Abstract
Metal–insulator–metal (MIM) capacitors with plasma enhanced chemical vapor deposited (PECVD) nitride exhibit trap-induced dispersive behavior and electrical hysteresis, which lead to degradation in capacitor linearity at low frequencies. The dominant defect was suggested to be silicon dangling bonds originated from nitrogen deficiency. Previous methods to eliminate the dispersive behavior and electrical hysteresis include use of oxide–nitride–oxide (ONO) stacks and/or plasma pre-treatment of silicon substrate before nitride deposition [Van Huylenbroeck S, Decoutere S, Venegas R, Jenei S, Winderickx G (2002) IEEE Electron Device Lett 23:191; Lau WS (1990) Jpn J Appl Phys 29:L690]. In this study, the plasma post-treatment method was employed; MIM capacitors with PECVD oxide and nitride were treated with N2O and SiH4/NH3 plasma, respectively, after deposition of the dielectric layer. No apparent change in film microstructure is observed after plasma treatment. Plasma post-treatment is effective in eliminating the electrical hysteresis shift of the nitride capacitors. Fourier transform infrared (FTIR) absorption spectra suggest an increase of the Si–H bond after SiH4/NH3 plasma bombardment of the nitride films. Auger depth profiling indicates a slight increase of nitrogen to silicon ratio after plasma treatment. The increase of the Si–H bonds as well as the raise of nitrogen to silicon ratio are two possible causes for the elimination of the hysteresis shift of the plasma-treated nitride capacitors. The time dependent dielectric breakdown testing indicates a decrease in both the leakage current and the lifetime of the MIM capacitors treated with plasma. Possible dielectric degradation mechanism is explored.
Similar content being viewed by others
References
Chang TY, Chen HW, Lei TF, Chao TS (2002) IEEE Trans Electron Devices 29:2163
Chang TY, Lei TF, Chao TS, Wen HC, Chen HW (2002) IEEE Electron Device Lett 23:389
Lim BC, Choi YJ, Choi JH, Jang J (2000) IEEE Trans Electron Devices 47:367
Chen CT, Chiou BS (2004) J Mater Sci Mater Electron 15:139
Van Huylenbroeck S, Decoutere S, Venegas R, Jenei S, Winderickx G (2002) IEEE Electron Device Lett 23:191
Lau WS (1990) Jpn J Appl Phys 29:L690
Kar-Roy A, Hu C, Racanelli M, Compton CA, Kempf P, Jolly G, Sherman PN, Zheng J, Zhang Z, Yin A (1999) in Proceedings of the 2nd IEEE International Interconnect Technology Conference, San Francisco, USA, May 1999 (IEEE, New York, USA) p 245
Babcock JA, Balster SG, Pinto A, Dirnecker C, Steinmann P, Jumpertz R, El-Kareh B, (2001) IEEE Electron Device Lett 22:230
Kaluri SR, Hess DW (1998) J Electromchem Soc 145:662
Van Delden MHWM, Van Der Wel PJ (2003) in Proceedings of the 41st International Reliability Physics Symp. Dallas, USA, March 2003 (IEEE, New York, USA) p. 293
Mcpherson JW, Kim J, Shanware A, Mogul H, Rodriguez J (2003) IEEE Trans Electron Device 50:1771
Acknowledgements
This work is sponsored by National Science Council, Taiwan, under the contract number NSC 93-2216-E-009-023.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ho, CC., Chiou, BS. Effect of plasma treatment on the microstructure and electrical properties of MIM capacitors with PECVD silicon oxide and silicon nitride. J Mater Sci 42, 941–947 (2007). https://doi.org/10.1007/s10853-006-0012-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-0012-0