Influence of multiphase on the strain hardening behavior of 60Si2CrVAT spring steel treated by a Q–P–T process

  • Yun Jiang
  • Yilong Liang
  • Chunhong Yin
  • Shaolei Long
  • Fei Zhao
  • Yu Xiao
Metals
  • 10 Downloads

Abstract

A strong strain hardening ability in ultra-high strength spring steel 60Si2CrVAT was achieved by the design of multiphase microstructures using a quenching–partitioning–tempering process. The microstructure consisted of ~ 70% martensite/bainite and ~ 30% retained austenite, which was obtained at an optimized partitioning temperature of 380 °C. The corresponding yield strength ratio and the product of strength and elongation were 0.81 and 34,828 MPa%, respectively. Interestingly, this sample exhibited a double-stage strain hardening characteristic with a concave-down shape, which was distinct from that of the other samples. The excellent performance of the ultra-high strength spring steel was mainly due to the interactions between the multiple phases and the stability of the retained austenite during cold deformation. This paper provides a new way of obtaining a strong strain hardening ability in ultra-high strength steels, which is expected to be applicable to the cold coiling process.

Notes

Acknowledgements

The research is jointly supported by the National Natural Science Foundation of China (Grant Nos. 51461006 and 51571066), the Natural Science Foundation of the Guizhou Province, China (Grant Nos. [2014]2003 and [2014] 6012) and the Guizhou Science and Technology Project (Grant No. (2015) 7646).

References

  1. 1.
    Prawoto Y, Sato N, Otani I, Ikeda M (2004) Carbon restoration for decarburized layer in spring steel. J Mater Eng Perform 13(5):627–636CrossRefGoogle Scholar
  2. 2.
    Wu R, Li W, Zhou S, Zhong Y, Wang L, Jin X (2014) Effect of retained austenite on the fracture toughness of quenching and partitioning (Q&P)-treated sheet steels. Metall Mater Trans A 45(4):1892–1902CrossRefGoogle Scholar
  3. 3.
    Hu J, Du LX, Wang JJ, Gao CR, Yang TZ, Wang AY, Misra RDK (2013) Microstructures and mechanical properties of a new as-hot-rolled high-strength DP steel subjected to different cooling schedules. Metall Mater Trans A 44(11):4937–4947CrossRefGoogle Scholar
  4. 4.
    Darabi AC, Chamani HR, Kadkhodapour J, Anaraki AP, Alaie A, Ayatollahi MR (2017) Micromechanical analysis of two heat-treated dual phase steels: dp800 and dp980. Mech Mater 110:68–83CrossRefGoogle Scholar
  5. 5.
    Tomita Y, Morioka K (1997) Effect of microstructure on transformation-induced plasticity of silicon-containing low-alloy steel. Mater Charact 38(4–5):243–250CrossRefGoogle Scholar
  6. 6.
    Li ZC, Ding H, Misra RDK, Cai ZH (2017) Deformation behavior in cold-rolled medium-manganese trip steel and effect of pre-strain on the lüders bands. Mater Sci Eng A 679:230–239CrossRefGoogle Scholar
  7. 7.
    Vercammen S, Blanpain B, Cooman BCD, Wollants P (2004) Cold rolling behaviour of an austenitic Fe–30Mn–3Al–3Si TWIP-steel: the importance of deformation twinning. Acta Mater 52(7):2005–2012CrossRefGoogle Scholar
  8. 8.
    Kusakin P, Belyakov A, Molodov DA, Kaibyshev R (2017) On the effect of chemical composition on yield strength of twip steels. Mater Sci Eng A 687:82–84CrossRefGoogle Scholar
  9. 9.
    Srivastava AK, Jha G, Gope N, Singh SB (2006) Effect of heat treatment on microstructure and mechanical properties of cold rolled C-Mn–Si TRIP-aided steel. Mater Charact 57(2):127–135CrossRefGoogle Scholar
  10. 10.
    Srivastava AK, Bhattacharjee D, Jha G, Gope N, Singh SB (2007) Microstructural and mechanical characterization of C–Mn–Al–Si cold-rolled trip-aided steel. Mater Sci Eng A 445(6):549–557CrossRefGoogle Scholar
  11. 11.
    Bachmaier A, Krizan D, Hausmann K, Pichler A (2013) Development of TBF steels with 980 MPa tensile strength for automotive applications: microstructure and mechanical properties. Int Symp New Dev Adv High Strength Sheet Steels 4:413–416Google Scholar
  12. 12.
    Speer JG, Matlock DK, Cooman BCD, Schroth JG (2003) Carbon partitioning into austenite after martensite transformation. Acta Mater 51(9):2611–2622CrossRefGoogle Scholar
  13. 13.
    Speer JG, Assunção FCR, Matlock DK, Edmonds DV (2005) The “quenching and partitioning” process: background and recent progress. Mater Res 8(4):417–423CrossRefGoogle Scholar
  14. 14.
    Speer JG, Moor ED, Findley KO, Matlock DK, Cooman BCD, Edmonds DV (2011) Analysis of microstructure evolution in quenching and partitioning automotive sheet steel. Metall Mater Trans A 42(12):3591–3601CrossRefGoogle Scholar
  15. 15.
    Hong SC, Ahn JC, Sang YN, Kim SJ, Yang HC, Speer JG, Matlock DK (2007) Mechanical properties of high-Si plate steel produced by the quenching and partitioning process. Met Mater Int 13(6):439–445CrossRefGoogle Scholar
  16. 16.
    Bagliani EP, Santofimia MJ, Zhao L, Sietsma J, Anelli E (2013) Microstructure, tensile and toughness properties after quenching and partitioning treatments of a medium-carbon steel. Mater Sci Eng A 559:486–495CrossRefGoogle Scholar
  17. 17.
    Wang X, Zhong N, Rong YH, Hsu TY, Wang L (2009) Novel ultrahigh-strength nanolath martensitic steel by quenching–partitioning–tempering process. J Mater Res 24(1):260–267CrossRefGoogle Scholar
  18. 18.
    Zhang K, Xu WZ, Guo ZH, Rong YH (2011) Effects of novel Q–P–T and traditional Q–T processes on the microstructure and mechanical properties of martensitic steels with different carbon content. Acta Metall Sin 47(4):489–496 (translated from Chinese) Google Scholar
  19. 19.
    Seo EJ, Cho L, Estrin Y, Cooman BCD (2016) Microstructure-mechanical properties relationships for quenching and partitioning (Q&P) processed steel. Acta Mater 113:124–139CrossRefGoogle Scholar
  20. 20.
    Xu T, Feng Y, Jin Z, Song S, Wang D (2012) Determination of the maximum strain–hardening exponent. Mater Sci Eng A 550(31):80–86CrossRefGoogle Scholar
  21. 21.
    Bowen AW, Partridge PG (1974) Limitations of the Hollomon strain-hardening equation. J Phys D Appl Phys 7(7):969–978CrossRefGoogle Scholar
  22. 22.
    Wang Y, Zhang K, Guo Z, Chen N, Rong YH (2012) A new effect of retained austenite on ductility enhancement in high strength bainitic steel. Mater Sci Eng A 552(34):288–294CrossRefGoogle Scholar
  23. 23.
    Somani MC, Porter DA, Karjalainen LP, Misra RDK (2014) On various aspects of decomposition of austenite in a high-silicon steel during quenching and partitioning. Metall Mater Trans A 45(3):1247–1257CrossRefGoogle Scholar
  24. 24.
    Koistinen DP, Marburger RE (1959) A general equation prescribing the extent of the austenite-martensite transformation in pure iron-carbon alloys and plain carbon steels. Acta Metall 7(1):59–60CrossRefGoogle Scholar
  25. 25.
    Krauss G (1990) STEELS: heat treatment and processing principles. American Society for Metals, Metals ParkGoogle Scholar
  26. 26.
    Magee CL (1970) The nucleation of martensite, in phase transformation. American Society for Metals, Metals Park, pp 115–116Google Scholar
  27. 27.
    Ju DY, Narazaki M, Kamisugi H (2000) Computer predictions and experimental verification of residual stresses and distortion in carburizing–quenching of steel. J Shanghai Jiaotong Univ 5(1):165–172Google Scholar
  28. 28.
    Jirková H, Mašek B, Wagner FX, Langmajerová D, Kučerová L, Treml R, Kiener D (2014) Influence of metastable retained austenite on macro and micromechanical properties of steel processed by the q&p process. J Alloys Compd 615(S1):S163–S168CrossRefGoogle Scholar
  29. 29.
    Chang GL, Kim SJ, Lee TH, Lee S (2004) Effects of volume fraction and stability of retained austenite on formability in a 0.1C–1.5Si–1.5Mn–0.5Cu TRIP-aided cold-rolled steel sheet. Mater Sci Eng A 371(1):16–23Google Scholar
  30. 30.
    Dijk NHV, Butt AM, Zhao L, Sietsma J, Offerman SE, Wright JP, Zwaag SVD (2005) Thermal stability of retained austenite in TRIP steels studied by synchrotron X-ray diffraction during cooling. Acta Mater 53(20):5439–5447CrossRefGoogle Scholar
  31. 31.
    Jimenez-Melero E, Dijk NHV, Zhao L, Sietsma J, Offerman SE, Wright JP, Zwaag SVD (2007) Characterization of individual retained austenite grains and their stability in low-alloyed trip steels. Acta Mater 55(20):6713–6723CrossRefGoogle Scholar
  32. 32.
    Caballero FG, Carlos G, Jesus SM, Garcia DAC (2008) Effects of morphology and stability of retained austenite on the ductility of TRIP-aided bainitic steels. Trans Iron Steel Inst Jpn 48(9):1256–1262CrossRefGoogle Scholar
  33. 33.
    Ju XH, Tian ZH, Cui GB, Men Y, Cai N (2014) Stability of retained austenite in quenching and partitioning steel. Trans Mater Heat Treat 35(10):119–124 (Translated from Chinese) Google Scholar
  34. 34.
    Chiang J, Lawrence B, Boyd JD, Pilkey AK (2011) Effect of microstructure on retained austenite stability and work hardening of trip steels. Mater Sci Eng A 528(13–14):4516–4521CrossRefGoogle Scholar
  35. 35.
    Mark AF, Wang X, Essadiqi E, Embury JD, Boyd JD (2013) Development and characterization of model trip steel microstructures. Mater Sci Eng A 576(576):108–117CrossRefGoogle Scholar
  36. 36.
    Chiang J, Boyd JD, Pilkey AK (2015) Effect of microstructure on retained austenite stability and tensile behavior in an aluminum-alloyed trip steel. Mater Sci Eng A 638:132–142CrossRefGoogle Scholar
  37. 37.
    Tang C, Zhu J, Zhang Y (1994) Effect of strain rate ε on strain hardening exponent n of some metallic materials. Acta Metall Sin 7(3):183–186Google Scholar
  38. 38.
    Ashby MF (1970) The deformation of plastically non-homogeneous materials. Philos Mag 21(170):399–424CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  1. 1.School of Mechanical EngineeringGuizhou UniversityGuiyangChina
  2. 2.College of Materials and MetallurgyGuizhou UniversityGuiyangChina
  3. 3.Guizhou Key Laboratory of Materials Strength and StructureGuizhou UniversityGuiyangChina
  4. 4.Guizhou Key Laboratory of High Performance Metal Structure and Manufacture TechnologyGuiyangChina
  5. 5.National Local Co-construction Engineering Laboratory for High Performance Metal Structure Material and Manufacture TechnologyGuiyangChina

Personalised recommendations