Using direct hot-rolling approach to obtain dual-phase weathering steel Cu–P–Cr–Ni–Mo
- 188 Downloads
A weathering steel Cu–P–Cr–Ni–Mo has been developed which exhibits special continuous cooling transformation characteristics which permit the desired dual-phase (DP) microstructure to be obtained by direct hot-rolling. Hot-rolling procedures to obtain DP microstructures have been designed based on the continuous cooling transformation diagram of weathering steel Cu–P–Cr–Ni–Mo. The results show that the microstructures of DP weathering steels Cu–P–Cr–Ni–Mo are characterized by an irregular distribution of island-shaped martensite–austenite in the matrix of polygonal ferrite grains. DP weathering steel Cu–P–Cr–Ni–Mo with favorable corrosion resistant property, weldability and mechanical properties, such as, high strain hardening exponent values, a lower ratio of yield to tensile strength, and higher strengths; and is obtained successfully by direct hot-rolling.
KeywordsFerrite Austenite Martensite Bainite Pearlite
The project supported by Natural Science Foundation-Steel and Iron Foundation of Hebei Province, P. R. China (No. E2008000843).
- 1.Erdogan M, Tekeli S (2002) Mater Des 23:597Google Scholar
- 4.Hong SC, Lee KS (2002) Mater Sci Eng A323:148Google Scholar
- 6.Zhang C, Liao B, Cai D (2007) Mater Des 28:1760Google Scholar
- 8.Greday T, Mathy H, Messien P (1979) In: Kot RA, Morris JM (eds) Structure and properties of dual-phase steels. AIME, New YorkGoogle Scholar
- 9.Coldren AP, Tither G (1978) J Metals 4:6Google Scholar