CO2–CO capture and kinetic analyses of sodium cobaltate under various partial pressures

Abstract

Sodium cobaltate and some Fe-containing samples were evaluated on the CO, CO2 and CO–CO2 sorption at high temperatures and low CO2 partial pressures, in the presence and absence of oxygen. Initially, CO2 chemisorption on these samples was analyzed using different PCO2. Results indicated that all the samples were able to chemisorb CO2 (if PCO2 ≥ 0.2), where Fe-containing NaCoO2 samples clearly showed higher CO2 chemisorption efficiencies than pristine NaCoO2. These results were explained by the partial iron reduction and the consequent oxygen release. When oxygen was added the chemisorption process was improved as a result of an iron reduction–oxidation mechanism. These results were confirmed kinetically by the Jander-Zhang and Eyring models. The temperature for complete CO catalytic conversion was shifted to lower temperatures as a function of iron content. Finally, simultaneous CO2 and CO sorption as well as catalytic experiments were tested (in absence or presence of O2). These results showed that CO was mainly oxidized and chemically captured, over the CO2 direct capture, in oxygen absence and presence. Iron is able to release and capture oxygen by reduction–oxidation effect and facilitates oxygen dissociation for the carbonation process, through the Mars van Krevelen reaction mechanism.

This is a preview of subscription content, access via your institution.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11

References

  1. Alcántar-Vázquez, B., Duan, Y., Pfeiffer, H.: CO oxidation and subsequent CO2 chemisorption on alkaline zirconates: Li2ZrO3 and Na2ZrO3. Ind. Eng. Chem. Res. 55, 9880–9886 (2016)

    Article  CAS  Google Scholar 

  2. Bhatta, L.K.G., Subramanyam, S., Chengala, M.D., Olivera, S., Venkatesh, K.: Progress in hydrotalcite like compounds and metal-based oxides for CO2 capture: a review. J. Cleaner Prod. 103, 171–196 (2015)

    Article  CAS  Google Scholar 

  3. Chowdhury, M.B.I., Quddus, M.R., de Lasa, H.I.: CO2 capture with a novel solid fluidizable sorbent: thermodynamics and temperature programmed carbonation-decarbonation. Chem. Eng. J. 232, 139–148 (2013)

    Article  CAS  Google Scholar 

  4. Dou, B., Wang, C., Song, Y., Chen, H., Jiang, B., Yang, M., Xu, Y.: Solid sorbents for in situ CO2 removal during sorption-enhanced steam reforming process: a review. Renew. Sustain. Energy Rev. 53, 536–546 (2016)

    Article  CAS  Google Scholar 

  5. Izquierdo, M.T., Saleh, A., Sánchez-Fernández, E., Maroto-Valer, M.M., García, S.: High-temperature CO2 capture by Li4SiO4 sorbents: effect of CO2 concentration and cyclic performance under representative conditions. Ind. Eng. Chem. Res. 57, 13802–13810 (2018a)

    Article  CAS  Google Scholar 

  6. Izquierdo, M.T., Turan, A., García, S., Maroto-Valer, M.M.: Optimization of Li4SiO4 synthesis conditions by solid state method for maximum CO2 capture at high temperature. J. Mat. Chem. A 6, 3249–3257 (2018b)

    Article  CAS  Google Scholar 

  7. Kaniwa, S., Yoshino, M., Niwa, E., Yashima, M., Hashimoto, T.: Analysis of chemical reaction between Li4SiO4 and CO2 by thermogravimetry under various CO2 partial pressures—clarification of CO2 partial pressure and temperature region of CO2 absorption or desorption. Mater. Res. Bull. 94, 134–139 (2017)

    Article  CAS  Google Scholar 

  8. Kaniwa, S., Yoshino, M., Niwa, E., Hashimoto, T.: Evaluation of reaction kinetics of CO2 and Li4SiO4 by thermogravimetry under various CO2 partial pressures. Mater. Res. Bull. 97, 56–60 (2018)

    Article  CAS  Google Scholar 

  9. Kenarsari, S.D., Yang, D., Jiang, G., Zhang, S., Wang, J., Russell, A.G., Wei, Q., Fan, M.: Review of recent advances in carbon dioxide separation and capture. RSC Adv. 3, 22739–22773 (2013)

    Article  CAS  Google Scholar 

  10. Lara-García, H.A., Vera, E., Mendoza-Nieto, J.A., Gomez-García, J.F., Duan, Y., Pfeiffer, H.: Bifunctional application of lithium ferrites (Li5FeO4 and LiFeO2) during carbon monoxide (CO) oxidation and chemisorption processes. A catalytic, thermogravimetric and theoretical analysis. Chem. Eng. J. 327, 783–791 (2017)

    Article  CAS  Google Scholar 

  11. Lara-García, H.A., Pfeiffer, H.: High and efficient Li2CuO2–CO2 chemisorption using different partial pressures and enhancement produced by the oxygen addition. Chem. Eng. J. 313, 1288–1294 (2017)

    Article  CAS  Google Scholar 

  12. Mars, P., van Krevelen, D.W.: Oxidations carried out by means of vanadium oxide catalysts. Chem. Eng. Sci. 3, 41–59 (1954)

    Article  CAS  Google Scholar 

  13. Ochoa-Fernández, E., Zhao, T., Rønning, M., Chen, D.: Effects of steam addition on the properties of high temperature ceramic CO2 acceptors. J. Environ. Eng. 135, 397–403 (2009)

    Article  CAS  Google Scholar 

  14. Oh-Ishi, K., Matsukura, Y., Okumura, T., Matsunaga, Y., Kobayashi, R.: Fundamental research on gas–solid reaction between CO2 and Li2CuO2 linking application for solid CO2 absorbent. J. Solid State Chem. 211, 162–169 (2014)

    Article  CAS  Google Scholar 

  15. Regufe, M.J., Ferreira, A.F.P., Loureiro, J.M., Shi, Y., Rodrigues, A., Ribeiro, A.M.: New hybrid composite honeycomb monolith with 13X zeolite and activated carbon for CO2 capture. Ads. 24, 249–265 (2018)

    Article  CAS  Google Scholar 

  16. Sánchez-Camacho, P., Gómez-García, J.F., Pfeiffer, H.: Thermokinetic and conductivity analyzes of the high CO2 chemisorption on Li5AlO4 and alkaline carbonate impregnated Li5AlO4 samples: effects produced by the use of CO2 partial pressures and oxygen addition. J. Energy Chem. 26, 919–926 (2017)

    Article  Google Scholar 

  17. Stonor, M.R., Ferguson, T.E., Chen, J.G., Park, A.H.A.: Biomass conversion to H2 with substantially suppressed CO2 formation in the presence of group I & group II hydroxides and a Ni/ZrO2 catalyst. Energy Environ. Sci. 8, 1702–1706 (2015)

    Article  CAS  Google Scholar 

  18. Vera, E., Alcantar-Vazquez, B., Pfeiffer, H.: CO2 chemisorption and evidence of the CO oxidation–chemisorption mechanisms on sodium cobaltate. Chem. Eng. J. 271, 106–113 (2015)

    Article  CAS  Google Scholar 

  19. Vera, E., Alcántar-Vázquez, B., Duan, Y., Pfeiffer, H.: Bifunctional application of sodium cobaltate as a catalyst and captor through CO oxidation and subsequent CO2 chemisorption processes. RSC Adv. 6, 2162–2170 (2016)

    Article  CAS  Google Scholar 

  20. Vera, E., Gomez-García, J.F., Pfeiffer, H.: Enhanced CO2 chemisorption at high temperatures via oxygen addition using (Fe, Cu or Ni)-containing sodium cobaltates as solid sorbents. J. CO2 Util. 25, 147–157 (2018)

    Article  CAS  Google Scholar 

  21. Wai, L.T., Jeng, S.L., Haslenda, H., Azizul, M.A., Wai, S.H., Shin, H.: Review of pre-combustion capture and ionic liquid in carbon capture and storage. Appl. Energy 183, 1633–1663 (2016)

    Article  CAS  Google Scholar 

  22. Wang, J., Huang, L., Yang, R., Zhang, Z., Wu, J., Gao, Y., Wang, Q., O’Hare, O., Zhong, Z.: Recent advances in solid sorbents for CO2 capture and new development trends. Energy Environ. Sci. 7, 3478–3518 (2014)

    Article  CAS  Google Scholar 

  23. Webley, P.A.: Adsorption technology for CO2 separation and capture: a perspective. Ads. 20, 225–231 (2014)

    Article  CAS  Google Scholar 

  24. Yañez-Aulestia, A., Gómez-García, J.F., Mendoza-Nieto, J.A., Duan, Y., Pfeiffer, H.: Thermocatalytic analysis of CO2–CO selective chemisorption mechanism on lithium cuprate (Li2CuO2) and oxygen addition effect. Thermochim. Acta 660, 144–151 (2018)

    Article  CAS  Google Scholar 

  25. Zhang, Q., Peng, D., Zhang, S., Ye, Q., Wu, Y., Ni, Y.: Behaviors and kinetic models analysis of Li4SiO4 under various CO2 partial pressures. AIChE J. 63, 2153–2164 (2017)

    Article  CAS  Google Scholar 

  26. Zhang, Y., Yu, F., Louis, B., Wang, Q.: Stable synthesis of the lithium silicate-based high-temperature CO2 sorbent from inexpensive raw material vermiculite. Chem. Eng. J. 349, 562–573 (2018)

    Article  CAS  Google Scholar 

  27. Zhang, Y., Gao, Y., Pfeiffer, H., Louis, B., Sun, L., O’Hare, D., Wang, Q.: Recent advances in lithium containing ceramic based sorbents for high-temperature CO2 capture. J. Mater. Chem. A 7, 7962–8005 (2019)

    Article  CAS  Google Scholar 

  28. Zhao, M., Fan, H., Song, Y., He, X., Memon, M.Z., Bathia, S.K., Ji, G.: Kinetic analysis for cyclic CO2 capture using lithium orthosilicate sorbents derived from different silicon precursors. Dalton Trans. 47, 9038–9050 (2018)

    Article  CAS  PubMed  Google Scholar 

Download references

Acknowledgements

E. Vera thanks to CONACYT for personal financial supports. This work was financially supported by Projects SENER-CONACYT (251801) and PAPIIT-UNAM (IN-201419). Authors thank to Adriana Tejeda and Omar Novelo for technical assistant.

Author information

Affiliations

Authors

Corresponding author

Correspondence to Heriberto Pfeiffer.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Below is the link to the electronic supplementary material.

10450_2019_167_MOESM1_ESM.docx

Fig. S1 XRD patterns of the pristine and Fe-containing NaCoO2 samples with 10, 20 and 30 mol% of iron. All these patterns were identified with the Na0.74CoO2 crystalline phase, where Fe-NaCoO2 samples presented small amounts of NaFeO2 and FeO phases. Supplementary material 1 (DOCX 259 kb)

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Vera, E., García, S., Maroto-Valer, M.M. et al. CO2–CO capture and kinetic analyses of sodium cobaltate under various partial pressures. Adsorption 26, 781–792 (2020). https://doi.org/10.1007/s10450-019-00167-6

Download citation

Keywords

  • CO2 chemisorption
  • CO oxidation
  • Sodium cobaltate
  • Catalysis
  • Kinetics
  • Thermogravimetric analysis
  • Jander-Zhang model