Low-melting non-frit glazes for construction and artistic ceramics

  • N. F. Zhernovaya
  • Yu. V. Burchakova
  • F. E. Zhernovoi
  • E. V. Miroshnikov
Coatings

Low-melting non-frit glazes with firing temperature 950 – 1000°C were obtained in the system datolite–perlite–cullet. The conditions under which high-quality coatings are formed were determined: pre-firing datolite and perlite, B2O3/Al2O3 > 2.5 in the glaze and slip ultradispersity.

Key words

glaze low-alkali borosilicate glass batch wet-milling activation melting efficiency 

References

  1. 1.
    A. P. Zubekhin, N. V. Tabarina, N. D. Yatsenko, and V. P. Rat’-kova, “A resource-saving technology for obtaining facing tile,” Steklo Keram., No. 6, 3–5 (1996); A. P. Zubekhin, N. V. Tabarina, N. D. Yatsenko, and V. P. Rat’kova, “A resource-saving technology for fabricating tile,” Glass Ceram., 53(6), 161–163 (1996).Google Scholar
  2. 2.
    A. M. Salakhov, O. V. Spirina, V. I. Remiznikova, and V. G. Khozin, “Low-melting glaze for construction ceramics,” Steklo Keram., No. 5, 19–20 (2001); A. M. Salakhov, O. V. Spirina, V. I. Remiznikova and V. G. Khozin, “Low-melting glaze for structural ceramics,” Glass Ceram., 58(5–6), 174–175 (2001).Google Scholar
  3. 3.
    A. G. Tkachev, O. N. Tkacheva, and I. S. Solov’eva, “Production of low-melting glazes without frit melting,” Steklo Keram., No. 11, 378–379 (2002); A. G. Tkachev, O. N. Tkacheva, and I. S. Solov’eva, “Production of low-melting Ggazes without frit melting,” Glass Ceram., 59(11–12), 378–379 (2002).Google Scholar
  4. 4.
    N. N. Ermolenko, “Chemical structure and some properties of oxide glasses,” in: Physical-Chemical Principles and Scientific-Technological Progress in the Technology of Glass and Glass Crystal Materials Using Secondary Raw Materials [in Russian], MISI – BTISM, Moscow (1987), pp. 77–88.Google Scholar
  5. 5.
    A. A. Appen, Chemistry of Glass [in Russian], Khimiya, Leningrad (1974).Google Scholar

Copyright information

© Springer Science+Business Media New York 2013

Authors and Affiliations

  • N. F. Zhernovaya
    • 1
  • Yu. V. Burchakova
    • 1
  • F. E. Zhernovoi
    • 1
  • E. V. Miroshnikov
    • 1
  1. 1.V. G. Shukhov Belgorod State Technological UniversityBelgorodRussia

Personalised recommendations