, Volume 42, Issue 16, pp 7046–7048 | Cite as

An investigation on the thermodynamic stability of V6Si5

  • Chao Zhang
  • Jiong Wang
  • Yong Du
  • Wenqing Zhang
Letter

The V–Si system has been assessed by Smith [1, 2], and results were collected in recently published binary phase diagram handbook [3]. The thermodynamic optimizations for the system were also performed by Luoma [4], Rand and Saunders [5]. However, the thermodynamic stability of V6Si5 is still in question. Using the method of solid state diffusion, Hallais et al. [6] noted that formation of V6Si5 could not be achieved below 1000 °C. By means of bulk V–Si diffusion couples, Milanese et al. [7] found that there is a nucleation barrier for the formation of V6Si5 at 1150 °C. Based on the electromotive force (emf) measurement, Eremenko et al. [8] realized that the difficulty of achieving an equilibrium state of V–Si alloys containing the phase V6Si5 is indeed overdrawn. Using activity data deduced from the Knudsen cell-mass spectrometry, Storms and Myers [9] indicated the eutectoid decomposition temperature (V6Si5⇔V5Si3 + VSi2) as 1160 ± 100 K. This temperature was mistakenly regarded to be...

Keywords

Decomposition Temperature Interstitial Element Calculated Enthalpy Thermodynamic Optimization Gibbs Energy Function 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Notes

Acknowledgements

The financial supports from the National Outstanding Youth Science Foundation of China (Grant No. 50425103), Hunan Provincial Natural Science Foundation of China (Grant No. 06JJ20010) and the State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics (Grant No. SKL200606SIC) are acknowledged.

References

  1. 1.
    Smith JF (1981) Bull Alloy Phase Digarams 2:42Google Scholar
  2. 2.
    Smith JF (1985) Bull Alloy Phase Diagrams 6:266Google Scholar
  3. 3.
    Smith JF (1990) In: Massalski TB (ed) Binary alloy phase diagrams, 2nd edn, vol 3. ASM Intl, Materials Park, OhioGoogle Scholar
  4. 4.
    Luoma R In: Thermodynamic analysis of the binary systems Mo–V, Ni–V, Si–V and Ti–V. (NTIS Report TKK-V-B76, 1992) p 19Google Scholar
  5. 5.
    Rand MH, Saunders N (1998) In: Ansara I, Dinsdale AT, Rand MH (eds) COST 507: thermochemical database for light metal alloys, vol 2. European Communities, Luxembourg, p 270Google Scholar
  6. 6.
    Hallais J, Senateur JP, Fruchart R (1967) C R Acad Sci (Paris) 264:1947Google Scholar
  7. 7.
    Milanese C, Buscaglia V, Maglia F, Anselmi-Tamburini U (2002) Acta Mater 50:1393CrossRefGoogle Scholar
  8. 8.
    Eremenko VN, Lukashenko GM, Sidorko VR, Kulik OG (1976) Dopov Akad Nauk Ukr RSR Ser A 38:365Google Scholar
  9. 9.
    Storms EK, Myers CE (1985) High Temp Sci 20:87Google Scholar
  10. 10.
    Parthe E, Nowotny H, Schmid H (1955) Monatsh Chem 86:385CrossRefGoogle Scholar
  11. 11.
    Kress G, Furthmuller J (1996) Phys Rev B 54:111169Google Scholar
  12. 12.
    Kress G, Furthmuller J (1996) J Comput Mater Sci 6:15CrossRefGoogle Scholar
  13. 13.
    Perdew JP, Burke K, Ernzerhof M (1996) Phys Rev Lett 77:3865CrossRefGoogle Scholar
  14. 14.
    Monkhorst HJ, Pack JD (1972) Phys Rev B 13:5188CrossRefGoogle Scholar
  15. 15.
    Eremenko VN, Lukashenko GM, Sidorko VR (1974) Dopov Akad Nauk Ukr RSR Ser B 36:712Google Scholar
  16. 16.
    Eremenko VN, Lukashenko GM, Sidorko VR (1975) Rev Intl Hautes Temp Refract 12:237Google Scholar
  17. 17.
    O’Hare PAG, Watling K, Hope GA (1999) J Chem Thermodyn 31:385Google Scholar
  18. 18.
    Wolverton C, Yan X-Y, Vijayaraghavan R, Ozolins V (2002) Acta Mater 50:2187CrossRefGoogle Scholar
  19. 19.
    Dinsdale AT (1991) CALPHAD 15:317CrossRefGoogle Scholar
  20. 20.
    Lozova OA, Zatorska GM, Kevorkov DG, Pavlyuk VV (2001) Ukrainskii Khimicheskii Zhurnal 67:27Google Scholar

Copyright information

© Springer Science+Business Media, LLC 2007

Authors and Affiliations

  • Chao Zhang
    • 1
  • Jiong Wang
    • 1
  • Yong Du
    • 1
  • Wenqing Zhang
    • 2
  1. 1.State Key Laboratory of Powder MetallurgyCentral South UniversityChangshaP.R. China
  2. 2.State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of CeramicsChinese Academy of SciencesShanghaiP.R. China

Personalised recommendations