Abstract
In this paper, poly(ethylene terephthalate) (PET) spunbonded fibers with tensile strength of 9.67 cN/dtex and diameter of 7 μm were produced in Nordson’s MicroFil™ Spunbond System with a positive attenuator pressure. The influences of the slot width of the attenuator on the properties of PET spunbonded fibers were studied, and Fourier transformation infrared spectrophotometry (FT-IR) and Wide-angle X-ray diffraction were applied to characterize the crystalline and orientation structure of PET spunbonded fibers as well. It was found the attenuator with positive air pressure is more advantageous to spin PET spunbonded fiber and the fiber becomes finer and its’ tensile strength becomes higher with the decrease of the slot width. The air speed in the attenuator was predicted as well.
Similar content being viewed by others
References
Zhang D, Bhat G, Malkan S, Wadsworth L (1994) In: Proc Forth Annual TANDEC Conference on Nonwovens, November
Zhang D, Bhat G, Malkan S, Wadsworth L (1998) Textile Res J 68:27
Ke QF, Jin XY (2004) In: Nonwovens, Donghua University Publishing Company, Shanghai, p 223
Hajji N, Spruiell JE, Lu FM, Malkan S, Richeson GC (1991) INDA J Nonwovens Res 4:16
Patel RM, Spruiell JE (1991) Polym Eng Sci 31:730
Zieminski KF, Spruiell JE (1988) J Appl Polym Sci 35:2223
Misra S, Spruiell JE, Richeson GC (1992) INDA J Nonwovens Res 4:13
Ziabicki A (1976) In: Fundamentals of fibre formation. Wiley and Sons, New York, p 186
Guo DS, Wang WK (2001) In: Polyest Fiber Science and Engineering. China’s Textiles Publishing Company, Beijing, p 64
Zhan HY (2005) In: Fiber Chemistry and Physics. Science Publishing Company, Beijing, p 143
Jiang Y, Guo FM, Sun L et al (2000) Spectroscopy Spectral Anal 20:665
Acknowledgements
The authors thank for Yaolong Spun-bond Technology Co., Ltd for their assist to make the two samples on their production line (Nordson’s MicroFil™ Spunbond System).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, H., Jin, X., Wu, H. et al. The influences of slot width of an attenuator on the properties of PET spunbonded fibers. J Mater Sci 42, 8006–8009 (2007). https://doi.org/10.1007/s10853-007-1607-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-007-1607-9