Abstract
In a Bi2O3–B2O3–ZnO glass system, glass structure change, sintering behavior and resultant physical characteristics of the glass were examined when various amounts of Bi2O3 and ZnO mixture were added. When the total amount of Bi2O3 and ZnO was below 30 mol%, a phase separation occurred and homogeneous glass was not obtained. The fraction of four-coordinated borons (BO4) was highest when the total amount of Bi2O3 and ZnO was 50mol%. Further addition over 50 mol% induced a borate anomaly phenomenon in the glass, which resulted in the decrease in BO4 fraction. The sintering temperature and glass transition temperature decreased as the amount of Bi2O3 and ZnO increased. The thermal expansion coefficient and dielectric constant of the specimens were also examined.
Similar content being viewed by others
References
Scholze, Translated by Michael J. Lakin., Glass: Nature, Structure, and Properties, 3rd Ed., Springer-Verlag, New York, 1991, p 129
Scholze, Translated by Michael J. Lakin., Glass: Nature, Structure, and Properties, 3rd Ed., Springer-Verlag, New York, 1991, p 137
Warren BE, Biscoe Z (1938) J Am Ceram Soc 21:278
Shibata M, Sanchez C, Patel H, Feller S, Stark J, Sumcad G, Kasper J (1986) J Non-Cryst Solids 85:29
Chong BCL, Choo SH, Feller S, Teoh B, Mathews O, Khaw EJ, Feil D, Chong KH, Affatigato M, Bain D, Hazen K, Farooqui K (1989) J Non-Cryst Solids 109:105
Bray PJ, O’ Keefe JG (1963) Phys Chem Glasses 4:37
Cha DJ (1989) Thesis, Department of Physics Graduate School, Chonnam National University, Gwangju, Korea
Bray PJ, Geissberger AE, Bucholts F, Harris IA (1982) J Non-Cryst Solids 52:45
Bray PJ, Leventhal M, Hooper HO (1963) Phys Chem Glasses 4:47
Hayashi A, Nakai M, Tatsumisago M, Minami T, Himei Y, Miura Y, Katada M (2002) J Non-Cryst Solids 306:227
Mulkern RV, Chung SJ, Bray PJ, Chryssikos GD, Turcotte DE, Risen WM (1986) J Non-Cryst Solids 85:69
Harris IA, Bray PJ (1984) Phys Chem Glasses 25:69
Lee CH, Yoo JR, Jung KW, Choi SC (2001) J Kor Ceram Soc 38:628
Scholze, Translated by Michael J. Lakin., Glass: Nature, Structure, and Properties, 3rd Ed., Springer-Verlag, New York, 1991, p. 162
Zhao P, Kroeker S, Stebbins JF (2000) J Non-Cryst Solids 276:122
Stebbins JF, Zhao P, Kroeker S (2000) Solid State NMR 16:9
Wang S, Stebbins JF (1998) J Non-Cryst Solids 231:286
Milberg ME, O’Keefe JG, Verhelst RA, Hooper HO (1972) J Chem Phys 13:79
Kroeker S, Stebbins JF (2001) Inorg Chem 40:6239
Boulos EN, Smith JW, Moynihan CT (1983) Glastech Ber 56:509
Scholze, Translated by Michael J. Lakin., Glass: Nature, Structure, and Properties, 3rd Ed., Springer-Verlag, New York, 1991, p 318
Dimitrov V, Sakka S (1996) J Appl Phys 79:1736
Scholze, Translated by Michael J. Lakin., Glass: Nature, Structure, and Properties, 3rd Ed., Springer-Verlag, New York, 1991, p 189
Acknowledgement
This work was supported by the National Research Laboratory grant from the Ministry of Science and Technology (MOST) and Korea Science and Engineering Foundation (KOSEF).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kim, BS., Lim, ES., Lee, JH. et al. Effect of structure change on thermal and dielectric characteristics in low-temperature firing Bi2O3–B2O3–ZnO glasses. J Mater Sci 42, 4260–4264 (2007). https://doi.org/10.1007/s10853-006-0638-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-0638-y