Acta Mechanica Solida Sinica

, Volume 21, Issue 4, pp 289–297 | Cite as

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

  • Xianfeng Ma
  • Huiji Shi
  • Jialin Gu
  • Zhaoxi Wang
  • Harald Harders
  • Thomas Malow
Article

Abstract

The low-cycle fatigue (LCF) behavior of a nickel-based single crystal superalloy with [001] orientation was studied at an intermediate temperature of T0° C and a higher temperature of T0 + 250° C under a constant low strain rate of 10−3 s−1 in ambient atmosphere. The superalloy exhibited cyclic tension-compression asymmetry which is dependent on the temperature and applied strain amplitude. Analysis on the fracture surfaces showed that the surface and subsurface casting micropores were the major crack initiation sites. Interior Ta-rich carbides were frequently observed in all specimens. Two distinct types of fracture were suggested by fractogaphy. One type was characterized by Mode-I cracking with a microscopically rough surface at T0 + 250° C. Whereas the other type at lower temperature T0° C favored either one or several of the octahedral {111} planes, in contrast to the normal Mode-I growth mode typically observed at low loading frequencies (several Hz). The failure mechanisms for two cracking modes are shearing of γ′ precipitates together with the matrix at T0 ° C and cracking confined in the matrix and the γ/γ′ interface at To + 250° C.

Key Words

low cycle fatigue single crystal nickel-based superalloy 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Maclachlan, D.W. and Knowles, D.M., Fatigue behaviour and lifing of two single crystal superalloys. Fatigue and Fracture of Engineering Materials and Structures, 2001, 24: 503–521.CrossRefGoogle Scholar
  2. [2]
    Suresh, S., Fatigue of Materials. 2nd ed. New York: Cambridge University Press, 1998.CrossRefGoogle Scholar
  3. [3]
    Chan, K.S. and Leverant, G.R., Elevated-temperature fatigue crack growth behaviour of MAR-M200 single crystals. Metallurgical Transactions A, 1987, 18A: 593–602.CrossRefGoogle Scholar
  4. [4]
    Walter, W., Stephen, D. and Antolovich, D., Yielding and deformation behaviour of the single crystal superalloy PWA1480. Metallurgical Transactions A, 1987, 18A: 85–95.Google Scholar
  5. [5]
    Yi, J.Z., Torbet, C.J., Feng, Q., et al., Ultrasonic Fatigue of a single crystal Ni-base superalloy at 1000° C. Material Science and Engineering A, 2007, 443: 142–149.CrossRefGoogle Scholar
  6. [6]
    Pope, D.P. and Ezz, S.S., Mechanical properties of Ni3Al and nickel-base alloys with high volume fraction of γ′. International Metals Reviews, 1984, 29: 136–167.CrossRefGoogle Scholar
  7. [7]
    Lall, C., Chin, S., and Pope, D.P., The orientation and temperature dependence of the yield stress of Ni3(Al, Nb) single crystals. Metallurgical Transactions A, 1979, 10A: 1323–1332.CrossRefGoogle Scholar
  8. [8]
    Shah, D.M. and Duhl, D.N., Superalloy 1984, M. Gell, et al., eds., AIME, Warrendale, PA, 1984, 105–114.Google Scholar
  9. [9]
    Miner, R.V., Gabb, T.P. and Jayda, J., et al., Orientation and Temperature Dependence of Some Mechanical Properties of the Single-Crystal Nickel-Base Superalloy Rene N4: Part III. Tension-Compression Anisotropy. Metallurgical Transactions A, 1986, 17A: 507–512.CrossRefGoogle Scholar
  10. [10]
    Jiao, F., Bettge, D. and Osterle, W., et al., Tension-compression Asymmetry of The (001) Single Crystal Nickel Base Superalloy SC16 under Cyclic Loading at Elevated Temperatures. Acta Materialia, 1996, 44(10): 3933–3942.CrossRefGoogle Scholar
  11. [11]
    Leverant, G.A. and Gell, M., The influence of Temperature and Cyclic Frequency on the Fatigue Fracture of Cube Orientated Nickel-Base Superalloy Single Crystal. Metallurgical Transactions A, 1975, 6A: 367–371.CrossRefGoogle Scholar
  12. [12]
    Telesman, J. and Ghosn, L.J., Fatigue Crack Growth Behavior of PWA 1484 Single Crystal Superalloy at Elevated Temperatures. Journal of Engineering for Gas Turbines and Power, 1996, 118: 399–405.CrossRefGoogle Scholar
  13. [13]
    Antolovich, B.F., Saxena, A. and Antolovich, S.D., Fatigue Crack Propagation in Single-Crystal CMSX-2 at Elevated Temperature. Journal of Materials Engineering and Performance, 1993, 2: 489–496.CrossRefGoogle Scholar
  14. [14]
    Swanson, G.R. and Arakere, N.K., Effect of Crystal Orientation on Analysis of Single-Crystal, Nickel-Based Turbine Blade Superalloys. NASA/TP-2000-210074. National Aeronautics and Space Administration. Marshall Space Flight Center. 2000.Google Scholar
  15. [15]
    Gabb, T.P., Gayda, J. and Miner, R.V., Orientation and temperature dependence of some mechanical properties of the single-crystal nickel-base superalloy Rene N4: Part II. Low cycle fatigue behaviour. Metallurgical Transactions A, 1986, 17A: 497–505.CrossRefGoogle Scholar
  16. [16]
    Deluca, D.P. and Cowles, B.A., Fatigue and Fracture of Single Crystal Nickel in High Pressure Hydrogen. Hydrogen Effects on Material Behavior, N.R. Moody and A.W. Thomson (eds.), TMS, Warrendale, PA, 1989.Google Scholar
  17. [17]
    Deluca, D. and Annis, C., Fatigue in Single Crystal Nickel Superalloys, Office of Naval Research, Department of the Navy FR23800, August 1995.Google Scholar
  18. [18]
    He, L.Z., Zheng, Q., Sun, X.F., et al., Effect of temperature and strain amplitude on dislocation structure of M963 superalloy during high-temperature low cycle fatigue. Materials Transactions, 2006, 47(1): 67–71.CrossRefGoogle Scholar
  19. [19]
    Lamm, M. and Singer, R.F., The effect of casting conditions on the high-cycle fatigue properties of the single-crystal nickel-base superalloy PWA1483. Metallurgical and Materials Transactions A, 2007, 38: 1177–1183.CrossRefGoogle Scholar

Copyright information

© The Chinese Society of Theoretical and Applied Mechanics and Technology 2008

Authors and Affiliations

  • Xianfeng Ma
    • 1
  • Huiji Shi
    • 1
  • Jialin Gu
    • 2
  • Zhaoxi Wang
    • 1
  • Harald Harders
    • 3
  • Thomas Malow
    • 3
  1. 1.Department of Engineering MechanicsTsinghua UniversityBeijingChina
  2. 2.Department of Material ScienceTsinghua UniversityBeijingChina
  3. 3.Siemens Power GenerationMülheim an der RuhrGermany

Personalised recommendations