yang, C.R. Kao, in Proceedings of the 10th International Symposium on Advanced Packaging Materials: Processes, Properties and Interface, IEEE/CPMT (Irvine, March 2005), p. 39

  91. C.E. Ho, Y.W. Lin, S.C. Yang, C.R. Kao, D. S. Jiang, J. Electron. Mater. 35, 1017 (2006)

    CAS  Google Scholar 

  92. M.O. Alam, Y.C. Chan, K.N. Tu, J.K. Kivilahti, Chem. Mater. 17, 2223 (2005)

    Article  CAS  Google Scholar 

  93. K.S. Kim, S.H. Huh, K. Suganuma, J. Alloys Compd. 352, 226 (2003)

    Article  CAS  Google Scholar 

  94. J.S. Ha, T.S. Oh, K.N. Tu, J. Mater. Res. 18, 2109 (2003)

    CAS  Google Scholar 

  95. C.H. Wang, S.W. Chen, Acta Mater. 54, 247 (2006)

    Article  CAS  Google Scholar 

  96. S.K. Kang, W.K. Choi, D.Y. Shih, P. Lauro, D.W. Henderson, T. Gosselin, D.N. Leonard, in Proceedings of 2002 IEEE Electron. Comp. Tech. Conf. (ECTC), p. 146

  97. Y. Zheng, C. Hillman, P. McCluskey, in Proceedings of 2002 IEEE Electron. Comp. Tech. Conf. (ECTC), p. 1226

  98. M.D. Cheng, S.Y. Chang, S.F. Yen, T.H. Chuang, J. Electron. Mater. 33, 171 (2004)

    CAS  Google Scholar 

  99. J.H. L. Pang, T.H. Low, B.S. Xiong, X. Luhua, C.C. Neo, Thin Sol. Films, 462–463, 370 (2004)

    Article  CAS  Google Scholar 

  100. J.W. Yoon, S.W. Kim, J.M. Koo, D.G. Kim, S.B. Jung, J. Electron. Mater. 33, 1190 (2004)

    CAS  Google Scholar 

  101. J.W. Yoon, S.W. Kim, S.B. Jung, J. Alloys Compd. 391, 82 (2005)

    Article  CAS  Google Scholar 

  102. C.B. Lee, S.B. Jung, Y.E. Shin, C.C. Shur, Mater. Trans. 43, 1858 (2002)

    Article  CAS  Google Scholar 

  103. A. Zribi, A. Clark, L. Zavalij, P. Borgesen, E.J. Cotts, J. Electron. Mater. 30, 1157 (2001)

    CAS  Google Scholar 

  104. G. Ghosh, Acta Mater. 49, 2609 (2001)

    Article  CAS  Google Scholar 

  105. G. Ghosh, J. Electron. Mater. 33, 229 (2004)

    CAS  Google Scholar 

  106. C.E. Ho, Doctor Dissertation, National Central University, Taiwan, (2002)

  107. C.E. Ho, L.C. Shiau, C.R. Kao, J. Electron. Mater. 31, 1264 (2002)

    CAS  Google Scholar 

  108. L.P. Lehman, S.N. Athavale, T.Z. Fullem, A.C. Giamis, R.K. Kinyanjui, M. Lowenstein, K. Mather, R. Patel, D. Rae, J.Wang, Y. Xing, L. Zavalij, P. Borgesen, E.J. Cotts, J. Electron. Mater. 33, 1429 (2004)

    CAS  Google Scholar 

  109. D.W. Henderson, T. Gosselin, A. Sarkhel, S.K. Kang, W.K. Choi, D.Y. Shih, C. Goldsmith, K. Puttlitz, J. Mater. Res. 17, 2775 (2002)

    CAS  Google Scholar 

  110. S.K. Kang, W.K. Choi, D.Y. Shih, D.W. Henderson, T. Gosselin, A. Sarkhel, C. Goldsmith, K. Puttlitz, in Proceedings of 2003 IEEE Electron. Comp. Tech. Conf. (ECTC), p. 64

  111. S.K. Kang, W.K. Choi, D.Y. Shih, D.W. Henderson, T. Gosselin, A. Sarkhel, C. Goldsmith, K. Puttlitz, J. Minerals Metals Mater. Soc. 55, 61 (2003)

    CAS  Google Scholar 

  112. S. Terashima, Y. Kariya, T. Hosoi, M. Tanaka, J. Electron. Mater. 32, 1527 (2003)

    CAS  Google Scholar 

  113. C.H. Lin, S.W. Chen, C.H. Wang, J. Electron. Mater. 31, 907 (2002)

    CAS  Google Scholar 

  114. C.Y. Li, J.G. Duh, J. Mater. Res. 20, 3118 (2005)

    Article  CAS  Google Scholar 

  115. P. Oberndorff, Doctoral Dissertation, Technical University of Eindhoven, (2001)

  116. G.Z. Pan, A.A. Liu, H.K. Kim, K.N. Tu, P.A. Totta, Appl. Phys. Lett. 71, 2946 (1997)

    Article  CAS  Google Scholar 

  117. C.R. Kao, C.E. Ho, L.C. Shiau, Solder Point with Low Speed of Consuming Nickel, R.O.C. patent, patent No. 181410, (2003)

  118. S.J. Wang, C.Y. Liu, J. Electron. Mater. 32, 1303 (2003)

    CAS  Google Scholar 

  119. T.L. Shao, T.S. Chen, Y.M. Huang, C. Chen, J. Mater. Res. 19, 3654 (2004)

    Article  CAS  Google Scholar 

  120. C.M. Tsai, W.C. Luo, C.W. Chang, Y.C. Shieh, C.R. Kao, J. Electron. Mater. 33, 1424 (2004)

    CAS  Google Scholar 

Download references

Acknowledegments

This work was supported by the National Science Council of R.O.C. through grants NSC-94-2216-E-008-001 and NSC-94-2214-E-008-005. The author (CRK) would like to thanks his students for their contributions to the study of soldering reactions (C. M. Liu, J. Y. Tsai, C. W. Chang, W. C. Luo, W. T. Chen, and L. C. Shiau).

Author information

Authors and Affiliations

  1. Department of Chemical Engineering & Materials Science, Michigan State University, East Lansing, MI, 48824, USA

    C. E. Ho

  2. Department of Chemical & Materials Engineering, National Central University, 320, Jhongli City, Taiwan

    S. C. Yang

  3. Department of Materials Science & Engineering, National Taiwan University, Taipei, 106, Taiwan

    C. R. Kao

Authors
  1. C. E. Ho
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. S. C. Yang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. C. R. Kao
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to C. R. Kao.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Ho, C.E., Yang, S.C. & Kao, C.R. Interfacial reaction issues for lead-free electronic solders. J Mater Sci: Mater Electron 18, 155–174 (2007). https://doi.org/10.1007/s10854-006-9031-5

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10854-006-9031-5

Keywords

Search

Navigation