Study of the alkali metal poisoning resistance of a Co-modified Mn/Ni foam catalyst in low-temperature flue gas SCR DeNO x
- 343 Downloads
A Co–Mn/Ni foam catalyst and alkali metal K-poisoned catalyst were prepared by an impregnation method using foamed Ni metal as a carrier. Mn was the active component, and Co was a trace auxiliary. The effects of different levels of alkali metal K poisoning and different concentrations of Co auxiliaries on the K poisoning resistance of the catalyst were studied. The results showed that the number of Brønsted acid sites on the surface of the catalyst, the reduction capacity and the number of unsaturated Ni atoms decreased after the addition of K. The interaction between the active Mn and the metallic Ni decreased, and the activity of the catalyst decreased. As the addition amount of added K increased, the catalyst alkali metal poisoning phenomenon became more significant. The kinetic studies showed that the activation energy increased after the addition of K, whereas the activation energy of K0.3Co0.5/Fresh catalyst decreased after Co modification. The amounts of Brønsted acid and Lewis acid sites on the surface of the K-poisoned catalyst were improved dramatically by Co modification of the Mn/Ni foam catalyst. K destroys the extremely important Brønsted acid sites that adsorb and activate NH3, reducing the performance to less than half. Additionally, NH3-TPD and in situ DRIFT analyses showed that Co, K, Mn and Ni synergistically improved the acid sites. The number of Brønsted acid sites and Lewis acid sites on the catalyst surface were greatly increased in the K0.3Co0.5/Fresh catalyst, whose reduction performance increased substantially compared with the K0.3/Fresh catalyst.
This work was supported by the National Natural Science Foundation of China (Nos. 51676001, 51376007, and U1660206), the Anhui Provincial Natural Science Foundation (No. 1608085ME104) and key projects of the Anhui province university outstanding youth talent support program (Nos. gxyqZD2016074 and gxyqZD2017038), the Funding Projects of Back-up Candidates (No. 2017H131) and the Anhui Provincial Education Foundation (No. KJ2016A090).
Compliance with ethical standards
Conflict of interest
The authors declare no competing financial interest.
- 33.Chen JY, Zhu BZ, Sun YL, Yin SL, Zhu ZC, Li JX (2017) Investigation of low-temperature selective catalytic reduction of NOx with ammonia over Mn-modified Fe2O3/AC catalysts. J Braz Chem Soc 00:1–9Google Scholar
- 55.Shan WP, Liu FD, He H, Shi XY, Zhang CB (2011) ChemInform abstract: novel cerium–tungsten mixed oxide catalyst for the selective catalytic reduction of NOx with NH3. J Cheminform 47(28):8046–8048Google Scholar
- 66.Nicosia D, Czekaj I, Kröcher O (2008) Chemical deactivation of V2O5/WO3–TiO2 SCR catalysts by additives and impurities from fuels, lubrication oils and urea solution: part II. Characterization study of the effect of alkali and alkaline earth metals. Appl Catal B Environ 77(3–4):228–236CrossRefGoogle Scholar