A novel boron–nitrogen intumescent flame retardant coating on cotton with improved washing durability

  • Shuk Ying Chan
  • Liping Si
  • Ka I. Lee
  • Pui Fai Ng
  • Lei Chen
  • Bin Yu
  • Yuan Hu
  • Richard K. K. Yuen
  • John H. Xin
  • Bin Fei
Original Paper
  • 653 Downloads

Abstract

A series of boron–nitrogen polymers (PEIPAs) were synthesized to provide a green alternative for flame retardant finishing on cotton fabrics. An organic boron compound, phenylboronic acid (PA) was successfully bonded to the branched polyethylenimine, which was confirmed by 1H NMR and FTIR analysis. Thermogravimetric analysis showed that the polymer with molar ratio 1:1 of ethylenimine:PA (PEIPA 1:1), presented the optimal thermal-oxidative stability. PEIPA 1:1 was easily applied on cotton fabrics through a simple dipping method with high uptake in acetone medium. The fabric with 33.8 wt% add-on got self-extinguishing ability. SEM analysis on the char morphology of the treated fabrics revealed the fire protection by the coating through intumescent flame retardant mechanism. TGIR analysis showed the coated fabric has significant reduction in the flammable volatiles production. Further improvement of the coating washing durability was achieved by a novel formaldehyde-free cross-linking treatment. The new washing stable coating achieved LOI values 29.6 and 23.2% before and after repeated launderings respectively with 30 wt% add-on. Cone calorimetry analysis showed that the total heat releases of PEIPA 1:1 treated sample and cross-linked sample (PEIPA 3:1/NeoFR treated) were decreased by 30.3 and 45.5% respectively. Smoke analysis revealed that the treated fabrics have significant decrease in CO2/CO ratio, indicating an effective flame inhibition in gas phase. The novel coatings, simple to synthesize and easy to apply with low waste, are suitable alternative to toxic halogenated flame retardants for cellulosic products.

Keywords

Flame retardant Cotton Boronic acid Intumescent char Volatiles reduction Durability 

Notes

Acknowledgments

We thank the funding support of GRF Project 15208015 and PolyU G-UA1Z.

Supplementary material

Supplementary material 1 (MP4 37544 kb)

Supplementary material 2 (MP4 7581 kb)

References

  1. Abdalla MO, Ludwick A, Mitchell T (2003) Boron-modified phenolic resins for high performance applications. Polymer 44:7353–7359.  https://doi.org/10.1016/j.polymer.2003.09.019 CrossRefGoogle Scholar
  2. Alongi J, Malucelli G (2015) Cotton flame retardancy: state of the art and future perspectives. RSC Adv 5:24239–24263.  https://doi.org/10.1039/C5RA01176K CrossRefGoogle Scholar
  3. Alongi J, Carletto RA, Di Blasio A, Cuttica F, Carosio F, Bosco F, Malucelli G (2013) Intrinsic intumescent-like flame retardant properties of DNA-treated cotton fabrics. Carbohydr Polym 96:296–304.  https://doi.org/10.1016/j.carbpol.2013.03.066 CrossRefGoogle Scholar
  4. Alongi J, Carosio F, Malucelli G (2014) Current emerging techniques to impart flame retardancy to fabrics: an overview. Polym Degrad Stab 106:138–149.  https://doi.org/10.1016/j.polymdegradstab.2013.07.012 CrossRefGoogle Scholar
  5. Alongi J, Han Z, Bourbigot S (2015) Intumescence: tradition versus novelty. A comprehensive review. Prog Polym Sci 51:28–73.  https://doi.org/10.1016/j.progpolymsci.2015.04.010 CrossRefGoogle Scholar
  6. Carosio F, Di Blasio A, Alongi J, Malucelli G (2013) Green DNA-based flame retardant coatings assembled through layer by layer. Polymer 54:5148–5153.  https://doi.org/10.1016/j.polymer.2013.07.029 CrossRefGoogle Scholar
  7. Chen XL, Huo LL, Jiao CM, Li SX (2013) TG-FTIR characterization of volatile compounds from flame retardant polyurethane foams materials. J Anal Appl Pyrol 100:186–191.  https://doi.org/10.1016/j.jaap.2012.12.017 CrossRefGoogle Scholar
  8. Chen S, Li X, Li Y, Sun J (2015) Intumescent flame-retardant and self-healing superhydrophobic coatings on cotton fabric. ACS Nano 9:4070–4076.  https://doi.org/10.1021/acsnano.5b00121 CrossRefGoogle Scholar
  9. Chen X, Ma C, Jiao C (2016) Enhancement of flame-retardant performance of thermoplastic polyurethane with the incorporation of aluminum hypophosphite and iron-graphene. Polym Degrad Stab 129:275–285.  https://doi.org/10.1016/j.polymdegradstab.2016.04.017 CrossRefGoogle Scholar
  10. Demirbas A (2009) Pyrolysis mechanisms of biomass materials. Energy Sources A 31:1186–1193.  https://doi.org/10.1080/15567030801952268 CrossRefGoogle Scholar
  11. Fei B, Yang Z, Shao S, Wan S, Xin JH (2010) Enhanced fluorescence and thermal sensitivity of polyethylenimine modified by Michael addition. Polymer 51:1845–1852.  https://doi.org/10.1016/j.polymer.2010.02.017 CrossRefGoogle Scholar
  12. Haile M, Leistner M, Sarwar O, Toler CM, Henderson R, Grunlan JC (2016) A wash-durable polyelectrolyte complex that extinguishes flames on polyester-cotton fabric. RSC Adv 6:33998–34004.  https://doi.org/10.1039/C6RA03637F CrossRefGoogle Scholar
  13. Haynes HJG (2016) Fire loss in the United States during 2015. National Fire Protection AssociationGoogle Scholar
  14. Horacek H, Grabner R (1996) Advantages of flame retardants based on nitrogen compounds. Polym Degrad Stab 54:205–215.  https://doi.org/10.1016/S0141-3910(96)00045-6 CrossRefGoogle Scholar
  15. Horrocks AR, Price D (2001) Fire retardant materials. Woodhead Pub., Boca RatonCrossRefGoogle Scholar
  16. Jia Y, Hu Y, Zheng D, Zhang G, Zhang F, Liang Y (2017) Synthesis and evaluation of an efficient, durable, and environmentally friendly flame retardant for cotton. Cellulose 24:1159–1170.  https://doi.org/10.1007/s10570-016-1163-z CrossRefGoogle Scholar
  17. Jimenez M, Lesaffre N, Bellayer S, Dupretz R, Vandenbossche M, Duquesne S, Bourbigot S (2015) Novel flame retardant flexible polyurethane foam: plasma induced graft-polymerization of phosphonates. RSC Adv 5:63853–63865.  https://doi.org/10.1039/c5ra08289g CrossRefGoogle Scholar
  18. Kilinc FS, Textile Institute (Manchester England) (2013) Handbook of fire resistant textiles. Woodhead Publishing series in textiles no 140. Oxford, PhiladelphiaGoogle Scholar
  19. Lambert JB (2011) Organic structural spectroscopy, 2nd edn. Prentice Hall/Pearson, Upper Saddle RiverGoogle Scholar
  20. LeVan SL, Tran HC (1990) The role of boron in flame-retardant treatments. In: Proceedings of the first international conference on wood protection with diffusible preservatives, vol 47355, pp 39–41Google Scholar
  21. Lindholm J, Brink A, Hupa M (2009) Cone calorimeter—a tool for measuring heat release rate. Åbo Akademi Process Chemistry Centre, FinlandGoogle Scholar
  22. Liu W, Chen L, Wang Y-Z (2012) A novel phosphorus-containing flame retardant for the formaldehyde-free treatment of cotton fabrics. Polym Degrad Stab 97:2487–2491.  https://doi.org/10.1016/j.polymdegradstab.2012.07.016 CrossRefGoogle Scholar
  23. Lu SY, Hamerton I (2002) Recent developments in the chemistry of halogen-free flame retardant polymers. Prog Polym Sci 27:1661–1712.  https://doi.org/10.1016/S0079-6700(02)00018-7 CrossRefGoogle Scholar
  24. Lv Q, Huang J-Q, Chen M-J, Zhao J, Tan Y, Chen L, Wang Y-Z (2013) An effective flame retardant and smoke suppression oligomer for epoxy resin. Ind Eng Chem Res 52:9397–9404.  https://doi.org/10.1021/ie400911r CrossRefGoogle Scholar
  25. Martin C, Ronda JC, Cadiz V (2006) Boron-containing novolac resins as flame retardant materials. Polym Degrad Stab 91:747–754.  https://doi.org/10.1016/j.polymdegradstab.2005.05.025 CrossRefGoogle Scholar
  26. Martín C, Hunt BJ, Ebdon JR, Ronda JC, Cádiz V (2006) Synthesis, crosslinking and flame retardance of polymers of boron-containing difunctional styrenic monomers. React Funct Polym 66:1047–1054.  https://doi.org/10.1016/j.reactfunctpolym.2006.01.013 CrossRefGoogle Scholar
  27. Mosurkal R, Kirby R, Muller WS, Soares JW, Kumar J (2011) Simple green synthesis of polyborosiloxanes as environmentally-safe, non-halogenated flame retardant polymers. Green Chem 13:659–665.  https://doi.org/10.1039/c0gc00376j CrossRefGoogle Scholar
  28. Mu XW, Yuan BH, Hu WZ, Qiu SL, Song L, Hu Y (2015) Flame retardant and anti-dripping properties of polylactic acid/poly(bis(phenoxy)phosphazene)/expandable graphite composite and its flame retardant mechanism. RSC Adv 5:76068–76078.  https://doi.org/10.1039/c5ra12701g CrossRefGoogle Scholar
  29. Naval Engineering Standard 713 (1985), Issue 3, Determination of the toxicity index of the products of combustion from small specimens of materialsGoogle Scholar
  30. Nedel’ko VV, Korsunskii BL, Dubovitskii FI, Gromova GL (1975) The thermal degradation of branched polyethylenimine. Polym Sci USSR 17:1697–1703.  https://doi.org/10.1016/0032-3950(75)90172-0 CrossRefGoogle Scholar
  31. Pan N, Sun G (2011) Functional textiles for improved performance, protection and health. Woodhead Publishing, OxfordCrossRefGoogle Scholar
  32. Pan Y, Zhan J, Pan HF, Wang W, Ge H, Song L, Hu Y (2015) A novel and effective method to fabricate flame retardant and smoke suppressed flexible polyurethane foam. RSC Adv 5:67878–67885.  https://doi.org/10.1039/c5ra09553k CrossRefGoogle Scholar
  33. Papaspyrides CD, Kiliaris P (2014) Chapter 1—Polymers on fires. Polymer green flame retardants. Elsevier, Amsterdam, pp 1–43Google Scholar
  34. Peng Q, Chen F, Zhong Z, Zhuo R (2010) Enhanced gene transfection capability of polyethylenimine by incorporating boronic acid groups. Chem Commun 46:5888–5890.  https://doi.org/10.1039/C0CC00877J CrossRefGoogle Scholar
  35. Romanos J et al (2013) Infrared study of boron–carbon chemical bonds in boron-doped activated carbon. Carbon 54:208–214.  https://doi.org/10.1016/j.carbon.2012.11.031 CrossRefGoogle Scholar
  36. Schartel B (2010) Phosphorus-based flame retardancy mechanisms—old hat or a starting point for future development? Materials 3:4710–4745.  https://doi.org/10.3390/ma3104710 CrossRefGoogle Scholar
  37. Shen KK (2014) Chapter 11—Review of recent advances on the use of boron-based flame retardants. In: Polymer Green Flame Retardants. Elsevier, Amsterdam, pp 367–388.  https://doi.org/10.1016/B978-0-444-53808-6.00011-1
  38. Stuart B (2004) Infrared spectroscopy: fundamentals and applications. Wiley, ChichesterCrossRefGoogle Scholar
  39. Tai QL, Song L, Feng H, Tao YJ, Yuen RKK, Hu Y (2012) Investigation of a combination of novel polyphosphoramide and boron-containing compounds on the thermal and flame-retardant properties of polystyrene. J Polym Res 19:9763.  https://doi.org/10.1007/s10965-011-9763-7 CrossRefGoogle Scholar
  40. Wang DC, Chang GW, Chen Y (2008) Preparation and thermal stability of boron-containing phenolic resin/clay nanocomposites. Polym Degrad Stab 93:125–133.  https://doi.org/10.1016/j.polymdegradstab.2007.10.021 CrossRefGoogle Scholar
  41. Wang W et al (2016) Fabrication of LDH nanosheets on beta-FeOOH rods and applications for improving the fire safety of epoxy resin. Compos A Appl Sci Manuf 80:259–269.  https://doi.org/10.1016/j.compositesa.2015.10.031 CrossRefGoogle Scholar
  42. Wiacek M, Wesolek D, Rojewski S, Bujnowicz K, Schab-Balcerzak E (2015) Boronated (co)polystyrene: monomer reactivity ratios, thermal behavior and flammability. Polym Adv Technol 26:49–56.  https://doi.org/10.1002/pat.3418 CrossRefGoogle Scholar
  43. Wilkie CA, Morgan AB (2010) Fire retardancy of polymeric materials, 2nd edn. CRC Press, Boca RatonGoogle Scholar
  44. Xie KL, Gao AQ, Zhang YS (2013) Flame retardant finishing of cotton fabric based on synergistic compounds containing boron and nitrogen. Carbohydr Polym 98:706–710.  https://doi.org/10.1016/j.carbpol.2013.06.014 CrossRefGoogle Scholar
  45. Xu PJ, Jing XL (2010) Pyrolysis of hyperbranched polyborate modified phenolic resin. Polym Eng Sci 50:1382–1388.  https://doi.org/10.1002/pen.21675 CrossRefGoogle Scholar
  46. Yang Z, Fei B, Wang X, Xin JH (2012a) A novel halogen-free and formaldehyde-free flame retardant for cotton fabrics. Fire Mater 36:31–39.  https://doi.org/10.1002/fam.1082 CrossRefGoogle Scholar
  47. Yang ZY, Wang XW, Lei DP, Fei B, Xin JH (2012b) A durable flame retardant for cellulosic fabrics. Polym Degrad Stab 97:2467–2472.  https://doi.org/10.1016/j.polymdegradstab.2012.05.023 CrossRefGoogle Scholar
  48. Zhang R, Xiao X, Tai Q, Huang H, Hu Y (2012) Modification of lignin and its application as char agent in intumescent flame-retardant poly(lactic acid). Polym Eng Sci 52:2620–2626.  https://doi.org/10.1002/pen.23214 CrossRefGoogle Scholar
  49. Zhou XD, Chen K, Yi H (2014) Synthesis and application of a formaldehyde-free flame retardant for bamboo viscose fabric. Text Res J 84:1515–1527.  https://doi.org/10.1177/0040517514525877 CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media B.V., part of Springer Nature 2017

Authors and Affiliations

  1. 1.Institute of Textiles and ClothingThe Hong Kong Polytechnic UniversityKowloonChina
  2. 2.State Key Lab of Fire ScienceUniversity of Science and Technology of ChinaHefeiChina
  3. 3.Department of Architecture and Civil EngineeringCity University of Hong KongKowloonChina

Personalised recommendations