Study of interactions between silicon and coated graphite for application to photovoltaic silicon processing
- 87 Downloads
The crystallization of silicon for photovoltaic applications is currently performed by directional solidification in amorphous silica crucibles. In order to avoid sticking, silica crucibles are coated with a layer of silicon nitride which acts as an interface releasing agent between the silicon and the crucible. Due to silica softening and subsequent transformations during the melting-solidification cycle, Si3N4-coated silica crucibles can be used only one time. A more interesting solution would be to have a graphite crucible which could be used several times in view of its high mechanical performances at elevated temperatures. The goal of this study is to determine in which way the Si3N4 coating can also be used for graphite crucibles. The study is conducted by means of the sessile drop technique and microstructure characterizations carried out by optical microscopy. For comparison purposes, experiments are also performed for the standard configuration of Si3N4-coated silica.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 3.Saito T, Shimura A, Ichikawa S (1981) A new directional solidification technique for polycrystalline solar grade silicon. In: Conference record 15th IEEE photovoltaic specialists conference, pp 576–580Google Scholar
- 5.Melting pot with silicon protective layers, method for applying said layer and the use thereof, Patent US006165425AGoogle Scholar
- 10.Champliaud J, Voytovych R, Rey D, Dechamp C, Huguet C, Drevet B, Camel D, Eustathopoulos N (2013) Mechanisms of oxygen transfer from the releasing coating into the melt during Si ingot crystallization. In: 28th European photovoltaic solar energy conference and exhibition, ParisGoogle Scholar
- 11.Huguet C (2012) Optimisation du couple revêtement anti-adhérent/matériau de creuset pour la cristallisation du Si-PV: application au moulage direct des wafers de Si. PhD Dissertation, INP Grenoble, 2012Google Scholar