Journal of Materials Science

, Volume 44, Issue 1, pp 280–284 | Cite as

Scaling down of organic thin film transistors: short channel effects and channel length-dependent field effect mobility

  • Yi Chen
  • Ishiang Shih


Organic thin film transistors with P3HT (poly-3-hexylthiophene) as active semiconducting layer, channel lengths from 0.3 to 20 μm, and gate oxide thicknesses from 15 to 170 nm have been successfully fabricated on Si substrates. The measurement results show that the channel length over oxide thickness ratio should be large enough (i.e., the vertical electric field should be at least 10 times higher than the lateral electric filed) in order to suppress the short channel effects of transistors. The field effect mobility of long channel devices (L ≥ 5 μm) is about an order of magnitude larger than small channel devices (L from 0.3 to 2.5 μm), which could be attributed to the more severe contact resistance effects between organic materials and metal contacts for devices with smaller dimensions.


Contact Resistance Gate Voltage Channel Length Oxide Thickness Pentacene 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.


  1. 1.
    Xu Y, Berger PR (2004) J Appl Phys 95:1497CrossRefADSGoogle Scholar
  2. 2.
    Wang JZ, Zheng ZH, Sirringhaus H (2006) Appl Phys Lett 89:083513Google Scholar
  3. 3.
    Tukagoshi K, Fujimori F, Minari T, Miyadera T, Hamano T, Aoyagi Y (2007) Appl Phys Lett 91:113508CrossRefADSGoogle Scholar
  4. 4.
    Chen Y, Zhu WW, Xiao S, Shih I (2004) J Vac Sci Technol 22:768CrossRefADSGoogle Scholar
  5. 5.
    Haddock JN, Zhang X, Zheng S, Marder SR, Kippelen B (2005) Proce SPIE 11:5940Google Scholar
  6. 6.
    Chabinyc ML, Lu J-P, Street RA, Wu Y, Liu P, Ong BS (2004) J Appl Phys 96:2063CrossRefADSGoogle Scholar
  7. 7.
    Xu Y, Berger PR (2004) J Appl Phys 95:1497CrossRefADSGoogle Scholar
  8. 8.
    Wang L, Fine D, Basu D, Dodabalapur A (2007) J Appl Phys 101:054515CrossRefADSGoogle Scholar
  9. 9.
    Leufgen M, Bass U, Muck T, Borzenko T, Schmidt G, Geurts J, Wagner V, Molenkamp LW (2004) Synth Met 146:341CrossRefGoogle Scholar
  10. 10.
    Klauk H, Schmid G, Zhou L, Sheraw CD, Huang J, Nichols JA, Jackson TN (2001) In: Inter Semi Cond Dev Reas Symp Proc, p 349Google Scholar
  11. 11.
    Maeda T, Kato H, Kawakami H (2006) Appl Phys Lett 89:123508CrossRefADSGoogle Scholar
  12. 12.
    Gundlach DJ, Zhou L, Nichols JA, Jackson TN, Necliudov PV, Shur MS (2006) J Appl Phys 100:024509CrossRefADSGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2008

Authors and Affiliations

  1. 1.Department of Electrical & Computer EngineeringMcGill UniversityMontrealCanada

Personalised recommendations