Abstract
The plastic collapse strength, energy absorption and elastic modulus of a closed cell aluminum foam are studied in relation to cell structures. The density, node size and the cell wall thickness of the aluminum foams decrease with increasing cell size. The failure of the foam cells under compressive load progresses successively from the top or/and bottom to the mid-layer of the compression specimens, and no initial rupture of the foam cells is observed in the mid-height of the foam samples. When foam density increases from 0.11 to 0.22 g/cm 3, the plastic collapse strength rises from 0.20 to 1.29 MPa, while the elastic modulus of the closed cell aluminum foam increases from 0.70 to 1.17 GPa. In contrast, the energy absorption of the foams decreases rapidly with increasing cell size. When cell size increases from 4.7 to 10.1 mm, the energy absorption drops from over unity to 0.3 J/cm 3. The normalized Yong’s modulus of the closed cell aluminum foam is E*/Es = 0.208 (ρ*/ρs), while the normalized strength of the foams, σ */σs is expressed by σ */σs = c ⋅ ρ */ρs where c is a density-dependent parameter. Furthermore, the plastic collapse strength and energy absorption ability of the closed cell aluminum foams are significantly improved by reducing cell size of the aluminum foams having the same density.
Similar content being viewed by others
References
T. MIYOSHI, M. ITOH, S. AKIYAMA and A. KITAHARA, Adv. Engng. Mater. 2 (4) (2000) 179.
W. J. CANTWELL, P. COMPSTON and G. REYES, J. Mater. Sci. Lett. 19(24) (2000) 2205.
WEIGANG, CHEN, TOMASZ and WIERZBICKI, Thin-Walled Struct. 39(4) (2001) 287.
A. -F. BASTAWROS, H. BART-SMITH and A. G. EVANS, J. Mech. Phys. Solids. 48(2) (2000) 301.
L. D. KENNY, Mater. Sci. Forum. 217–222(3) (1996) 1883.
IIJOON JIN, LORNE D. KENNY and HARRY SANG, Method of Producing Light Weight Foamed Metal, US Patent 4973358, 1990.
P. H. THORNTON and C. K. H. DHARAN, Mater. Sci. Eng. 18(1) (1975) 97.
A. E. SIMONE and L. J. GIBSON, Acta Mater. 46 (1998) 2139.
WANG DEQING and SHI ZIYUAN, Mater. Sci. Engng. A 361 (1–2) (2003) 45.
KATHRYN A. DANNEMANN and JAMES LANKFORD JR, Mater. Sci. Engng. A293 (1–2) (2000) 157.
E. ANDREWS, W. SANDERS and L. J. GIBSON, Mater. Sci. Engng. A270(2) (1999) 113.
S. SANTOSA and T. WIERZBICKI, J. Mech. Phys. Solids 46(4) (1998) 645.
I. W. HALL, M. GUDEN and C.-J. YU, Scripta Materialia 43(6) (2000) 515.
A. PAUL and U. RAMAMURTY, Mater. Sci. Engng. A281(1–2) (2000) 1.
T. MUKAI, H. KANAHASHI, T. MIYOSHI, M. MABUCHI, T. G. NIEH and K. HIGASHI, Scripta Materialia 40(8) (1999) 921.
A.-F. BASTAWROS, H. BART-SMITH and A. G. EVANS, J. Mech. Phys. Solids 48(2) (2000) 301.
A. E. SIMONE and L. J. GIBSON, Acta Materialia 46(9) (1998) 3109.
KATHRYN A. DANNEMANN and JAMES LANKFORD JR., Mater. Sci. Engng. A293 (2000) 157.
A. M. KRAYNIK, M. K. NEILSEN, D. A. REINELT and W. E. WARREN, Foam Micromechanics, Foams and Emulsions, in Proceedings of the NATO Advanced Study Institute on ‘Foams, Emulsions and Cellular Materials, Cargese, Corsica, 12–24 May, 1997, edited by J. F. Sadoc and N. Rivier (Kluwer Academic Publishers, Dordrecht, 1999) p. 259.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Deqing, W., Weiwei, X., Xiangjun, M. et al. Cell structure and compressive behavior of an aluminum foam. J Mater Sci 40, 3475–3480 (2005). https://doi.org/10.1007/s10853-005-2852-4
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-2852-4