Abstract
A low alloy steel containing 0.09% C was thermomechanically processed at the intercritical annealing temperature of 790 °C to produce dual-phase microstructure from 50% of austenite. After applying different rolling reductions at this temperature, the specimens were quenched in boiling water to promote the growth of epitaxial ferrite. Warm rolling at 790 °C decreased the hardenability of austenite due to increased in interfacial area of austenite and ferrite. Tensile strength was improved by increasing the rolling reductions both in longitudinal and transverse directions without any significant loss in ductility attributed to the presence of epitaxial ferrite. Microvoid formation in the necked region and their percentage area fraction was measured. The correlation between the area fractions of microvoids formation with strain in the necked region ultimately defined the mode of failure.
Similar content being viewed by others
References
Dinda S, Di Cello JA, Kasper AS (1975) In: Microalloyin 75. Union Carbide, Washington, p 33
Rashid MS (1979) In: Davenport AT (ed) Formable HSLA and dual phase steels. AIME, New York, NY, pp 1–24
Owen WS (1980) Met Technol 7:1
Bittence JC (1978) Mater Eng 87(5):39
Sarwar M, Priestner R (1996) J Mater Sci 31:2091
Ahmad E, Priestner R (1998) J Mater Eng Perform 7(6):772
Ahmad E, Manzoor T, Liaqat Ali K, Akhter JI (2000) J Mater Eng Perform 9(3):306
Sin S, Pugh M (2002) Mater Sci Eng 335(1–2):298
Erdogen M, Tekeli S (2002) Mater Des 23:597
Lawson R, Matlock DK, Krauss G (1980) Metallography 13:71
Speich GR, Miller RI (1979) In: Kot RA, Morris JW (eds), Structures and properties of dual phase steels. TMS-AIME, Warrendale, PA pp 145
Ajmal M, Priestner R (1988) In: Tamura I (ed) Int. Conf. Phys. Met. T. M. P. Steel and other Metal. ISIJ, pp 642–691
Priestner R (1987). Conf. Proc., Phase Transformation87. Institute of Metals, Cambridge
Tanaka T (1985) Intern Metal Rev 4:185
Steinbrunner DL, Matlock DK, Krauss G (1988) Met Trans 19(A):579
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ahmad, E., Sarwar, M., Manzoor, T. et al. Effect of rolling and epitaxial ferrite on the tensile properties of low alloy steel. J Mater Sci 41, 5417–5423 (2006). https://doi.org/10.1007/s10853-006-0266-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-0266-6